A ballistic-proof and anti-stab technology and preparation technology, which is applied in the field of preparation technology and preparation technology of flexible bullet-proof and anti-stab structures, can solve the problems of limited application occasions, poor high temperature resistance, high material cost, etc., and achieve low production cost and long service life , The effect of simple preparation process

Active Publication Date: 2018-12-18
SUZHOU GAOJIA PROTECTION TECH CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned technical solution has the following disadvantages: (1) metal materials have limited application occasions and are easily detected, and the material is relatively hard, not soft, and heavy; (2) high-strength polyethylene or aramid non-woven fabrics use water-based polyurethane glue Bonding has only a 5-year shelf life, and the cost is also high. In addition, the cost of this non-weft material is high; (3) The high temperature resistance is poor, and the performance drops significantly above 80 °C

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of a flexible bullet-proof and stab-proof structure
  • Preparation process of a flexible bullet-proof and stab-proof structure
  • Preparation process of a flexible bullet-proof and stab-proof structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Embodiment one, as attached figure 1 Shown, the preparation technology of flexible bullet-proof stab-proof structure of the present invention, mass proportion is 75% polycarbonate, mass proportion is 20% glass fiber and auxiliary components such as a certain amount of fire retardant, toughening agent, color particle ( Content at 5%) after mixing and stirring, put into the injection molding machine 1. Among them, flame retardants, tougheners, color particles and other additives play a role in improving the performance and appearance of protective materials. Two groups of symmetrical injection molds 2 that can be injection molded at the same time are arranged at the opposite positions in the left and right directions on the injection molding machine 1 , and then the base cloth 3 is laid between the symmetrical injection molds 2 . The base fabric 3 is in the shape of a strip, one end is wound on the shrink tube 4, and the other end extends downwards, and then stretched by...

Embodiment 2

[0032] Embodiment 2, the preparation process of the flexible bullet-proof and stab-proof structure of the present invention, the mass specific gravity is respectively 65% ​​nylon 66, mixed with the mass specific gravity of 35% carbon fiber short fiber, and then put into the injection molding machine 1. Two groups of symmetrical injection molds 2 that can be injection molded at the same time are arranged at the opposite positions in the left and right directions on the injection molding machine 1 , and then the base cloth 3 is laid between the symmetrical injection molds 2 . The base fabric is in the shape of a long strip, one end is wound on the shrink tube 4, and the other end extends downwards, and then it is stretched by the transmission mechanism 5, wherein the base fabric is a fabric made of interlaced carbon fiber and aramid fibers, and the weight of the material ranges from 200 grams / square meter, the thickness is 0.15mm, on the basis of ensuring the strength, it makes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparing technology for a flexible bullet-proof and piercing-proof structure. The preparing technology specifically comprises the following preparing steps that firstly, a protection composite particle material is prepared; secondly, base cloth is laid between two sets of injection molds of an injection molding machine, the protection composite particle material is arranged on the two sides of the base cloth in an injection molding manner through the injection molds at the same time, the protection composite particle material is subjected to hot melting, seeps into a base cloth layer and then is cured to form a two-face protection material layer, mold opening is conducted, after the base cloth of an injection molding part is downwards transmitted, the base cloth is tensioned, and then injection molding is conducted; and thirdly, a flexible gap is machined. The structure of the product prepared through the preparing technology has excellent bullet-proof and piercing-proof performance and also has improved flexibility performance. A thermoplastic material and an enhanced material composite material are arranged on the adopted base cloth in an injection molding manner, the thermoplastic material and the enhanced material composite material are subjected to hot melting, seep into the base cloth layer and then are cured to form the two-face protection material layer, gaps among particles of the thermoplastic material and the enhanced material composite material can be eliminated, and the structure is compact and has more excellent bullet-proof and piercing-proof performance; and in addition, the preparing technology is simple, and the production efficiency is high.

Description

technical field [0001] The invention relates to a preparation process, in particular to a preparation process of a flexible bulletproof and stab-proof structure, which is applied in the technical field of composite materials for human life safety protection. Background technique [0002] Body armor is a kind of equipment that can absorb and dissipate the energy of warheads, prevent penetration, reduce blunt trauma and effectively protect the protective parts of the human body. Stab-proof clothing is a kind of clothing that can effectively protect the human body from various angles and reduce the threat of stab wounds to the protective parts of the human body. They are protective equipment that public security officers and security personnel must wear when performing dangerous tasks to protect the main organs of public security officers and security personnel from damage caused by common offensive weapons such as bullets and daggers. [0003] At present, the international an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B29C70/50B29C70/54
CPCB29C70/50B29C70/504B29C70/545
Inventor 谢正权姜华李刚
Owner SUZHOU GAOJIA PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products