A preparation method and application of a capacitor material with a 3D hollow structure

A hollow structure, capacitor technology, used in hybrid capacitor electrodes, nanotechnology for materials and surface science, nanotechnology, etc., can solve problems such as complex process, achieve a wide contact area, excellent electrochemical performance The effect of improving transmission efficiency

Active Publication Date: 2019-08-23
QINGDAO UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these methods have certain risks and hazards, and the process is relatively complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method and application of a capacitor material with a 3D hollow structure
  • A preparation method and application of a capacitor material with a 3D hollow structure
  • A preparation method and application of a capacitor material with a 3D hollow structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] In this embodiment, cobalt chloride, nickel chloride, ammonium fluoride, sodium sulfide, urea and silk are used as experimental raw materials, and the specific preparation process is as follows:

[0021] (1) Take 50ml of sodium carbonate solution with a mass fraction of 5% and place it in a 100ml beaker, immerse the silkworm cocoons in the solution, heat it to 100°C by means of oil bath heating and keep it warm for 30min, then use the obtained silk to remove Wash with deionized water several times, and dry at 60°C for 12 hours;

[0022] (2) Take by weighing reagent 1mmol nickel chloride (0.2377g), 2mmol cobalt chloride (0.4759g), 10mmol urea (0.6006g), 10mmol ammonium fluoride (0.3700g), be dissolved in the beaker of 50mL deionized water, In the process of adding the reagent, the solution needs to be stirred continuously until a clear pink solution is formed; then the solution and the silk obtained in step (1) are placed in a 100mL stainless steel autoclave lined with p...

Embodiment 2

[0026] Concrete preparation steps (1), (2), (3) of the present embodiment are the same as embodiment 1, and step (4) is:

[0027] (4) Put the 3D hollow structural material obtained in step (3) in a porcelain boat and place it in a tube furnace, heat it to 300°C in an air atmosphere and keep it warm for 2 hours to obtain the oxidized 3D hollow structural material, It is a capacitor material with a 3D hollow structure.

Embodiment 3

[0029]Concrete preparation steps (1), (2), (3) of the present embodiment are the same as embodiment 1, and step (4) is:

[0030] (4) Put the 3D hollow structural material obtained in step (3) in a porcelain boat and place it in a tube furnace, heat it to 500°C in an air atmosphere and keep it warm for 2 hours to obtain the oxidized 3D hollow structural material, It is a capacitor material with a 3D hollow structure.

[0031] Through the characterization of the scanning electron microscope, the thorny NiCo that grows on the surface of the silk is prepared in Example 1. 2 S 4 The nanowire structure remained intact and formed a hollow structure with a diameter of 8.23nm, and no "collapse" phenomenon was observed, such as figure 1 . And changing the oxidation and calcination treatment conditions, mainly the temperature, has a great impact on the material NiCo 2 S 4 The morphology and structure of the nanowires have a significant impact, such as figure 2 , at lower or higher...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impedanceaaaaaaaaaa
Login to View More

Abstract

The invention, which belongs to the technical field of energy material preparation, relates to a preparation method for growing a NiCo2S4 nanowire by using silk as a substrate to form a capacitor material. The specific preparation process comprises: growing a nickel-cobalt precursor on silk; carrying out hydrothermal vulcanization treatment on the obtained nickel-cobalt precursor to remove the silk and thus forming a hollow structure; and then carrying out oxidative calcination treatment to obtain a capacitor material having a 3D hollow structure. According to the invention, the spinous structure of the NiCo2S4 nanowire is kept well; a large specific surface area and more active sites are provided; the electron / ion in the electrolyte solution can be absorbed conveniently, so that the electrochemical performance of the material becomes excellent and stable. In addition, the hollow structure has the diameter of 8 to 9 nm and thus a convenient passage is provided for electron / ion transport, so that the reaction is carried out continuously and effectively. The prepared capacitor material having the excellent electrochemical performance and the outstanding cycle stability is a potentialmaterial and has broad application prospects.

Description

technical field [0001] The invention belongs to the technical field of energy material preparation, and in particular relates to a method for growing NiCo based on silk as a substrate. 2 S 4 Preparation methods of nanowires as capacitor materials. Background technique [0002] Oil and other energy resources are becoming increasingly scarce and the exhaust emissions of internal combustion engines after burning oil are increasingly polluting the environment. People are studying new energy devices to replace internal combustion engines. At present, research and development of hybrid power, fuel cells, and chemical battery products and applications have been carried out, and certain results have been achieved. However, due to their inherent shortcomings such as short service life, poor temperature characteristics, environmental pollution by chemical batteries, complex systems, and high cost, there has been no good solution. [0003] Supercapacitor is a new type of energy stor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/24H01G11/30B82Y40/00B82Y30/00
CPCB82Y30/00B82Y40/00H01G11/24H01G11/30Y02E60/13
Inventor 刘敬权黄卫国张爱堂
Owner QINGDAO UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com