Packaging container

A technology for packaging containers and thermoplastic materials, which is applied in packaging, wrapping paper, transportation and packaging, etc. It can solve the problems of raw material waste and energy waste, and achieve the effects of reduced necking, good sealing strength, and rapid heat sealing

Inactive Publication Date: 2013-04-17
TAIZHOU ZHUYE MACHINERY SCI & TECH
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

All three solutions require the extruder die to be much wider than the width of the paper substrate and barrier layers, requiring more heat to heat and melt the thermoplastic material, wasting energy, and cutting off after lamination is complete Defects on both sides of packaging materials, resulting in waste of raw materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Packaging container
  • Packaging container
  • Packaging container

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] Such as figure 2 and image 3 As shown, a packaging container of the present invention includes the outermost layer 21 of thermoplastic material, the core layer 22, the middle layer 23 of thermoplastic material, the barrier layer 24, the adhesive layer 25 and the innermost layer 26 of thermoplastic material from outside to inside.

[0024] The innermost layer 26 of thermoplastic material comprises metallocene-catalyzed linear low-density polyethylene (MLLDPE) and low-density polyethylene (LDPE), wherein metallocene-catalyzed linear low-density polyethylene (mLLDPE) has the following parameters: average density 0.88g / cm 3 ~0.925g / cm 3 , Melt flow index (190℃, 2.16kg) is 5g / 10min~20g / 10min, peak melting point is 85℃~130℃, expansion ratio is 1.2~1.8; low density polyethylene (LDPE) has the following parameters: average density 0.90g / cm 3 ~0.925g / cm 3 , Melt flow index (190℃, 2.16kg) is 5g / 10min~20g / 10min, peak melting point is 85℃~110℃, expansion ratio is 1.2~1.8, lo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a packaging container which comprises an outmost thermoplastic material layer, a core layer, an intermediate thermoplastic material layer, a blocking layer and an innermost thermoplastic material layer from outside to inside. The innermost thermoplastic material layer contains metalloscene catalyst polymerized linear low density polyethylene (MLLDPE) and low density polyethylene (LDPE), the MLLDPE has following parameters: average density of 0.88g / cm3-0.925g / cm3, melt flow index (190 DEG C, 2.16kg) of 5g / 10min-20g / 10min, peak melting point of 85 DEG C-130 DEG C, and expansion ratio of 1.2-1.8, and the LDPE has following parameters: average density of 0.90g / cm3-0.925g / cm3, melt flow index (190 DEG C, 2.16kg) of 5g / 10min-20g / 10min, peak melting point of 85 DEG C-110 DEG C, and expansion ratio of 1.2-1.8. A longitudinal sealing portion can realize quick thermal sealing during the process of manufacturing the packaging container, sealing intensity is high, and the manufactured packaging container is high in pass percentage and long in shelf life of liquid food.

Description

technical field [0001] The invention relates to a packaging container, in particular to a packaging container used for packaging liquid food. Background technique [0002] At present, disposable disposable packaging containers for liquid food have shapes such as bricks, squares, triangles, octahedrons with hexagonal cross-sections, and pillows. Usually, the laminated packaging materials used to manufacture these packaging containers include sequential layers. The outermost layer of thermoplastic material, the core layer, the middle layer of thermoplastic material, the barrier layer, the adhesive layer and the innermost layer of thermoplastic material, and there are also low-density polyethylene (LDPE) / printing ink layer / paper ( fiber) base layer / LDPE / aluminum foil AL / LDPE / LDPE, LDPE / printing ink layer / paper base layer / LDPE / LDPE, printing ink layer / LDPE / paper base layer / LDPE / LDPE, such as LDPE / printing ink layer / paper Laminated packaging materials with multi-layer structure ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B65D65/40B65D85/72C08L23/08C08L23/06B32B27/32
Inventor 吴壮
Owner TAIZHOU ZHUYE MACHINERY SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com