A production method of large stainless steel forgings for thermonuclear fusion reactors

A technology of thermonuclear fusion and production methods, applied in the direction of metal processing equipment, etc., can solve the problems of long delivery cycle, many surface cracks, high production costs, etc.

Active Publication Date: 2016-01-20
NORTHEASTERN UNIV LIAONING +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] If the forging is produced by the usual forging process, the grain size of the forging is less than grade 2, and there are many surface cracks, and the crack depth reaches more than 2mm; it cannot meet the requirements of ITER for the grain size of the forging ≥ grade 2, and the forging is due to the surface Deep cracks require a large amount of turning, resulting in high production costs and long lead times

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The stainless steel grade of this embodiment is 316L(N)-IG.

[0040] Finished product specifications: 450 -0 +30 ×1100 -0 +50 ×2193 0 +50 mm.

[0041] Theoretical weight of finished forgings: 8.608 tons.

[0042] The steps of this embodiment are as follows:

[0043] (1) Steel ingot pretreatment

[0044] Steel ingot size and type: circular frustum steel ingot, the diameter of the lower section is 1000mm, the diameter of the upper section is 945mm, the height is 1807mm (height after cutting the head and tail), and the height / diameter ratio is 1.8.

[0045] Ingot weight (after removing head and tail): 11.100 tons.

[0046] Chemical composition of steel ingot:

[0047] C: 0.012%Si: 0.43%Mn: 1.77%Cr: 16.26%

[0048] Ni: 13.77%P: 0.016%S: 0.002%N: 751ppm

[0049] Mo: 2.15% Co: 0.03%, Nb: 0.01%, Ta: 0.010%

[0050] (2) Steel ingot heating

[0051] The first fire heating: the steel ingot is put into the furnace as a cold ingot, and heated at a temperature below 50...

Embodiment 2

[0071] The stainless steel grade of this embodiment is 316LN.

[0072] Finished product specifications: 600 -0 +30 ×1500 -0 +50 ×1900 0 +50 mm.

[0073] Theoretical weight of finished forgings: 13.56 tons.

[0074] The steps of this embodiment are as follows:

[0075] (1) Steel ingot

[0076] Steel ingot size and type: circular frustum steel ingot, the diameter of the lower section is 1200mm, the diameter of the upper section is 1135mm, the height is 1850mm (height after cutting the head and tail), and the height / diameter ratio is 1.58.

[0077] Ingot weight (after removing the head and tail): 15.70 tons.

[0078] Chemical composition of steel ingot:

[0079] C: 0.017%Si: 0.50%Mn: 1.51%Cr: 16.15%

[0080] Ni: 12.43%P: 0.018%S: 0.0012%N: 1312ppm

[0081] Mo: 2.08% Co: 0.03%, Nb: 0.01%, Ta: 0.010%

[0082] (2) Steel ingot heating

[0083] The first fire heating: the steel ingot is put into the furnace as a cold ingot, and heated at a temperature below 500°C at a ra...

Embodiment 3

[0104] The stainless steel grade of this embodiment is 316L.

[0105] Finished product specifications: 450 -0 +30 ×1150 -0 +50 ×2100 -0 +50 mm.

[0106] Theoretical weight of finished forgings: 8.62 tons.

[0107] The steps of this embodiment are as follows:

[0108] (1) Steel ingot

[0109] Steel ingot size and type: octagonal steel ingot, the diameter of the lower section is 1150mm, the diameter of the upper section is 1175mm, the height is 2230mm (height after cutting the head and tail), and the height / diameter ratio is 2.0.

[0110] Ingot weight (after removing the head and tail): 18.65 tons.

[0111] Chemical composition of steel ingot:

[0112] C: 0.015%Si: 0.48%Mn: 1.62%Cr: 16.32%

[0113] Ni: 12.50%P: 0.018%S: 0.001%N: 880ppm

[0114] Mo: 2.11% Co: 0.03%, Nb: 0.01%, Ta: 0.010%

[0115] (2) Steel ingot heating

[0116] The first fire heating: the steel ingot is put into the furnace as a cold ingot, and heated at a temperature below 500°C at a rate of 50°C-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing large stainless steel forgings for thermonuclear fusion reactors, including: (1) steel ingot pretreatment; (2) steel ingot heating process; (3) steel ingot forging process; (4) two upsetting and two drawing processes; (5) Shaping of finished products; (6) Heat treatment process of finished forgings; the thickness of the final large stainless steel forgings is 300-1000mm; the width is 300-1800mm; the length is 500-2200mm. The method realizes that the grain size of the stainless steel forging is ≥2 grades, and the surface crack depth of the forging is less than 1mm, which meets the quality requirements of thermonuclear fusion reactors (including the ITER program).

Description

technical field [0001] The invention relates to a production method for a large stainless steel forging for a thermonuclear fusion reactor, in particular to a production method for a stainless steel forging with a thickness of 300-1000mm and a width of 300-1800mm for a thermonuclear fusion reactor. Background technique [0002] The ITER program (International Thermonuclear Experimental Reactor International Thermonuclear Experimental Reactor) is a new type of thermonuclear experimental reactor project participated by seven countries and regions including the European Union, the United States, China, Japan, Russia, India and South Korea. [0003] The project requires a large number of 316LN and 316L(N)-IG stainless steel forging products with a thickness exceeding 300mm. The main stainless steel material components are as follows: [0004] Steel number: 316L(N)-IG, composition requirements: C≤0.03%, Si≤0.75%, Mn≤2.00%, P≤0.03%, S≤0.01%, Cr16.00%-18.00%, Ni11.00% -14.00%, Mo2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): B21J5/00B21J5/06B21J5/08B21J1/06
Inventor刘承志姜周华李花兵尹嵬李筱张剑桥
OwnerNORTHEASTERN UNIV LIAONING