PS-ABS (polystyrene-acrylonitrile butadiene styrene) solvent type adhesive
A PS-ABS, solvent-based technology, used in adhesive types, hydrocarbon copolymer adhesives, acrylonitrile butadiene styrene polymer adhesives, etc., can solve the bonding ability of polar adherends Poor, unfavorable adhesive preservation, hard adhesive layer and other problems, to achieve the effect of good dimensional stability, high hardness and low corrosiveness
Inactive Publication Date: 2013-04-24
NINGBO DINGCHENG ADHESIVE
View PDF5 Cites 8 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
However, PS solvent-based adhesives have the following disadvantages: PS is a non-polar substance, and its bonding ability with polar adherends is poor; PS resin is of average strength and brittle, and the adhesive layer is hard and brittle, which is prone to stress brittle cracking ;PS solvent-based adhesives often use low-cost toluene and xylene as solvents. These solvents are highly toxic and harmful to human health; they are corrosive to soft aluminum tubes, which is not conducive to long-term storage of adhesives.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0018] The preparation method is as follows: 250 parts of PS resin, 40 parts of ABS resin, and 670 parts of ethyl acetate are mixed and stirred evenly to obtain a transparent glue, which is packaged in a soft aluminum tube for use.
Embodiment 2
[0020] The preparation method is as follows: 280 parts of PS resin, 53 parts of ABS resin, and 630 parts of ethyl acetate are mixed and stirred evenly to obtain a transparent glue, which is packaged in soft aluminum tubes for use.
Embodiment 3
[0022] The preparation method is as follows: 300 parts of PS resin, 50 parts of ABS resin, and 650 parts of ethyl acetate are mixed and stirred evenly to obtain a transparent glue, which is packaged in soft aluminum tubes for use.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to a PS-ABS (polystyrene-acrylonitrile butadiene styrene) solvent type adhesive. The PS-ABS solvent type adhesive is prepared from the following raw materials in parts by weight: 250-350 parts of PS resin, 40-60 parts of ABS resin and 600-700 parts of ethyl acetate. The PS-ABS resin co-mixing can greatly improve the hard and crisp performances of an adhesive layer, increase the range of applications of the adhesive disclosed by the invention and be used for adhering wood, ceramic, plastic, cloth, paper and other materials. According to the PS-ABS solvent type adhesive disclosed by the invention, the ethyl acetate is taken as a solvent, the toxicity is low, and the corrosion to a packaging material, namely a flexible aluminum pipe is small. The PS-ABS solvent type adhesive disclosed by the invention has the advantages of good adhesion with an adhered object, high strength, low toxicity, long preservation time, simplicity and convenience for use and the like.
Description
technical field [0001] The invention relates to a PS-ABS solvent type adhesive. Background technique [0002] PS is a thermoplastic resin that can be directly dissolved in solvents to make PS solvent-based adhesives. PS solvent-based adhesive is easy to use, fast in positioning, water-resistant and corrosion-resistant. However, PS solvent-based adhesives have the following disadvantages: PS is a non-polar substance, and its bonding ability with polar adherends is poor; PS resin is of average strength and brittle, and the adhesive layer is hard and brittle, which is prone to stress brittle cracking ; PS solvent-based adhesives often use low-cost toluene and xylene as solvents. These solvents are highly toxic and endanger human health; they are also corrosive to soft aluminum tubes, which is not conducive to long-term storage of adhesives. Contents of the invention [0003] The technical problem to be solved in the present invention is to provide a PS-ABS solvent-based adh...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C09J125/06C09J155/02
Inventor 朱志恩
Owner NINGBO DINGCHENG ADHESIVE
PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.