A kind of water-based antirust paint and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A water-based anti-rust paint, water-based paint technology, applied in anti-corrosion coatings, polyester coatings, coatings, etc., can solve problems such as complex construction processes, and achieve good thermal stability, good anti-rust function, and safe use
Active Publication Date: 2016-10-19
LIAOYANG YIBANG NEW BUILDING MATERIALS GRP CO LTD
View PDF4 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] However, the above-mentioned water-based metal antirust paint adopts the mode of separate construction of primer and top coat, and the construction process is complicated.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0018] A water-based antirust paint of the present invention, taking blue as an example, it includes the following raw materials in parts by mass: 650 parts of acrylic modified alkyd resin emulsion, 113 parts of deionized water, 100 parts of pigment and filler, 9 parts of rheological agent 1 part, 4 parts of dispersant, 2 parts of wetting agent, 3 parts of defoamer, 1 part of bactericide, 80 parts of film-forming aid, 20 parts of co-solvent, 5 parts of flash rust agent, 6 parts of multi-functional additive, thickener 6 parts of drug solution.
[0019] The above-mentioned pigments and fillers include 20 parts of R501 titanium dioxide, 10 parts of phthalocyanine blue pigment, 20 parts of precipitated barium sulfate, and 50 parts of aluminum tripolyphosphate;
example 2
[0021] A water-based antirust paint of the present invention, taking yellow as an example, it includes the following raw materials in parts by mass: 650 parts of acrylic modified alkyd resin emulsion, 115 parts of deionized water, 100 parts of pigment and filler, and 9 parts of rheological agent , 4 parts of dispersant, 2 parts of wetting agent, 3 parts of defoamer, 1 part of bactericide, 80 parts of film-forming aid, 20 parts of co-solvent, 5 parts of flash rust agent, 6 parts of multi-functional additive, thickener 4 parts of the solution.
[0022] The above-mentioned pigments and fillers include 20 parts of R501 titanium dioxide, 60 parts of medium chrome yellow powder, and 20 parts of aluminum tripolyphosphate;
example 3
[0024] A water-based antirust paint of the present invention, taking gray as an example, it includes the following raw materials in parts by mass: 650 parts of acrylic modified alkyd resin emulsion, 115 parts of deionized water, 100 parts of pigment and filler, and 9 parts of rheological agent , 4 parts of dispersant, 2 parts of wetting agent, 3 parts of defoamer, 1 part of bactericide, 80 parts of film-forming aid, 20 parts of co-solvent, 5 parts of flash rust agent, 6 parts of multi-functional additive, thickener 8 parts of the solution.
[0025] The above-mentioned pigments and fillers include 25 parts of R501 titanium dioxide, 15 parts of iron black powder, 20 parts of aluminum tripolyphosphate, and 40 parts of precipitated barium sulfate;
[0026] Preferably, the mass-number ratio of thickener to water in the thickener solution is 1:1.
[0027] The preparation process steps of water-based antirust paint are as follows:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
An aqueous anti-rusting paint and a preparation method therefor. The paint is characterized in that: the raw materials in a formula in parts by mass are as follow: 600-700 parts of an acrylate modified alkyd resin emulsion, 100-120 parts of deionized water, 90-110 parts of pigments and fillers, 5-10 parts of a rheological agent, 5-10 parts of a dispersant, 1-5 parts of a defoamer, 1-3 parts of a bactericide, 70-90 parts of film forming auxiliaries, 15-25 parts of a co-solvent, 3-8 parts of a flash-rust agent, 5-10 parts of a multi-functional agent and 4-10 parts of a thickener solution. The process steps comprises: dispersing, milling, paint mixing, thickening, filtering and packaging. According to the present invention, water is used as a dispersion medium, multiple anti-rusting mechanism of physical, chemical and the like are used to prepare and produce the anti-rusting industrial paint. The paint combines an undercoat and a finishing coat and is constructed at one-time, so that the mode that the undercoat and the finishing coat of the conventional paint are constructed separately is broken. The paint is unequalled in environmental protection performance, good in salt-spray resistance and weather resistance and strong in anti-rusting function, and is an excellent product of a new generation that can replace the traditional anti-rusting paint. The paint has water solubility and non-flammable property, and is safe in use, and the paint is good in water resistance and good in thermal stability, and has a good anti-rusting function even in a high-temperature state.
Description
technical field [0001] The invention belongs to the technical field of paint manufacture, and in particular relates to a water-based antirust paint with an acrylic modified alkyd resin emulsion as a base material and a preparation method thereof. Background technique [0002] The antirust paint currently used is roughly two types: oily and water-based. Oil-based antirust paint makes it difficult to remove the greasy surface of the material, so it is rarely used. Oil-based antirust paint is easy to use and low in price, but because it contains toxic substances such as nitrite and chromate, it is harmful to operators. Rust requirements. [0003] The water-based metal anti-rust paint is made of metal strong chelating agent phytate as the main component, and is compounded with several other water-based additives. Phytate is a natural non-toxic organic chemical product extracted from food crops. When it is used as an antirust agent for magnetic materials, it can quickly chelat...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D167/08C09D5/08
Inventor 崔桐嘉孙宝财
Owner LIAOYANG YIBANG NEW BUILDING MATERIALS GRP CO LTD