A production method and technology of painted pottery, which is applied in the field of pottery firing, can solve the problems of black pottery such as low density, high air permeability, loss of use value and collection value, and achieve the effect of hard texture, crisp sound and kiln transformation effect

Inactive Publication Date: 2014-11-19
汤小丽
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, the density of black pottery is low, the air permeability is too large, too permeable, an

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A method for making black painted pottery, which is characterized in that the old soil that has been deposited for thousands of years at the foot of Shennong Mountain is used as the material. The old soil contains a large proportion of iron, good viscosity, and rich trace elements; Firstly, the selected materials are fired into black pottery through wood kiln firing, and the selected materials are first fired to 800°C-900°C, and the carburizing kiln is carried out when the temperature drops to about 500°C, and then the kiln is opened after the temperature drops below 40°C. Out of the kiln; then put it into the gas kiln for the second stage of firing. In the gas kiln, the temperature is first raised to 900°C, and then the temperature is raised little by little through the method of raising the temperature up and down. First, it is raised by 10°C to maintain half a Hours, lower 5°C and maintain for half an hour, then raise the temperature by 10°C for half an hour, then low...

Embodiment 2

[0014] A method for making black painted pottery, which is characterized in that the old soil that has been deposited for thousands of years at the foot of Shennong Mountain is used as the material. The old soil contains a large proportion of iron, good viscosity, and rich trace elements; Firstly, the selected materials are fired into black pottery through wood kiln firing, and the selected materials are first fired to 800°C-900°C, and the carburizing kiln is carried out when the temperature drops to about 500°C, and then the kiln is opened after the temperature drops below 40°C. Out of the kiln; then put it into the gas kiln for the second stage of firing. In the gas kiln, the temperature is first raised to 900°C, and then the temperature is raised little by little through the method of raising the temperature up and down, first rising 10°C and maintaining it for 20 minutes After lowering the temperature by 5°C, keep it for 20 minutes, then raise the temperature by 10°C and ke...

Embodiment 3

[0016] A method for making black painted pottery, which is characterized in that the old soil that has been deposited for thousands of years at the foot of Shennong Mountain is used as the material. The old soil contains a large proportion of iron, good viscosity, and rich trace elements; Firstly, the selected materials are fired into black pottery through wood kiln firing, and the selected materials are first fired to 800°C-900°C, and the carburizing kiln is carried out when the temperature drops to about 500°C, and then the kiln is opened after the temperature drops below 40°C. Out of the kiln; then put it into the gas kiln for the second stage of firing. In the gas kiln, the temperature is first raised to 900°C, and then the temperature is raised little by little through the method of raising the temperature up and down, first rising 10°C and maintaining it for 40 minutes After lowering the temperature by 5°C, maintain it for 40 minutes, then raise the temperature by 10°C an...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for making black colored pottery. The method comprises the following steps: firstly, calcining aged soil which is deposited for thousands of years at the foot of the Shennong mountain into black pottery in a wood kiln, namely, calcining the material to be 800-900 DEG C, performing carburization kiln transmutation when the temperature is reduced to be about 500 DEG C, subsequently opening the kiln, and discharging the pottery; putting the pottery into an air kiln for secondary calcining, namely, raising the temperature to be 900 DEG C in the air kiln firstly, subsequently raising the temperature step by step by using a method that the temperature is highly increased and slightly reduced, that is, raising by 10 DEG C firstly, keeping for 20-40 minutes, reducing the temperature by 5 DEG C, keeping the temperature for 20-40 minutes, raising the temperature by 10 DEG C for another time, keeping for 20-40 minutes, subsequently reducing the temperature by 5 DEG C, keeping for 20-40 minutes, raising the temperature for another time, repeating the operation sequentially till the temperature is 1200 DEG C, turning off an air source, opening the kiln when the temperature is reduced to be less than 100 DEG C, subsequently reducing the temperature to be less than 50 DEG C, and discharging the pottery, thereby obtaining the black colored pottery. The method has the beneficial effects that the defect that the black colored pottery is too rough, and the black colored pottery calcined by using the method is relatively high in density, relatively hard in texture, relatively unique in kiln transmutation, relatively high in artistic value and relatively high in collection.

Description

technical field [0001] The invention relates to the technical field of pottery firing, in particular to a method for making black painted pottery. Background technique [0002] Thousands of years have passed, and there is a kind of life that, in the long multiplication of washing away the lead, gave birth to a cultural treasure in the soil of the land of China-black pottery. Generations of craftsmen have worked tirelessly for this and passed it down from generation to generation. [0003] The development of pottery culture is writing a glorious chapter of Chinese history and civilization. Qinyang City, located in the birthplace of Chinese historical civilization, was historically known as the Yiqi feudal territory, the former land of Shangji, and the famous state of Heshuo. It is now a famous historical and cultural city in Henan Province, and a "Millennium Ancient County" recognized by the Geography Department of the United Nations Educational, Scientific and Cultural Orga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B33/32
Inventor 汤小丽
Owner 汤小丽
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap