Microporous-fiber composite sound absorbing board

A fiber composite, sound-absorbing board technology, applied in the direction of sound-generating equipment, instruments, etc., can solve the problem of not satisfying low-frequency sound absorption and so on

Active Publication Date: 2015-01-21
CHINA ELECTRIC POWER RES INST +3
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0026] Application No. 201010191493.3, an invention patent named "A Microporous Fiber Perforated Plate and Its Preparation Method", its technical solution provides a microporous fiber perforated plate and its preparation method, and the examples obtained The effect is at 125Hz, and the sound absorption coefficient is below 0.1, which cannot meet the requirements of low-frequency sound absorption

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Microporous-fiber composite sound absorbing board
  • Microporous-fiber composite sound absorbing board
  • Microporous-fiber composite sound absorbing board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0064] Example 1: Sound-absorbing panel 1#

[0065] Micro-perforated plate 1: Prepare the micro-perforated plate 1 with a commercially available 0.5mm aluminum plate, in which the hole spacing is 2mm and the hole diameter is 1.5mm;

[0066] Manufacturer Name: Zhongzhou Aluminum Co., Ltd.

[0067] Factory Address: Koutou Industrial Zone, Xiaoguan Town, Gongyi City, Henan Province

[0068] Aluminum plate model: 1050 series aluminum plate

Embodiment 2

[0069] The aluminum plates in Embodiment 2, Embodiment 3 and Embodiment 4 are all purchased from the above-mentioned manufacturers.

[0070] Aluminum fiberboard 2: customized areal density is 300g / m 2 Aluminum fiber board 2, wherein the aluminum fiber is prepared by melting and pumping method, and the fiber diameter is 120 μm;

[0071] Combination: Combine the micro-perforated board 1 and the aluminum fiber board 2, and connect them through the keel 3. The distance between the micro-perforated board and the aluminum fiber board is 20mm, and the distance between the aluminum fiber board 2 and the wall is 180mm; it is made into a sound-absorbing board 1#;

[0072] See the sound absorption coefficient curve (red line) of sound-absorbing panel 1# image 3 , image 3 The sound absorption coefficient curve of the aluminum fiber sound-absorbing board (AL-fibre board) used as a comparative experiment is represented by a black line, and the distance between the aluminum fiber sound...

Embodiment 3

[0078] Example 3: Sound-absorbing panel 3#

[0079] Micro-perforated plate 1: A commercially available 0.8mm aluminum plate was used to prepare a micro-perforated plate, in which the hole spacing was 15mm and the hole diameter was 0.8mm;

[0080] Aluminum fiberboard 2: customized areal density is 500g / m 2 Aluminum fiber board, wherein the aluminum fiber is prepared by melting and pumping method, and the fiber diameter is 90 μm;

[0081] Combination: Combine the micro-perforated plate 1 and the aluminum fiber plate 2, and connect them through the keel 3. The distance between the micro-perforated plate 1 and the aluminum fiber plate 2 is 60mm for the first resonance cavity 7, and the second between the aluminum fiber plate 2 and the wall The distance of resonance cavity 8 is 120mm; it is made into sound-absorbing board 3#;

[0082] See the sound absorption coefficient curve (red line) of sound-absorbing panel 3# Figure 5 , Figure 5 The sound absorption coefficient curve of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a microporous-fiber composite sound absorbing board, belonging to the field of instruments for absorbing noises through adopting the resonance principle. The sound absorbing board has a good low-frequency sound absorbing effect, and the sound absorbing coefficient of the sound absorbing board is larger than 0.5 at 125Hz. Compared with an aluminum fiber absorbing board, the sound absorbing board has a wider absorbing absorption band. The sound absorbing coefficient of the sound absorbing board is not smaller than 0.4 at 250-1600Hz. The composite sound absorbing board is formed by compounding a micro-perforated board with an aluminum fiber board and adopts a double-resonance coupling structure. The micro-perforated board is connected with the aluminum fiber board through a keel frame to form a first resonating cavity, and the aluminum fiber board is connected with a wall through the keel frame to form a second resonating cavity. The micro-perforated board and the aluminum fiber board are coupled through a resonance peak to achieve the purposes of increasing the low-frequency sound absorbing effect and expanding the absorbing absorption band. The composite sound absorbing board adopting an all aluminum structure has the characteristic of good recycling, and the problems of aging, dropping and the like do not exist. The sound absorbing board also has the characteristic of good heat conduction, and is convenient for equipment to dissipate heat.

Description

technical field [0001] The invention belongs to the field of instruments for absorbing noise by using the principle of resonance, and in particular relates to a microporous fiber composite sound-absorbing board. Background technique [0002] With the development of urbanization and the enhancement of residents' awareness of environmental protection, the noise problem of substations has gradually become a problem that the power grid operation department needs to face up to. At present, whether it is an urban substation or a rural substation, with the increasing shortage of land resources, the surrounding buildings and population density of the substation are gradually increasing, which also objectively causes the noise of the substation to become a hot spot for some urban residents to complain to the environmental protection department. The resulting petitions and mass incidents are increasing day by day. In the "Macro Environmental Strategy of the State Council" that has be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G10K11/172
Inventor 聂京凯陈新韩钰杨富尧祝志祥马光朱全军李现兵
Owner CHINA ELECTRIC POWER RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com