Low-temperature heat-sealing package film and preparation method thereof

A low-temperature heat-sealing and packaging film technology, which is applied in packaging, household packaging, and food packaging, can solve problems such as low sealing strength, high heat-sealing temperature, and unfavorable environmental protection, and achieve the effect of reducing heating temperature and improving product quality

Inactive Publication Date: 2015-12-09
李文东
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the domestic packaging film sealing technology generally adopts the glue sealing method, which has the following disadvantages: 1. Increased user pr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Embodiment 1: Three-layer die head, taking 20 micron low-temperature heat-sealing film as an example

[0019] Low-temperature heat-sealing layer A: 40% polyester aluminized, 47% polypropylene resin, 3% VM3980 thermoplastic elastomer;

[0020] Core layer B: 97% polypropylene, 1% antistatic smooth masterbatch;

[0021] Print layer C: 96% polypropylene, 2% anti-blocking agent.

[0022] The thickness distribution of each layer: the low-temperature heat-sealing layer A is 3 microns, the core layer B is 15 microns, and the printing layer C is 2 microns.

[0023] The above raw materials are mixed, melted and extruded, cast, stretched longitudinally, stretched transversely, drawn and trimmed, rolled, and then cut into finished products. The extrusion temperature during extrusion is 190-260°C, and the die head temperature is 248°C, the temperature of the quenching roll and the water tank during the casting process is 32°C; the longitudinal preheating temperature is 116-142°C, ...

Embodiment 2

[0025] Low-temperature heat-sealing layer A: 45% polyester aluminized, 50% polypropylene resin, 5% VM3980 thermoplastic elastomer;

[0026] Core layer B: 99% polypropylene, 3% antistatic smooth masterbatch;

[0027] Printing layer C layer: 98% polypropylene, 4% anti-anti-adhesive agent.

[0028] The thickness distribution of each layer: the low-temperature heat-sealing layer A is 3 microns, the core layer B is 15 microns, and the printing layer C is 2 microns.

[0029] The above raw materials are mixed, melted and extruded, cast, stretched longitudinally, stretched transversely, drawn and trimmed, rolled, and then cut into finished products. The extrusion temperature during extrusion is 190-260°C, and the die head temperature is 248°C, the temperature of the quenching roll and the water tank during the casting process is 32°C; the longitudinal preheating temperature is 116-142°C, the longitudinal stretching temperature is 126-135°C, the longitudinal setting temperature is 140...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Longitudinal stretch temperatureaaaaaaaaaa
Transverse stretch temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-temperature heat-sealing package film and a preparation method thereof. The heat-sealing package film includes an A layer, a B layer and a C layer, wherein the A layer is a low-temperature heat-sealing layer, the B layer is a core layer and the C layer is a printing layer. The A layer includes 40-45% of a polyester aluminum-plated film, 47-50% of polypropylene resin and 3-5% of a VM3980 thermoplastic elastomer; the B layer includes 97-99% of polypropylene and 1-3% of an anti-static smooth master batch; and the C layer includes 96-98% of polypropylene and 2-4% of an anti-adhesion agent. The preparation method includes the following steps: material blending, melt extrusion, sheet casting, longitudinal stretch, transversal stretch, drawing and trimming, rolling-up, cutting and production of the finish product. The package film reduces solvent pollution due to thin film printing and pre-coating treatment, is reduced in processing cost, and is reduced in cost and is environment-friendly. The method reduces the initial heat-sealing temperature of the heat-sealing package film and increases sealing strength of the package film product.

Description

technical field [0001] The invention relates to a film and a preparation method thereof, in particular to a low-temperature heat-sealing packaging film and a preparation method thereof. Background technique [0002] With the increasing awareness of environmental protection in the domestic printing industry, it is imperative to develop and apply "green" materials and processes that are pollution-free and pollution-free. Heat-sealing bags are widely used in daily chemical product packaging, food and drug packaging and other fields. Since the heat seal of the packaging bag is most likely to leak when the product is filled, and the damage of the packaging bag also occurs in the heat-sealed part during actual use, a good heat-sealing film can effectively improve the overall barrier performance of the packaging film. At present, the domestic packaging film sealing technology generally adopts the glue sealing method, which has the following disadvantages: 1. Increase the user's pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/08B32B27/32B32B27/20B32B15/20B32B15/09
CPCB32B27/08B32B15/09B32B15/20B32B27/20B32B27/32B32B2307/308B32B2439/00
Inventor 李文东
Owner 李文东
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap