A kind of welding wire steel for manual argon arc welding

A technology of manual argon arc welding and welding wire steel, which is applied in the field of metallurgy, can solve problems such as increasing product costs, and achieve the effects of ensuring performance, low spatter rate, and high strength

Active Publication Date: 2022-01-11
TANGSHAN NORMAL UNIV +1
View PDF14 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, according to statistics, currently in the welding consumables market, most of the welding 690MPa low-alloy high-strength steels use the Mn-Ni-Mo alloy system. Since Ni is a precious metal, adding too much will inevitably increase the product cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of welding wire steel for manual argon arc welding
  • A kind of welding wire steel for manual argon arc welding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Welding wire steel for manual argon arc welding, the mass percentage composition is: C is 0.03%, Mn is 1.15%, Si is 0.80%, S is 0.005%, P is 0.010%, Cr is 0.25%, Mo is 0.25%, Ni is 0.15%, Microalloy: 0.015% Ti, 0.025% Nb, 0.010% Zr, 97.305% Fe and unavoidable impurity elements.

Embodiment 2

[0030] Welding wire steel for manual argon arc welding, the mass percentage composition is: C is 0.06%, Mn is 1.50%, Si is 0.70%, S is 0.010%, P is 0.020%, Cr is 0.10%, Mo is 0.20%, Ni is 0.20%, Microalloy: 0.010% for Ti, 0.020% for Nb, 0.010% for Zr, 97.170% for Fe and unavoidable impurity elements.

Embodiment 3

[0032]Welding wire steel for manual argon arc welding, the mass percentage composition is: C is 0.04%, Mn is 0.80%, Si is 0.70%, S is 0.005%, P is 0.015%, Cr is 0.05%, Mo is 0.10%, Ni is 0.10%, microalloying: Ti is 0.005%, Nb is 0.010%, Zr is 0.010%, Fe and unavoidable impurity elements are 98.165%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
impact absorption energyaaaaaaaaaa
Login to View More

Abstract

The invention discloses a welding wire steel for manual argon arc welding. In terms of mass percentage, the composition of the welding wire is: C is 0.0001-0.08%, Mn is 0.80-1.50%, Si is 0.70-0.95%, and S is 0.0001-0.010% %, P is 0.0001-0.020%, Cr is 0.0001-0.40%, Mo is 0.10-0.30%, Ni is 0.0001-0.40%, and the rest are Fe and inevitable impurity elements. The invention has low cost, high welding seam strength and toughness, stable quality and good welding performance, and can meet the use requirements of welding wire manufacturers. While ensuring the high strength of the weld metal, the invention improves the welding performance of the low-alloy high-strength welding wire to a limited extent, controls the appearance of cold cracks, has a small spatter rate, and meets the welding requirements of low-alloy high-strength steel.

Description

technical field [0001] The invention relates to the technical field of metallurgy, in particular to a welding wire steel for manual argon arc welding. Background technique [0002] At present, with the rapid development of energy, petroleum, chemical industry, hydropower and other industries, engineering structures are becoming more and more large-scale and lightweight, and the demand for steel plates is also increasing, such as large crude oil storage tanks, large spherical Tanks, offshore oil production platforms, long-span bridge dyeing, large pipelines, etc. Low-alloy high-strength steel has good weldability, excellent formability and low manufacturing cost, so it is widely used in pressure vessels, vehicles, bridges, construction, construction machinery, mining machinery, textile machinery, marine structures and other fields. Among them, 690MPa low-alloy high-strength steel has been widely used. With the development of modern industry, the welding structure is developi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/30
CPCB23K35/3073
Inventor 杨会静李国民尚丽娟
Owner TANGSHAN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com