A kind of anti-yellowing water-based adhesive and preparation method thereof

An adhesive and anti-yellowing technology, applied in adhesives, adhesive types, adhesive additives, etc., can solve problems affecting product appearance and quality, low 180° peel strength, poor bonding performance, etc., to save manpower And equipment cost, 180°peel strength improvement, good effect of yellowing resistance

Active Publication Date: 2021-07-27
福建省统一环保科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] 1. The existing adhesive (glue) is prone to change in the sun, and white and light colors will turn yellow. For example, the white shoe lining and upper (also called shoe upper) will turn yellow after a period of time, which seriously affects the appearance and quality of the product. The quality is not durable; when storing and transporting, it cannot be exposed to light and is not resistant to storage;
[0007] 2. The bonding performance is poor, and performance indicators such as 180°peel strength are low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-yellowing water-based adhesive and preparation method thereof
  • A kind of anti-yellowing water-based adhesive and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An anti-yellowing water-based adhesive, made of the following raw materials in parts by weight: 38-48 parts of polyvinyl alcohol, 23-29 parts of water-soluble polyvinyl formal, 28-35 parts of water-based ethylene-vinyl acetate copolymer 12-16 parts of silicone acrylic emulsion, 2-4 parts of emulsifier, 3-6 parts of ultraviolet absorber, 2.5-4 parts of antioxidant; the ultraviolet absorber is 2-(2ˊ-hydroxyl-5ˊ-methylbenzene base) a mixture of benzotriazole and resorcinol monobenzoate.

[0036] Preferably, the anti-yellowing water-based adhesive is made of the following raw materials in parts by weight: 43 parts of polyvinyl alcohol, 26.5 parts of water-soluble polyvinyl formal, 31.5 parts of water-based ethylene-vinyl acetate copolymer, silicone acrylic 14 parts of emulsions, 3.2 parts of emulsifiers, 4.8 parts of ultraviolet absorbers, and 3.6 parts of antioxidants; A mixture of quinone esters.

[0037] Preferably, in the mixture of 2-(2'-hydroxyl-5'-methylphenyl) ben...

Embodiment 2

[0046] An anti-yellowing water-based adhesive, made of the following raw materials in parts by weight: 38 parts of polyvinyl alcohol, 23 parts of water-soluble polyvinyl formal, 28 parts of water-based ethylene-vinyl acetate copolymer, 12 parts of silicon-acrylic emulsion 2 parts, 2 parts of emulsifier, 3 parts of ultraviolet absorber, 2.5 parts of antioxidant; Described ultraviolet absorber is 2-(2'-hydroxyl-5'-methylphenyl) benzotriazole and isophthalic acid monobenzoic acid A mixture of phenolic esters.

[0047] In this example, in the mixture of 2-(2'-hydroxy-5'-methylphenyl)benzotriazole and resorcinol monobenzoate, 2-(2'-hydroxyl-5'-methyl The mass ratio of phenyl)benzotriazole to resorcinol monobenzoate is 1:0.6.

[0048] In this embodiment, the polyvinyl alcohol is 1799 type polyvinyl alcohol.

[0049] In this embodiment, the emulsifier is cocoamine polyoxyethylene ether.

[0050] In this embodiment, the antioxidant is tetrakis[β-(3,5-di-tert-butyl 4-hydroxyphenyl) ...

Embodiment 3

[0057] An anti-yellowing water-based adhesive, made of the following raw materials in parts by weight: 48 parts of polyvinyl alcohol, 29 parts of water-soluble polyvinyl formal, 35 parts of water-based ethylene-vinyl acetate copolymer, 16 parts of silicon acrylic emulsion part, 4 parts of emulsifier, 6 parts of ultraviolet absorber, 4 parts of antioxidant; Described ultraviolet absorber is 2-(2'-hydroxyl-5'-methylphenyl) benzotriazole and monobenzoic acid A mixture of phenolic esters.

[0058] In this example, in the mixture of 2-(2'-hydroxy-5'-methylphenyl)benzotriazole and resorcinol monobenzoate, 2-(2'-hydroxyl-5'-methyl The mass ratio of phenyl)benzotriazole to resorcinol monobenzoate is 1:0.7.

[0059] In this embodiment, the polyvinyl alcohol is 1799 type polyvinyl alcohol.

[0060] In this embodiment, the emulsifier is cocoamine polyoxyethylene ether.

[0061] In this embodiment, the antioxidant is tetrakis[β-(3,5-di-tert-butyl 4-hydroxyphenyl) propionate] pentaeryth...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anti-yellowing water-based adhesive and a preparation method thereof. The anti-yellowing water-based adhesive is made of the following raw materials in parts by weight: 38-48 parts of polyvinyl alcohol, water-soluble polyvinyl formal 23-29 parts, 28-35 parts of water-based ethylene-vinyl acetate copolymer, 12-16 parts of silicon acrylic emulsion, 2-4 parts of emulsifier, 3-6 parts of ultraviolet absorber, 2.5-4 parts of antioxidant; The UV absorber is a mixture of 2‑(2ˊ‑hydroxy‑5ˊ‑methylphenyl)benzotriazole and resorcinol monobenzoate. The present invention selects the composition of raw materials and optimizes the content of each raw material, which not only gives full play to their respective advantages, but also complements and promotes each other. The prepared anti-yellowing water-based adhesive has good yellowing resistance and high / low temperature resistance; 180°peel strength is high.

Description

technical field [0001] The invention relates to the field of adhesives, in particular to a yellowing-resistant water-based adhesive and a preparation method thereof. Background technique [0002] With the development of industry, the application market of adhesives (glue, or adhesives) is becoming more and more extensive, and the varieties are also increasing. Commonly used adhesives mainly include solvent-based, water-based and hot-melt types. At present, the amount of solvent-based products is relatively large. It uses volatile organic compounds such as benzene and toluene as solvents. These solvents will directly volatilize into the atmosphere during use to pollute the environment and endanger the health of workers. Therefore, many foreign government departments Promulgation of laws and regulations to limit the use of volatile organic compounds, the transformation of adhesives from solvent-based to water-based has become inevitable. [0003] Water-based (based) adhesives...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J129/04C09J129/14C09J123/08C09J133/04C09J11/06C09J11/08
CPCC08L2201/08C08L2205/02C08L2205/035C09J11/06C09J11/08C09J129/04C08L29/14C08L23/0853C08L43/04C08K5/3475C08K5/107
Inventor 邓宋明张国华
Owner 福建省统一环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products