Rubber material and preparation method thereof

A technology of rubber materials and natural rubber, which is applied in the field of rubber materials, can solve the problems that it is difficult to meet the technical requirements of automobiles, natural rubber materials are not resistant to high temperature thermal oxygen aging, ozone resistance, and poor weather resistance, so as to achieve easy implementation and improve durability. High temperature thermal oxygen aging ability, the effect of prolonging the service life of high temperature fatigue resistance

Inactive Publication Date: 2018-07-06
JIANXIN ZHAOS GRP CORP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Due to the characteristics of natural rubber materials that are not resistant to high temperature thermal oxygen aging, ozone resistance and weather resistance, it is difficult to meet the continuously improving technical requirements of the automotive industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rubber material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The rubber material of the present invention uses part of PDM as auxiliary vulcanizing agent and effective modifier in the natural rubber sulfur vulcanization system to achieve the purpose of improving the high temperature resistance, heat resistance and oxygen aging resistance of natural rubber.

[0019] The raw materials of the rubber material include: 100 parts by weight of natural rubber, 0.5-1.5 parts by weight of sulfur, 0.5-1.5 parts by weight of PDM, 1-2.5 parts by weight of vulcanization aid, 5-10 parts by weight of anti-aging agent, 4-10 parts by weight of zinc oxide The parts by weight are 4-8 parts by weight of white carbon black, 10-30 parts by weight of carbon black, and 4-8 parts by weight of softener. The vulcanizing agent, vulcanization aid, anti-aging agent, zinc oxide and white carbon black are all called fine materials, and the carbon black and softener are all called coarse materials. The vulcanization aid can be MBT (2-mercaptobenzothiazole), MBTS ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a rubber material. The rubber material comprises the following raw materials: 100 parts by weight of natural rubber, 0.5-1.5 parts by weight of sulfur, 0.5-1.5 parts by weightof PDM, 1-2.5 parts by weight of a vulcanization auxiliary agent, 5-10 parts by weight of an anti-aging agent, 4-10 parts by weight of zinc oxide, 4-8 parts by weight of white carbon black, 10-30 parts by weight of carbon black, and 4-8 parts by weight of a softener. The invention also provides a preparation method of the above rubber material. The rubber material provided by the invention has high-temperature resistance, heat resistance and aging resistance, and the rubber preparing process is simple and easy to implement.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to a rubber material and a preparation method thereof. Background technique [0002] The automotive industry has continuously improved the heat and oxygen aging resistance requirements of natural rubber shock absorbers, especially for products such as rubber shock absorbers for automobile engines and rubber shock absorbers for gearboxes, which are required to withstand high-intensity heat in ultra-high temperature and ultra-long-term environments. Oxygen aging can meet the development needs of high temperature thermal oxygen aging dynamic fatigue performance in the automotive industry. [0003] Due to the characteristics of natural rubber materials that are not resistant to high temperature thermal oxygen aging, ozone resistance and weather resistance, it is difficult to meet the continuously improving technical requirements of the automotive industry. Improving and improv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/00C08L91/00C08K13/02C08K3/06C08K5/00C08K5/47C08K5/40C08K3/011B29B7/00
Inventor 胡旻晓胡海勤李恒荣汪海峰汪挺
Owner JIANXIN ZHAOS GRP CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap