A ceramic tile surface glaze with high whiteness and preparation method thereof

A ceramic tile, high whiteness technology, applied in the field of ceramic tile glaze, can solve the problem of not appearing ideal, and achieve the effects of good post-processing performance, close color and good luster.

Active Publication Date: 2020-03-27
FOSHAN OCEANO CERAMICS
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is imperative to improve the whiteness of the glaze, but in the existing glaze formulation system, it is difficult to increase the whiteness of the glaze to more than 80 degrees only by adding zirconium silicate to the glaze, so there is no ideal high-grade glaze on the market. Whiteness ceramic tile surface glaze, so the industry urgently needs to develop a glaze whose whiteness is better than the glaze effect of the existing product whiteness to meet the needs of design

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A ceramic tile surface glaze with high whiteness and preparation method thereof
  • A ceramic tile surface glaze with high whiteness and preparation method thereof
  • A ceramic tile surface glaze with high whiteness and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A ceramic tile surface glaze with high whiteness, which is composed of the following raw material components in parts by weight:

[0025]

[0026] Wherein, the glaze powder includes the following raw material components in parts by weight:

[0027]

[0028] The potassium sodium stone powder is formed by mixing potassium feldspar and albite at a ratio of 1:1 by weight; the quartz powder is high-purity quartz powder with a purity of 98% to 99%; the alumina is α- Aluminum oxide; the chemical composition of the glaze: SiO 2 : 55.47%, Al 2 o 3 : 27.24%%, Fe 2 o 3 : 0.05%, TiO 2 : 3.21%, CaO: 4.69%, MgO: 0.64%, K 2 O: 1.94%, Na 2 O: 2.60%, ZnO: 1.0%, loss on ignition: 3.14%; the zirconium content in the zirconium silicate is not more than 24.5% of the total weight of the surface glaze raw materials; the carboxymethyl cellulose is a high-viscosity methyl group, its The viscosity is greater than 300mPa.s.

[0029] Preparation:

[0030] Mix the raw material compo...

Embodiment 2

[0033] A ceramic tile surface glaze with high whiteness, which is composed of the following raw material components in parts by weight:

[0034]

[0035] Wherein, the glaze powder includes the following raw material components in parts by weight:

[0036]

[0037]

[0038] The potassium sodium stone powder is formed by mixing potassium feldspar and albite at a ratio of 1:1 by weight; the quartz powder is high-purity quartz powder with a purity of 98% to 99%; the alumina is α- Aluminum oxide; chemical composition of the glaze: SiO 2 : 52.57%, Al 2 o 3 : 24.32%%, Fe 2 o 3 : 0.05%, TiO 2 : 7.15%, CaO: 7.14%, MgO: 0.57%, K 2 O: 1.74%, Na 2 O: 2.32%, ZnO: 0.89%, loss on ignition: 2.81%; the zirconium content in the zirconium silicate is not more than 24.5% of the total weight of the surface glaze raw materials; the carboxymethyl cellulose is a high-viscosity methyl group, its The viscosity is greater than 300mPa.s.

[0039] Preparation:

[0040] Mix the raw materia...

Embodiment 3

[0043] A ceramic tile surface glaze with high whiteness, which is composed of the following raw material components in parts by weight:

[0044]

[0045] Wherein, the glaze powder includes the following raw material components in parts by weight:

[0046]

[0047] The potassium sodium stone powder is formed by mixing potassium feldspar and albite at a ratio of 21:22 by weight; the quartz powder is high-purity quartz powder with a purity of 98% to 99%; the alumina is α- Aluminum oxide; the chemical composition of the glaze powder: SiO 2 : 53.27%, Al 2 o 3 : 23.19%%, Fe 2 o 3 : 0.05%, TiO 2 : 7.67%, CaO: 7.22%, MgO: 0.79%, K 2 O: 2.03%, Na 2 O: 2.74%, ZnO: 0.83%, loss on ignition: 2.22%; the zirconium content in the zirconium silicate is not more than 24.6% of the total weight of the surface glaze raw materials; the carboxymethyl cellulose is a high-viscosity methyl group, its The viscosity is greater than 300mPa.s.

[0048] Preparation:

[0049] Mix the raw mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
viscosityaaaaaaaaaa
whitenessaaaaaaaaaa
Login to view more

Abstract

The invention discloses ceramic tile overglaze with high brightness. The ceramic tile overglaze comprises, by weight parts, 80-120 parts of overglaze powder, 10-28 parts of zirconium silicate, 0.25-0.35 part of sodium tripolyphosphate, 0.2-0.4 part of carboxymethyl cellulose and 35-50 parts of water. By adjusting overglaze raw material ingredients and proportions and particularly by optimizing the added amounts of titanite and zirconium silicate in the overglaze powder, the ceramic tile overglaze has high brightness and has good postprocessing property, and apparent mass problems such as pinholes, blistering and deformation after application of the ceramic tile overglaze are solved.

Description

technical field [0001] The invention relates to the field of ceramic tile glaze, in particular to a ceramic tile surface glaze with high whiteness and a preparation method thereof. Background technique [0002] At present, the texture of high-quality stone on the market is better than that of glazed tiles. One of the most important items is the whiteness of the background color. The whiteness of high-quality white stone can reach 75 to 85 degrees or even higher. The whiteness that the current ceramic tile production process in the building materials industry can achieve is only 64 to 67 degrees. Especially the marble-like ceramic tiles have higher and higher requirements for the whiteness of the glazed surface. In order for ceramic products to obtain a texture closer to stone, and even obtain an artistic expression effect beyond stone. It is imperative to improve the whiteness of the glaze, but in the existing glaze formulation system, it is difficult to increase the white...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/20
CPCC03C8/20
Inventor 赵光岩黄星刘俊荣
Owner FOSHAN OCEANO CERAMICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap