Coating rubber roller for high-grade automobile plate production line and manufacturing method thereof

A manufacturing method and technology for automotive sheets, applied in coatings, devices for coating liquids on the surface, etc., can solve problems such as the roughness of the roll surface is difficult to meet the requirements, the hardness consistency of the roll surface is poor, and the roll surface is prone to rubber-covered lines, etc. , to achieve the effect of avoiding the difference in rubber properties, consistent material properties, and uniform vulcanization degree

Active Publication Date: 2014-03-05
南京金三力橡塑有限公司 +1
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention aims at the existing problems of the coated rubber rollers used in the high-grade automobile sheet production line: a. the surface of the roller is prone to rubber coating lines; b. the roughness of the roller surface is difficult to meet the requirements; c. the hardness consistency of the roller surface is poor. Starting from the aspects of gluing process, vulcanization process, car grinding process, etc., a coating rubber roller for high-grade automobile sheet production line and its manufacturing method are provided. Requirements for the use of coated rubber rollers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coating rubber roller for high-grade automobile plate production line and manufacturing method thereof
  • Coating rubber roller for high-grade automobile plate production line and manufacturing method thereof
  • Coating rubber roller for high-grade automobile plate production line and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A coating rubber roller for a high-grade automobile sheet production line in this embodiment has a specification of Φ300×Φ260×2270, and the rubber used in it includes the following components by weight percentage:

[0031]

[0032] According to the design formula requirements, the ethylene propylene rubber is Jihua 4045 EPDM rubber, the carbon black of the filling and reinforcing material is Cabot N330 high wear-resistant carbon black and N660 general carbon black, and the naphthenic oil is Shanghai Luobo Lubricant Co., Ltd. The naphthenic rubber oil produced by the company, Qi polyester is a liquid rubber cross-linking agent produced by Xi'an Organic Chemical Factory, the tackifier is 501 resin produced by German DOG company, and the flow aid is Deoflow represented by Yuanqing International Trade Co., Ltd. S, the vulcanizing agent DCP is a bridging agent produced by Taicang Plastic Auxiliary Factory Co., Ltd., the sulfur is 200 mesh sulfur powder produced by Anqing C...

Embodiment 2

[0044] A coated rubber roller for a high-grade automobile sheet production line in this embodiment has a specification of Φ300×Φ260×2370, and the rubber used in it includes the following components by weight percentage:

[0045]

[0046] According to the design formula requirements, the ethylene propylene rubber is Jihua 4045 EPDM rubber, the carbon black of the filling and reinforcing material is Cabot N330 high wear-resistant carbon black and N660 general carbon black, and the naphthenic oil is Shanghai Luobo Lubricant Co., Ltd. The naphthenic rubber oil produced by the company, Qi polyester is a liquid rubber cross-linking agent produced by Xi'an Organic Chemical Factory, the tackifier is 501 resin produced by German DOG company, and the flow aid is Deoflow represented by Yuanqing International Trade Co., Ltd. S, the vulcanizing agent DCP is a bridging agent produced by Taicang Plastic Auxiliary Factory Co., Ltd., the sulfur is 200 mesh sulfur powder produced by Anqing Ch...

Embodiment 3

[0056] A coating rubber roller for a high-grade automobile sheet production line in this embodiment has a specification of Φ440×Φ400×2100, and the rubber used in it includes the following components by weight percentage:

[0057]

[0058] According to the design formula requirements, the ethylene propylene rubber is Jihua 4045 EPDM rubber, the carbon black of the filling and reinforcing material is Cabot N330 high wear-resistant carbon black and N660 general carbon black, and the naphthenic oil is Shanghai Luobo Lubricant Co., Ltd. The naphthenic rubber oil produced by the company, Qi polyester is a liquid rubber cross-linking agent produced by Xi'an Organic Chemical Factory, the tackifier is 501 resin produced by German DOG company, and the flow aid is Deoflow represented by Yuanqing International Trade Co., Ltd. S, the vulcanizing agent DCP is a bridging agent produced by Taicang Plastic Auxiliary Factory Co., Ltd., the sulfur is 200 mesh sulfur powder produced by Anqing C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a coating rubber roller for a high-grade automobile plate production line and a manufacturing method thereof, belonging to the field of rubber rollers and preparation methods thereof. The rubber for the rubber roller comprises the following components in percentage by weight: 50.7-58.1% of ethylene-propylene rubber, 29.1-38.1% of carbon black, 2.5-2.9% of naphthenic oil, 2.5-2.9% of ester oligomer, 2.5-2.9% of tackifier, 1.0-1.2% of flow promoter, 1.9-2.2% of vulcanizing agent DCP, 0.28-0.32% of sulfur, 0.18-0.20% of accelerator BZ and 0.18-0.20% of accelerator DPTT. The method comprises the following steps: compounding the rubber; winding and rubberizing; vulcanizing in a vulcanizer; and carrying out lathe grinding. In the rubber compounding process, the materials can be sufficiently dispersed and fused. the rubberizing grain color difference on the roller surface can be eliminated, the consistency of internal and external hardness of the rubber roller is high, and the material distribution consistency and roller surface roughness consistency are high, thereby satisfies the operational requirements for the coating rubber roller for a high-grade automobile plate production line.

Description

technical field [0001] The present invention relates to a coated rubber roller and a manufacturing method thereof, more specifically, to a EPDM rubber coated rubber roller used for coating a layer of special lubricating film on the surface of a steel plate during the production of high-grade automobile sheets and its method of manufacture. Background technique [0002] With the rapid development of the automobile industry and the popularization of family cars, the demand for automobile steel plates is also increasing, which drives the rapid development of the automobile steel plate industry. However, automotive steel sheets, especially automotive outer panels and door inner panels, are prone to cracks and surface coating peeling off during stamping, which not only reduces the product quality of automotive steel sheets, but also increases the production cost of automobiles. . In order to improve the stamping formability of the steel plate and reduce the production cost, a s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08K13/02C08K3/04C08K5/01C08K3/06B29B7/00B29C35/02B29C47/14B05C1/00B29C48/305
CPCB05C1/08B29B7/28B29C35/049B29C48/30B29C48/305C08K2201/014C08L23/16C08K13/02C08K3/04C08K5/01C08K3/06
Inventor 徐海潮戎启虎朱文华吴润生高剑刘朴林上辉姚建庆王鲁
Owner 南京金三力橡塑有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com