TC128GrB steel plate for oil bath tank truck and production method of TC128GrB steel plate

A production method and steel plate technology, which are applied in the field of steel for tank cars, can solve the problems of high production difficulty and high price, and achieve the effects of low production cost, good welding performance and low cost.

Active Publication Date: 2015-04-01
WUYANG IRON & STEEL
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing TC128GrB steel plate has the disadvantages of high difficulty in production, high price and only guarantee of transverse impact energy at -20°C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TC128GrB steel plate for oil bath tank truck and production method of TC128GrB steel plate
  • TC128GrB steel plate for oil bath tank truck and production method of TC128GrB steel plate
  • TC128GrB steel plate for oil bath tank truck and production method of TC128GrB steel plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1: The TC128GrB steel plate for the oil tanker is produced by the following method.

[0021] (1) The chemical composition (weight) of the billet is: C 0.15%, Si 0.15%, Mn 1.65%, P 0.012%, S 0.002%, Cu 0.25%, V 0.095%, Nb 0.006%, Ti 0.016%, Al 0.032 %, Cev 0.46%, the balance is Fe and unavoidable inclusions. In order to avoid cracking on the surface of low-alloy high-strength billets, the billets are required to be stacked for more than 24 hours to release stress.

[0022] (2) The TC128GrB steel plate for the oil tanker is produced by the following process steps:

[0023] A. Heating process: steel billets are stacked for 30 hours before being loaded into the furnace; low temperature and slow heating, the maximum heating temperature is 1250°C, to ensure that the billets are evenly burned through, and the heating speed is 1.5min / mm (calculated as 1.5 minutes per millimeter thickness of steel plate) , The temperature in the soaking section is 1220℃~1240℃, and t...

Embodiment 2

[0032] Embodiment 2: The TC128GrB steel plate for the oil tanker is produced by the following method.

[0033] (1) The chemical composition (weight) of the billet is: C 0.16%, Si 0.37%, Mn 1.55%, P 0.011%, S 0.004%, Cu 0.18%, V 0.070%, Nb 0.017%, Ti 0.011%, Al 0.020 %, Cev 0.44%, the balance is Fe and unavoidable inclusions. In order to avoid cracking on the surface of low-alloy high-strength billets, the billets are required to be stacked for more than 24 hours to release stress.

[0034] (2) The TC128GrB steel plate for the oil tanker is produced by the following process steps:

[0035] A. Heating process: billets are loaded into the furnace after being stacked for 30 hours; low temperature and slow heating, the maximum heating temperature is 1245°C, to ensure that the billets are evenly burned through, the heating speed is 2.0min / mm, the temperature of the soaking section is 1220°C ~ 1230°C, The heating time of the hot section is 100 minutes to ensure that the ingot is even...

Embodiment 3

[0043] Embodiment 3: The TC128GrB steel plate for the oil tanker is produced by the following method.

[0044] (1) The chemical composition (weight) of the billet is: C 0.23%, Si 0.40%, Mn 1.32%, P 0.008%, S 0.005%, Cu 0.05%, V 0.065%, Nb 0.010%, Ti 0.002%, Al 0.021 %, Cev 0.48%, the balance is Fe and unavoidable inclusions. In order to avoid cracking on the surface of low-alloy high-strength billets, the billets are required to be stacked for more than 24 hours to release stress.

[0045] (2) The TC128GrB steel plate for the oil tanker is produced by the following process steps:

[0046] A. Heating process: billets are stacked for 30 hours before being loaded into the furnace; low temperature and slow heating, the maximum heating temperature is 1250°C, to ensure that the billets are evenly burned through, the heating speed is 1.0min / mm, the temperature of the soaking section is 1230°C ~ 1240°C, The heating time of the hot section is 150 minutes to ensure that the ingot is e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a TC128GrB steel plate for an oil bath tank truck and a production method of the TC128GrB steel plate. The TC128GrB steel plate comprises the following components in percentage by weight: 0.14%-0.24% of C, 0.15%-0.50% of Si, 1.30%-1.65% of Mn, no more than 0.015% of P, no more than 0.005% of S, no more than 0.30% of Cu, 0.020%-0.10% of V, 0.005%-0.020% of Nb, no more than 0.020% of Ti, 0.020%-0.050% of Al, no more than 0.53% of Cev, and the balance of Fe and inevitable impurities, wherein Cev=C+Mn / 6+(Cr+Mo+V) / 5 +(Ni+Cu) / 15. The TC128GrB steel plate is high in carbon content, relatively low in microalloy content and low in cost; the strength and toughness are matched; the mechanical property of the steel plate can completely meet the standard requirements of steel for the tank truck on TC128GrB steel; and the TC128GrB steel plate has high surplus, and is low in added precious metal content, and low in production cost.

Description

technical field [0001] The invention relates to a steel for tank cars, in particular to a TC128GrB steel plate for tank cars and a production method thereof. Background technique [0002] Since the 1960s, most of the steel used for the tank body of liquefied gas tankers in my country is Q345R steel with a lower strength level (tensile strength Rm is 500MPa), resulting in a thicker tank wall thickness, resulting in the existing The tank car has a large weight coefficient, a small volume-to-weight ratio, and low carrying efficiency, which limits the large-scale (high parameter) development of domestic liquefied gas tank cars. Compared with advanced foreign countries, the self-weight coefficient of my country's tank trucks is about 30% higher than that of advanced countries such as Japan, Europe and the United States. Therefore, thinning, reducing the weight of the tank body and increasing the strength of the steel plate are a direction for the development of tank cars in our c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/16C22C38/14C22C38/12C22C33/04C21D8/00
Inventor 刘丹刘利香
Owner WUYANG IRON & STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap