Ceramic glaze with stable performance and preparation method thereof

A ceramic glaze and stable technology, which is applied in the field of ceramic glaze and its preparation, can solve the problems of insufficient smoothness of the surface, low sintering hardness of the glaze, and insufficient stability of performance, so as to enhance hydrophobicity and weather resistance, and improve stain resistance. Aging ability, strong anti-scratch effect

Inactive Publication Date: 2021-03-19
江西亚航科技有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional glazes tend to produce air bubbles and uneven glazing during use, which leads to the surface of ceramic products not smooth enough, easy to stain, and difficult to clean; also the glaze has low sintering hardness and is easy to scratch during use, which further leads to its Poor stain resistance and wear resistance, not stable performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A ceramic glaze with stable performance, including the following raw materials in parts by weight: 18 parts of quartz, 10 parts of levodolite, 5 parts of frit, 3 parts of modified nano-silica composite graphene oxide, 3 parts of boric acid, silicic acid 10 parts of zirconium, 6 parts of calcite, 2 parts of strontium titanate, 2 parts of barium carbonate, 0.5 part of ammonium dihydrogen phosphate, 0.5 part of zinc oxide and 0.5 part of zinc hexafluorosilicate.

[0033] A preparation method of a ceramic glaze with stable performance, comprising the following steps:

[0034] S1. Preparation of modified nano-silica composite graphene oxide:

[0035] S11. Take 1 part of nano silicon dioxide, 1 part of silicon micropowder, dispersant Disponer 929, defoamer Deform 6800 and wetting agent alkyl sodium sulfate, add them into deionized water, stir and disperse for 60 minutes, and prepare nano Silica emulsion;

[0036] S12, preparation mass concentration is 10% trimethylolpropane...

Embodiment 2

[0041] A ceramic glaze with stable performance, comprising the following raw materials in parts by weight: 18 parts of quartz, 10 parts of levodolite, 15 parts of frit, 10 parts of modified nano-silica composite graphene oxide, 10 parts of boric acid, silicic acid 3 parts of zirconium, 2 parts of calcite, 2 parts of strontium titanate, 6 parts of barium carbonate, 3 parts of ammonium dihydrogen phosphate, 3 parts of zinc oxide, 3 parts of zinc hexafluorosilicate, 0.1 part of sodium nitrite.

[0042] A preparation method of a ceramic glaze with stable performance, comprising the following steps:

[0043]S1. Preparation of modified nano-silica composite graphene oxide:

[0044] S11. Take 5 parts of nano-silica, 1 part of silicon micropowder, dispersant EFKA SL 3034, defoamer Efka SL 2038 and wetting agent sodium sulfonate, add them into deionized water, stir and disperse for 60 minutes, and prepare 2.5% mass concentration Nano silica emulsion;

[0045] S12, preparation mass co...

Embodiment 3

[0050] A ceramic glaze with stable performance, including the following raw materials in parts by weight: 12 parts of quartz, 17 parts of levodolite, 10 parts of frit, 8 parts of modified nano-silica composite graphene oxide, 6 parts of boric acid, silicic acid 5 parts of zirconium, 4 parts of calcite, 4 parts of strontium titanate, 3 parts of barium carbonate, 1 part of ammonium dihydrogen phosphate, 2 parts of zinc oxide, 2 parts of hydroxyfluorosilicone oil, 0.5 parts of sodium nitrite, and 0.5 parts of sodium nitrate.

[0051] A preparation method of a ceramic glaze with stable performance, comprising the following steps:

[0052] S1. Preparation of modified nano-silica composite graphene oxide:

[0053] S11. Take 3 parts of nano silicon dioxide, 2 parts of silicon micropowder, dispersant Dow Corning 51, defoamer SRE-CN and wetting agent alkyl sulfate, add them into deionized water, stir and disperse for 60 minutes, and prepare a mass concentration of 2.0% Nano silica emu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of ceramic glaze production, and provides a ceramic glaze with stable performance and a preparation method thereof. The ceramic glaze is prepared from 10-18 parts of quartz, 10-18 parts of Zuoyun soil, 5-15 parts of frit, 3-10 parts of modified nano silicon dioxide compounded graphene oxide, 3-10 parts of boric acid, 3-10 parts of zirconium silicate, 2-6 parts of calcite, 2-6 parts of strontium titanate, 2-6 parts of barium carbonate, 0.5-3 parts of ammonium dihydrogen phosphate, 0.5-3 parts of zinc oxide and 0.5-3 parts of fluorine-containing auxiliaries. The preparation method comprises the following steps: S1, preparing modified nano silicon dioxide compounded graphene oxide; S2, crushing and sieving; and S3, preparing slurry. The hardness and wear resistance of the glaze can be greatly improved, the glaze layer is compact in structure and can fill pores in the surface of a ceramic matrix, the stain resistance and cold resistance of a ceramic product are improved, and the obtained glaze is high in quality, stable in performance and long in service life.

Description

technical field [0001] The invention relates to the technical field of ceramic glaze production, in particular to a ceramic glaze with stable performance and a preparation method thereof. Background technique [0002] Glaze refers to a glassy thin layer covering the ceramic body, but its composition is more complex than glass, and its properties and microstructure are also quite different from glass. For example, its high temperature viscosity is much greater than that of glass, and its composition and The preparation process is similar to the blank and different from glass. The function of glaze is to improve the surface properties of ceramic products, make the surface of the product smooth, impermeable to liquid and gas, and not easy to be stained. Secondly, it can improve the mechanical strength and electrical properties of the product. Performance, chemical stability and thermal stability. Glaze also plays a decorative role on the body. It can cover the bad color and rou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20
CPCC03C8/20
Inventor 涂祈林
Owner 江西亚航科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap