Inflaming-retarding and smoke-suppressing PVC (polyvinyl chloride) pipe material and preparation method thereof

A PVC resin and flame-retardant technology, which is applied in the field of flame-retardant and smoke-suppressing PVC drainage pipe materials and its preparation, can solve problems such as the limitation of application range, and achieve excellent mechanical properties and flame-retardant and smoke-suppressing properties.

Active Publication Date: 2014-05-14
HENAN LIANSU IND
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the event of a fire, a large number of people died due to smoke suffocation, which limits the application range of PVC to a certain extent.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Mg(OH) 2 First use titanate coupling agent NDZ-311 with a mass fraction of 2% for surface treatment, Sb 2 o 3 The titanate coupling agent KR-38S with a mass fraction of 2% was used for surface treatment. Then the surface treated Mg(OH) 2 with Sb 2 o 3 Composite flame retardants are prepared by mixing in a weight ratio of 2:1. The composite flame retardant and PVC resin are mixed according to the weight ratio of 2.5:97.5 in a hot mixer at 100°C to obtain a mixture. The mixture is melted and blended by a single-screw extruder, shaped, and finally cooled and shaped to obtain a high-quality product. Flame retardant PVC drain pipe material.

Embodiment 2

[0024] Mg(OH) 2 First use titanate coupling agent NDZ-311 with a mass fraction of 2% for surface treatment, Sb 2 o 3 The titanate coupling agent HY-101 with a mass fraction of 2% was used for surface treatment. Then the surface treated Mg(OH) 2 with Sb 2 o 3 Composite flame retardants are prepared by mixing in a weight ratio of 2:1. The composite flame retardant and PVC resin are mixed according to the weight ratio of 2.5:97.5 in a hot mixer at 100°C to obtain a mixture. The mixture is melted and blended by a single-screw extruder, shaped, and finally cooled and shaped to obtain a high-quality product. Flame retardant PVC drain pipe material.

Embodiment 3

[0026] Mg(OH) 2 First, the titanate coupling agent NDZ-311 with a mass fraction of 2% was used for surface treatment, and the ZnO surface was treated with a silane coupling agent KH-550 with a mass fraction of 2%. Then the surface treated Mg(OH) 2 It is mixed with ZnO at a weight ratio of 2:1 to prepare a composite flame retardant. The composite flame retardant and PVC resin are mixed according to the weight ratio of 2.5:97.5 in a hot mixer at 100°C to obtain a mixture. The mixture is melted and blended by a single-screw extruder, shaped, and finally cooled and shaped to obtain a high-quality product. Flame retardant PVC drain pipe material.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of plastic pipes, and discloses an inflaming-retarding and smoke-suppressing PVC (polyvinyl chloride) pipe material and a preparation method thereof. A fire retardant Mg(OH)2 is subjected to surface treatment by adopting a special coupling agent, and is prepared into a compound fire retardant together with a modified inflaming-retarding additive, thus due to cooperation of the fire retardant Mg(OH)2 and the modified inflaming-retarding additive, the compound fire retardant can be prepared into a PVC drainage pipe material which is more excellent in processability, mechanical property and inflaming-retarding and smoke-suppressing properties. According to the preparation method disclosed by the invention, black smoke and toxic gases released during combustion of the PVC pipe material are greatly reduced, and a large quantity of casualties caused by smoke asphyxia in a fire accident are reduced.

Description

technical field [0001] The invention belongs to the technical field of plastic pipes, and in particular relates to a flame-retardant and smoke-suppressing PVC drainage pipe material and a preparation method thereof. Background technique [0002] The raw material polyvinyl chloride (PVC) used in the PVC-U drainage pipe is a self-extinguishing material, but PVC will emit a large amount of black smoke and toxic gases when burned. Such as HCl, CO, a small amount of phosgene, benzene, naphthalene and other aromatic compounds. In the event of a fire, a large number of people died due to smoke suffocation, which limits the application range of PVC to a certain extent. At the same time, the addition of plasticizers, lubricants and other additives during the processing of PVC-U drainage pipes will also reduce the flame retardancy and smoke suppression performance of the material. Therefore, research on smoke suppression and flame retardant modification of PVC-U drainage pipes Gaini...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08K9/04C08K3/22C08K9/06
Inventor 代营伟李锦松
Owner HENAN LIANSU IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products