A processing and baking technology, applied in the direction of fiber processing, plant fibers, fibers affecting crease behavior, etc., can solve the problem of weakening anti-wrinkle performance of POLO shirts, and achieve the effect of improving anti-wrinkle performance.

Active Publication Date: 2019-01-08
BEIJING BAO LUO SHENGSHI GARMENTS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nowadays, people are more and more pursuing wearing comfort, but this will cause the anti-wrinkle performance of POLO shirts to weaken

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • An anti-wrinkle treatment process for polo shirts
  • An anti-wrinkle treatment process for polo shirts

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1: A POLO shirt anti-wrinkle treatment process, the POLO shirt is composed of 85% pure cotton by mass and 15% polyester by mass, including the following steps: 1) Put the prepared POLO shirt into the mixed solution Soaking, soaking time 1h, mixed solution includes 6 parts of MgCl in parts by mass 2 ·6H 2 0, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acid; 2) the POLO shirt after soaking is carried out padding, and the liquid rolling rate is 72%; 3) the POLO shirt after 2) is baked, and the baking temperature 132°C, bake for 3 minutes.

Embodiment 2

[0024] Embodiment 2: A POLO shirt anti-wrinkle treatment process, the POLO shirt is composed of 85% pure cotton by mass and 15% polyester by mass, including the following steps: 1) Put the prepared POLO shirt into the mixed solution Soaking, soaking time 1h, mixed solution includes 6 parts of MgCl in parts by mass 2 ·6H 2 0, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acid; 2) the POLO shirt after soaking is carried out padding, and the liquid rolling rate is 72%; 3) the POLO shirt after 2) is baked, and the baking temperature 136°C, bake for 3 minutes.

Embodiment 3

[0025] Embodiment 3: A POLO shirt anti-wrinkle treatment process, the POLO shirt is composed of 85% pure cotton by mass and 15% polyester by mass, including the following steps: 1) Put the prepared POLO shirt into the mixed solution Soaking, soaking time 1h, mixed solution includes 6 parts of MgCl in parts by mass 2 ·6H 2 0, 7 parts of BTCA, 94 parts of acrylic resins, 4 parts of citric acid; 2) the POLO shirt after soaking is carried out padding, and the liquid rolling rate is 72%; 3) the POLO shirt after 2) is baked, and the baking temperature 141°C, bake for 3 minutes.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a wrinkle-resisting treatment technology for a POLO shirt. The POLO shirt is prepared from purified cotton with mass percent of 85 percent mass or above and dacron with mass percent of 10 percent or above. The wrinkle-resisting treatment technology comprises the following steps: firstly, putting the prepared POLO shirt into a mixed solution and soaking for 1 hour, wherein the mixed solution is prepared from the following components in parts by mass: 6 to 8 parts of MgCl2.6H2O, 7 parts of BTCA, 93 to 95 parts of acrylic resin and 2 to 4 parts of citric acid; secondly, padding the soaked POLO shirt, wherein the mangle expression is 75 percent; thirdly, baking the POLO shirt subjected to the treatment in the second step at the baking temperature of 130 to 160 DEG C for0.2 hour. According to the technical scheme, firstly, the raw material of the POLO shirt is more inclined to the purified cotton, the amount of the purified cotton is 85 percent, and the overall wearing is more comfortable; in addition, by adopting the process to carry out the wrinkle-resisting treatment, the POLO shirt has good wrinkle resistance.

Description

technical field [0001] The invention relates to anti-wrinkle treatment of clothes, in particular to an anti-wrinkle treatment process for POLO shirts. Background technique [0002] Polo shirts were originally called tennis shirts, which were originally worn by nobles when they played polo. Because of their comfort, they like to wear short-sleeved clothes with collars. Over time, it was called "polo shirt" (polo shirt), and later became popular with the public, so it evolved into general casual clothing. [0003] The structure of the POLO shirt is generally the same as the patent disclosure of CN206576313U as the notification number, including the clothes body, and the POLO shirt arranged on the top of the clothes body; and the sleeves arranged on both sides of the clothes body top. [0004] Existing POLO shirts are generally made of pure cotton or pure cotton + polyester. The more pure cotton content, the better the wearing comfort. The larger the proportion of polyester, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): D06M15/263D06M11/155D06M13/207D06M11/56D06M101/06D06M101/32
CPCD06M11/155D06M11/56D06M13/207D06M15/263D06M2101/06D06M2101/32D06M2200/20
Inventor杜春柏
OwnerBEIJING BAO LUO SHENGSHI GARMENTS CO LTD