Fabric composite film and its preparation method and application

A composite film and fabric technology, applied in chemical instruments and methods, diaphragm structures, synthetic resin layered products, etc.

Inactive Publication Date: 2018-07-06
DONGGUAN JINRUI ELECTRONICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Another object of the present invention is to provide a preparation method of a fabric composite membrane, which has simple steps, is easy to operate, and has high production efficiency, and can produce a fabric composite membrane, which can effectively improve the distortion problem of the speaker

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fabric composite film and its preparation method and application
  • Fabric composite film and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] The preparation method of fabric composite film, comprises the following steps:

[0071] Step 1: Put the resin film on the roll, and apply adhesive glue, the glue amount is 8g / m 3 , the roller tension on the resin film is 0.5kgf / m 2 ;

[0072] Step 2: Attach the cloth to the resin film, the lamination tension of the cloth is 0.1kgf / m 2 .

[0073] The thickness of the resin film is 0.10mm, and the tensile strength of the resin film is 50kg / cm 2 , the elongation of the resin film is 500%, and the hardness modulus of the resin film is 10kg / cm 2 .

[0074] The density of the knitted fabric is 30g / m 3 , the tensile strength of the knitted fabric is 1kg / cm 2 .

[0075] The resin film in this embodiment is a TPU film. The fabric composite film material prepared by the above method can be applied to the speaker edge material.

Embodiment 2

[0077] The preparation method of fabric composite film, comprises the following steps:

[0078] Step 1: Put the resin film on the roll, and apply adhesive glue, the glue amount is 16g / m 3 , the roller tension on the resin film is 1kgf / m 2 ;

[0079] Step 2: Attach the cloth to the resin film, the lamination tension of the cloth is 0.4kgf / m 2 .

[0080] The thickness of the resin film is 0.015mm, and the tensile strength of the resin film is 100kg / cm 2 , the elongation of the resin film is 400%, and the hardness modulus of the resin film is 50kg / cm 2 .

[0081] The density of the knitted fabric is 60g / m 3 , the tensile strength of the knitted fabric is 100kg / cm 2 .

[0082] The resin film of this example is a PC film. The fabric composite film material prepared by the above method can be applied to the sound film material of the tweeter dome.

Embodiment 3

[0084] The preparation method of fabric composite film, comprises the following steps:

[0085] Step 1: Put the resin film on the roll, and apply adhesive glue, the glue amount is 280g / m 3 , the roller tension on the resin film is 4kgf / m 2 ;

[0086] Step 2: Attach the cloth to the resin film, the lamination tension of the cloth is 2kgf / m 2 .

[0087] The thickness of the resin film is 0.05mm, and the tensile strength of the resin film is 400kg / cm 2 , the elongation of the resin film is 100%, and the hardness modulus of the resin film is 100kg / cm 2 .

[0088] The density of the knitted fabric is 100g / m 3 , the tensile strength of the knitted fabric is 120kg / cm 2 .

[0089] The resin film of this example is a PEEK film. The fabric composite membrane material is prepared by the above method, which can be applied to the micro horn diaphragm material of the loudspeaker.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
densityaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of technology and application of composite materials of fabric and film materials, in particular to a fabric composite film and its preparation method and application. The fabric composite film includes cloth and resin film, and the cloth and resin film are coated and bonded Adhesive, the material of the resin film includes TPU, PC, PEEK, PP, PEI, PEN, PTFE, PU, ​​PVA, silica gel, rubber, acrylic, the resin film is rolled up, and the adhesive glue is coated, and the glue amount is 50 ‑180g / m3, the roller tension on the resin film is 1.5‑3.5kgf / m2, step 2: paste the cloth on the resin film, the lamination tension of the cloth is 1.2‑2.7kgf / m2, which can improve the suspension of the cloth The audio performance of the low frequency and intermediate frequency of the side speaker improves the internal damping and vibration compliance of the speaker diaphragm, reduces abnormal sound, and reduces the distortion rate, which improves the electrical efficiency of the speaker.

Description

technical field [0001] The invention relates to the technical field of technology and application of a composite material of fabric and film material, in particular to a fabric composite membrane and a preparation method and application thereof. Background technique [0002] Loudspeaker, also known as "horn", is a very commonly used electroacoustic transducer device, which can be seen in electronic circuits that produce sound. The loudspeaker is the weakest device among electronic components, but it is the most important device for sound effects. There are many types of speakers, and their prices vary widely. Audio electric energy makes its paper cone or diaphragm vibrate the surrounding air through electromagnetic, piezoelectric or electrostatic effects to produce sound. The sound quality of the speaker is the most important inspection index of the speaker, and a very important reason that affects the sound quality is the membrane vibration. Among them, the hanging edge ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H04R7/02H04R31/00B32B7/12B32B27/06
Inventor 余承鸿余建兴
Owner DONGGUAN JINRUI ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka