Glistening glaze for glass mosaic, and glass mosaic preparation process

A technology of glass mosaic and preparation process, which is applied in the direction of coating, etc., can solve the problem of single surface effect, and achieve the effect of good applicability and good dirt resistance

Inactive Publication Date: 2019-07-05
佛山市唯格建材有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the splicing pattern of glass mosaic is very rich, the surface effect of a single glass mosaic product on the market is very single, which is not enough to meet the needs of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glistening glaze for glass mosaic, and glass mosaic preparation process
  • Glistening glaze for glass mosaic, and glass mosaic preparation process
  • Glistening glaze for glass mosaic, and glass mosaic preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] A flash glaze for glass mosaics, the flash glaze includes the following raw materials in parts by mass: 70-80 parts of glass powder, 10-20 parts of low-temperature glass frit, 5-10 parts of high-temperature flash powder, and 0 parts of stabilizer -10 parts, 0.2-0.8 parts of binder and water; and the fineness of the flash glaze is 200-250 mesh.

[0022] Although the mosaic pattern of the glass mosaic in the prior art is very rich, the surface effect of a single glass mosaic product is very single, which is not enough to meet the needs of users. The present invention proposes a flash glaze for the surface of glass mosaic. The flash glaze includes the following raw materials in parts by mass: 70-80 parts of glass powder, 10-20 parts of low-temperature glass frit, 5-10 parts of high-temperature flash powder, stable 0-10 parts of agent, 0.2-0.8 parts of binder and water; since the flash glaze is used on the surface of glass mosaic, its raw material formula uses the same glas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

A glistening glaze for glass mosaic is disclosed, and includes following raw materials by mass: 70-80 parts of glass powder, 10-20 parts of low-temperature glass frit, 5-10 parts of high-temperature glistening powder, 0-10 parts of a stabilizer, 0.2-0.8 part of a binder and water. The fineness of the glistening glaze is 200-250 meshes. According to a technical scheme, the low-temperature glass frit and the high-temperature glistening powder are blended according to a certain ratio, a melting temperature difference between the low-temperature glass frit having a low softening temperature and the high-temperature glistening powder having a high melting temperature is utilized, the fineness of powder materials is controlled to be 200-250 meshes, finally a certain amount of the stabilizer, thebinder and the water are added, and the mixture is ground to obtain the low-temperature glaze that can be applied onto a glass mosaic surface. After the glaze is applied onto the glass mosaic surfaceto form a glaze layer and low-temperature firing is performed, the glaze layer on the glass mosaic surface has fine, smooth and glistening decorative effects, and has good stain resistance and betterapplicability.

Description

technical field [0001] The invention relates to the technical field of glass mosaics, in particular to a flash glaze for glass mosaics and a preparation process for glass mosaics. Background technique [0002] Made of natural minerals and glass powder, glass mosaic is the safest building material and an outstanding environmental protection material. With the continuous improvement of people's living standards, people's pursuit of home interior decoration is also changing, and the requirements for decorative mosaics are also increasing. At present, for home decoration, especially the decoration of bathrooms and kitchens, glass mosaics can be used to create richer pattern effects, so more people choose glass mosaics with rich pattern effects. Although the splicing pattern of glass mosaic is very rich, the surface effect of a single glass mosaic product on the market is very single, which is not enough to meet the needs of users. Therefore, in order to further improve the ric...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C03C8/04C03C17/04
CPCC03C8/04C03C8/20C03C17/04C03C2217/72C03C2217/78
Inventor 姚文江任东王飞韦明皇
Owner 佛山市唯格建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com