Antistatic shirt collar compound velvet two-piece suit and production process thereof

A production process and technology for shirt collars, which are applied in the field of antistatic shirt collar velvet two-piece suits and their production technology, can solve the problems of uneven appearance and large static electricity problems of the two-piece suits, so as to improve wearing experience and washability. Good, functional warmth

Pending Publication Date: 2018-01-09
桐乡市百代服饰有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The problem to be solved by the present invention is that the appearance of the existing two-piece suit is not smooth, and the problem of static electricity is relatively large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antistatic shirt collar compound velvet two-piece suit and production process thereof
  • Antistatic shirt collar compound velvet two-piece suit and production process thereof
  • Antistatic shirt collar compound velvet two-piece suit and production process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] Add 45kg of adipic acid, 12kg of hexamethylenediamine, 35kg of polyetheramine, 0.2kg of phosphite, 3kg of silane coupling agent, and 2kg of carbodiimide into the reaction kettle at the same time and stir to raise the temperature to form a mixture. Turn on the motor and powder condenser And the cooling water of the total condenser pipeline; when the temperature in the tank rises to 120°C, turn off the heat medium and stir for 1 hour; The cooling water is half open, when the temperature rises to 250°C, add 3kg of sodium hypophosphite, and vacuumize, the vacuum degree is -0.1Mpa, and react for 1 hour; after reacting for 1 hour, turn off the vacuum, and cool the temperature in the tank to 180°C. Start unloading to obtain the antistatic agent, and dip the two-piece shirt collar fuzzing into the antistatic agent for padding treatment.

Embodiment 2

[0049] Add 50kg of adipic acid, 10kg of hexamethylenediamine, 35kg of polyether amine, 0.2kg of phosphite, 1kg of silane coupling agent, and 1kg of carbodiimide into the reaction kettle at the same time and stir to raise the temperature to form a mixture. Turn on the motor and powder condenser And the cooling water of the total condenser pipeline; when the temperature in the tank rises to 120°C, turn off the heat medium and stir for 1 hour; The cooling water is half open, when the temperature rises to 250°C, add 3kg of sodium hypophosphite, and vacuumize, the vacuum degree is -0.1Mpa, and react for 1 hour; after reacting for 1 hour, turn off the vacuum, and cool the temperature in the tank to 180°C. Start unloading to obtain the antistatic agent, and dip the two-piece shirt collar fuzzing into the antistatic agent for padding treatment.

Embodiment 3

[0051] Add 45kg of adipic acid, 12kg of hexamethylenediamine, 35kg of polyetheramine, 0.2kg of phosphite, 3kg of silane coupling agent, and 2kg of carbodiimide into the reaction kettle at the same time and stir to raise the temperature to form a mixture. Turn on the motor and powder condenser And the cooling water of the total condenser pipeline; when the temperature in the tank rises to 120°C, turn off the heat medium and stir for 1 hour; The cooling water is half open, when the temperature rises to 250°C, add 3kg of sodium hypophosphite, and vacuumize, the vacuum degree is -0.1Mpa, and react for 1 hour; after reacting for 1 hour, turn off the vacuum, and cool the temperature in the tank to 180°C. Start unloading to obtain the antistatic agent, and dip the two-piece shirt collar fuzzing into the antistatic agent for padding treatment.

[0052] In order to prove the antistatic performance, with the two-piece suit of shirt collar fuzz in the present invention as the experimenta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an antistatic shirt collar compound velvet two-piece suit and a production process thereof. The antistatic shirt collar compound velvet two-piece suit comprises an inner layer,an outer layer and a false layer, the inner layer is a flannelette layer, the outer layer is a knitting fabric layer, the false layer is a shirt collar layer, the inner layer is spliced with the falselayer, the outer layer wraps the inner layer, and antistatic layers are arranged on the surfaces of the inner layer and the outer layer. The two-piece suit solves the problem of corner angles of theouter surface of an existing two-piece suit, is more comfortable to wear, quite novel in style, high in grade and good in heat insulating ability and has good static electricity resistance and wash resistance.

Description

technical field [0001] The invention relates to the field of functional clothing, in particular to a two-piece antistatic shirt collar plus fleece and a production process thereof. Background technique [0002] Knitted fabric refers to the fabric formed by sequentially bending yarns into coils, and the coils are intertwined with each other. The process of yarn forming coils can be carried out horizontally or vertically. Horizontal weaving is called weft knitting, while longitudinal weaving is called weft knitting. Warp-knitted fabrics and knitted fabrics are divided into basic weaves, variable weaves and color weaves according to the coil structure and mutual arrangement. The basic weave is the basis of all knitted fabrics and consists of loops combined in the simplest possible way. Such organizations include weft knitting, ribbing, double reverse, warp knitting chain, warp flat, warp satin and so on. The change organization is formed by arranging another or several other ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(China)
IPC IPC(8): A41D1/04A41D31/02D03D15/00D06M13/192D06M13/332D06M15/53D06M13/292D06M11/70D06M101/06D06M101/34D06M101/32D06M101/12
Inventor吴家明
Owner桐乡市百代服饰有限公司