Optimization method and processing step of high-end hot work die steel

A technology of hot work die steel and optimization method, applied in the field of mechanical parts forming, can solve the problems of inconsistent mechanical properties of the die in all directions, die failure, etc., to achieve excellent thermal crack resistance, improved service life, good thermal strength and toughness Effect

Inactive Publication Date: 2018-07-10
浙江嵊州元丰模具有限公司
View PDF2 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After thermal processing and annealing, carbon-poor areas and carbon-rich areas are alternately distributed to form a ba

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optimization method and processing step of high-end hot work die steel
  • Optimization method and processing step of high-end hot work die steel
  • Optimization method and processing step of high-end hot work die steel

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0028] Example 1:

[0029] Take YFH-17 steel as an example,

[0030] 1. The chemical composition formula (weight ratio) of trace elements of YFH-17 die steel, please refer to the following table.

[0031] chemical composition

[0032] It can be seen from the above table:

[0033] The content of molybdenum (MO) in YFH-17 steel breaks the upper limit of the H13 standard of 1.75 and is greatly increased to above 2.20, which can refine the steel's grains, improve hardenability and thermal strength, and maintain sufficient strength and creep resistance at high temperatures Variable capacity (the gradual deformation that occurs when working at high temperature for a long time is called creep).

[0034] At the same time, YFH-17 steel greatly reduces the content of vanadium (V) below the lower limit of the H13 standard, and the vanadium content in the steel is generally not more than 0.5%. Vanadium has a strong affinity with carbon, ammonia, and oxygen, and forms corresponding stable compo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an optimization method and a processing step of high-end hot work die steel. On the basis of national standard die steel H13, an optimized raw material formula, an optimized melting process and an optimized heat treatment process are adopted, and the high stability of the H13 is combined, so that heat fatigue resistance and tempering resistance are further improved, better hot strength and toughness are realized, and the service life of a die is remarkably improved. The optimization method and the processing step of the high-end hot work die steel have the following characteristics and advantages of (1) high purity and prolonged fatigue life of the die; (2) high isotropy and excellent shock cracking resistance; (3) excellent toughness and excellent wear resistance; (4) excellent hardenability and dimension stability during high-temperature heat treatment; and (5) excellent hot flush corrosion resistance and excellent hot fracturing resistance.

Description

technical field [0001] The invention relates to the technical field of forming mechanical parts, in particular to an optimization method and process steps of a high-end hot work die steel. Background technique [0002] With the rapid development of the mold industry, more and more parts are formed by die-casting, hot extrusion and hot forging. At present, the hot work die steel widely used in my country is mainly the national standard H13 (4Cr5MoSiV1), which has good toughness and thermal fatigue properties. The demand for aluminum die-casting molds and hot forging molds for components is growing exponentially, and more than 100 million sets of such molds are opened every year. [0003] The service conditions of aluminum alloy die-casting molds and hot forging molds are relatively harsh. The temperature of the aluminum alloy melt is usually around 650-700°C, and the temperature of hot forged products is around 1000°C. The mold must be in contact with high-temperature metal d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/22C22C38/24C22C38/02C22C38/04C22C33/04C21D8/00
CPCC21D8/005C22C33/04C22C38/005C22C38/02C22C38/04C22C38/22C22C38/24
Inventor 范国勇
Owner 浙江嵊州元丰模具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap