A kind of ice crack product and preparation method thereof

A technology for ice cracks and products, which is applied in special decorative structures, decorative arts, filling slurry, etc., can solve the problems of inability to engrave, high cost, heavy pollution, etc., achieve low production cost, short cycle, and avoid high production cost Effect

Active Publication Date: 2017-05-03
黄山市徽漆工艺有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the above method can also form ice cracks through chemical reagents, it has defects such as high cost, heavy smell, heavy pollution, and inability to carry out subsequent engraving.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Taking wood blanks as an example, a method for preparing ice cracked products includes six steps: blank selection, preparation of pig blood putty, production of exposed pattern cloth, kneading, bonding and trimming, and decoration.

[0022] Specifically, the first step is to select the blank, that is, to select the wood and process it into the required size and shape. The second step is to prepare the pig blood putty, and its specific operation steps are as follows: firstly, fresh pig blood is filtered to obtain plasma. Then, the filtered plasma and lime water were mixed at room temperature at a ratio of 3:1 to prepare jelly-like blood material. The ratio of lime to water in the lime water was 1:5, and the mixing reaction time was 12 hours. Finally, fully stir the blood material and Shuangfei powder at a ratio of 1:3 to make pig blood material putty. The above-mentioned Shuangfei powder is produced by Tianbao White Jade Powder Factory in Jingdezhen City, Jiangxi Provin...

Embodiment 2

[0025] Taking the piece to be processed as porcelain as an example, except when preparing pig blood putty, blood plasma and lime water are mixed at a ratio of 3:1 under water-proof heating to obtain jelly-like blood material, and the mixing reaction time is 6 hours; the third When making the exposed pattern cloth in the first step, arrange the exposed pattern in the dryer to dry; the thickness of the pig blood putty coated on the cotton cloth or non-woven fabric is 0.3-0.5mm, and the exposed pattern in the fourth step kneading After the cloth is completely dry, fold it in half and press it in half, and fold it in half and press it several times until there are ice cracks with moderate cracks on the exposed cloth. All the other are with embodiment 1.

Embodiment 3

[0027] Take the plastic part to be processed as an example, except that the thickness of the pig's blood putty coated on the cotton cloth or non-woven fabric is 0.5-1mm; in the fourth step of kneading, after the exposed cloth is completely dry, fold it in half and knead it , and fold it in half and press it a few times, until the ice cracks with large cracks appear on the exposed cloth. All the other are with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ice crack product and a preparation method thereof. The preparation method comprises the following six steps: selecting blanks; preparing pig blood material putty; preparing exposure grain cloth; kneading; bonding and finishing; and decorating. The ice crack product is characterized by uniformly coating cotton cloth or a non-woven fabric with the prepared pig blood material putty to prepare the exposure grain cloth; after the exposure grain cloth is thoroughly dried, folding and kneading the cloth, wherein an ice crack pattern appears on the exposure grain cloth; then coating the other side of the exposure grain cloth with an adhesive; adhering the exposure grain cloth on a to-be-processed article; then finishing, spraying and decorating; and finally preparing the splendid ice crack product. According to the ice crack product, on the one hand, avoid the defects of high production cost, great energy consumption and great pollution caused by high-temperature firing can be avoided, and the ice crack product has the advantages of low production cost and short period; on the other hand, the ice crack product is formed by virtue of a physical modification method in the process, so that the size of the ice crack can be controlled. The ice crack product can be widely applied to woodware, porcelains, lacquerware, ironware and plastic artware and is worth of popularization and application.

Description

technical field [0001] The invention relates to the technical field of ice crack manufacture, and the manufacturing technology can be used to decorate woodware, porcelain, lacquerware, ironware, plastic handicrafts and other devices. Background technique [0002] "Ice crack" is called because the grains are broken like ice, the lobes are stacked, and it has a three-dimensional effect. It was first used in the ceramic firing process of the Han Dynasty. As one of the five famous kilns in the Song Dynasty in China, Zhejiang Longquan Ge Kiln produced Celadon products with cracks are treasured in the world, and "ice cracks" rank first among all kinds of patterns in Ge Kiln, known as "ice cracks are the best patterns". Unfortunately, due to the extremely complicated production process of ice cracks at that time, the production process was lost after the fall of the Southern Song Dynasty. [0003] In the contemporary era, Ye Xiaochun, a native of Longquan, Zhejiang Province, after...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B44C5/00C09D5/34
Inventor 奚建辉
Owner 黄山市徽漆工艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com