Flame-retardant antibacterial transparent polypropylene material and preparation method thereof

A transparent polypropylene and polypropylene technology, applied in the field of polymer materials, can solve the problems of easy discoloration and high price, and achieve the effects of not easy discoloration, low cost and low smoke density

Inactive Publication Date: 2012-02-01
SHENZHEN KEJU NEW MATERIAL
View PDF2 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The antibacterial agents that play an antibacterial role in antibacterial plastics can be mainly divided into organic antibacterial agents and ino

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retardant antibacterial transparent polypropylene material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The flame retardant antibacterial transparent polypropylene material of this embodiment is made up of following components by weight percentage: polypropylene 91.2%; Polyethylene 3.0%; Toughener 2.0%; White oil 0.1%; Flame retardant 1.0%; Nucleating agent 0.1%; antibacterial agent 2.0%; lubricant 0.4%; antioxidant 0.2%.

[0027] Its preparation method is as follows:

[0028] Step 1, take polypropylene, linear low-density polyethylene, toughening agent, white oil, fire retardant, nucleating agent, antibacterial agent, lubricant, antioxidant by the above-mentioned percentage by weight;

[0029] Step 2, mixing the components weighed in step 1 evenly;

[0030] Step 3: Add the mixed material obtained in Step 2 into the hopper of the twin-screw extruder, melt and react, extrude, and granulate; The temperature in the second zone is 200°C, the temperature in the third zone is 200°C, the temperature in the fourth zone is 210°C, the temperature of the head is 220°C, the residen...

Embodiment 2

[0032] The flame retardant and antibacterial transparent polypropylene material of this embodiment is made up of following components by weight percentage: 86.8% of polypropylene; 4.0% of polyethylene; 3.0% of toughening agent; 0.2% of white oil; 2.0% of flame retardant; Nucleating agent 0.2%; antibacterial agent 3.0%; lubricant 0.5%; antioxidant 0.3%.

[0033] Its preparation method is as follows:

[0034] Step 1, take polypropylene, linear low-density polyethylene, toughening agent, white oil, fire retardant, nucleating agent, antibacterial agent, lubricant, antioxidant by the above-mentioned percentage by weight;

[0035] Step 2, mixing the components weighed in step 1 evenly;

[0036] Step 3: Add the mixed material obtained in Step 2 into the twin-screw extruder, melt and react, extrude, and granulate; The temperature is 210°C, the temperature in the third zone is 210°C, the temperature in the fourth zone is 200°C, the temperature of the head is 230°C, the residence time...

Embodiment 3

[0038] The flame retardant antibacterial transparent polypropylene material of this embodiment is made up of following components by weight percentage: polypropylene 83.6%; Polyethylene 4.0%; Toughening agent 4.0%; White oil 0.2%; Flame retardant 3.0%; Nucleating agent 0.3%; antibacterial agent 4.0%; lubricant 0.6%; antioxidant 0.3%.

[0039] Its preparation method is as follows:

[0040] Step 1, take polypropylene, linear low-density polyethylene, toughening agent, white oil, fire retardant, nucleating agent, antibacterial agent, lubricant, antioxidant by the above-mentioned percentage by weight;

[0041] Step 2, mixing the components weighed in step 1 evenly;

[0042] Step 3: Add the mixed material obtained in Step 2 into the twin-screw extruder, melt and react, extrude, and granulate; The temperature is 210°C, the temperature in the third zone is 210°C, the temperature in the fourth zone is 200°C, the temperature of the head is 230°C, the residence time is 3min, and the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a flame-retardant antibacterial transparent polypropylene material and a preparation method thereof. The polypropylene material is prepared from the following components in percentage by weight: 79.1-91.2% of polypropylene, 3.0-5.0% of linear low-density polyethylene, 2.0-5.0% of toughening agent, 0.1-0.3% of white oil, 1.0-4.0% of flame retardant, 0.1-0.4% of nucleating agent, 2.0-5.0% of antibacterial agent, 0.4-0.8% of lubricant and 0.2-0.4% of antioxidant. The flame-retardant antibacterial transparent polypropylene material disclosed by the invention has the advantages that the flame retardant and antibacterial agent in the formula are compounded, thus the prepared polypropylene material has the flame retardant and antibacterial effects at the same time; and the product has low smoke density during combustion, is difficult to change color and has low cost.

Description

[technical field] [0001] The invention relates to the field of polymer materials, in particular to a flame-retardant and antibacterial transparent polypropylene material and a preparation method thereof. [Background technique] [0002] Polypropylene has the characteristics of low production cost, good comprehensive mechanical properties, non-toxic, light weight, corrosion resistance, easy processing and recycling, etc., so it has been widely used, but it is a flammable material, so it is very important to give it flame retardant properties. important and necessary. [0003] In daily life, people will inevitably come into contact with bacteria. As people's health awareness increases, antibacterial plastics will also be used more and more. Antibacterial agents that play an antibacterial role in antibacterial plastics can be mainly divided into organic antibacterial agents and inorganic antibacterial agents. At present, the commonly used inorganic antibacterial agents have pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L23/08C08K13/06C08K9/04C08K3/34C08K5/20C08K5/134C08K5/526B29C47/92B29C48/92
Inventor 徐东徐永杨秋会
Owner SHENZHEN KEJU NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap