A technology of non-woven fabrics and writing paper, which is applied in the field of papermaking and can solve problems such as high prices, limited wood fiber resources, and lack of texture

Active Publication Date: 2020-04-17
温州新宇无纺布有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The thickness of the existing writing paper is limited. Due to the good water absorption of wood fiber, the ink is easy to permeate, and the paper is thin and lacks texture. The

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-woven fabric writing paper and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Embodiment 1 A kind of preparation of non-woven writing paper

[0024] Raw materials: mixing 65 parts by mass of low-denier polyester fibers of 33-38DTEX;

[0025] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0026] Sizing: sizing the polyester fiber web with sizing, which is prepared by 30 parts by mass of soft adhesive, 4 parts by mass of hard adhesive, 1 part by mass of water repellent and 35 parts by mass of water;

[0027] Drying: Dry the sized polyester fiber web at 200° C. for 30 minutes to obtain non-woven writing paper.

[0028] In this embodiment, the SHD soft adhesive of Transfar Chemical is used as the soft adhesive, the 351HA hard adhesive of Transfar Chemical is used as the hard adhesive, and the FS01 waterproofing agent of Transfar Chemical is used as the waterproofing agent.

[0029] The slurry mixed with soft and hard binders will bind the fibers and reinforce the writing paper at the sam...

Embodiment 2

[0030] Embodiment 2 A kind of preparation of non-woven writing paper

[0031] Raw materials: mixing 60 parts by mass of low-denier polyester fibers of 33-38DTEX;

[0032] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0033] Sizing: sizing the polyester fiber web with sizing, the sizing is prepared by 25 parts by mass of soft adhesive, 3 parts by mass of hard adhesive, 1 part by mass of water repellent plus 24 parts by mass of water;

[0034] Drying: Dry the sized polyester fiber web at 220° C. for 30 minutes to obtain non-woven writing paper.

Embodiment 3

[0035] Embodiment 3 A kind of preparation of non-woven writing paper

[0036] Material preparation: mixing 80 parts by mass of low-denier polyester fiber of 33-38DTEX;

[0037] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0038] Sizing: sizing the polyester fiber web with sizing, the slurry is prepared from 35 parts by mass of soft adhesive, 5 parts by mass of hard adhesive, 2 parts by mass of water repellent and 50 parts by mass of water;

[0039] Drying: drying the sized polyester fiber web at 180° C. for 60 minutes to obtain non-woven writing paper.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of non-woven fabric writing paper. The preparation method comprises the following steps: preparing materials, namely uniformly mixing polyester fibers or mixed fibers containing more than 80wt% of polyester fibers; carding and web forming: carding for forming net: carding the fibers and laying the carded fibers in a staggered mode to form a polyester fiber net; sizing, specifically, sizing the polyester fiber net, wherein a sizing agent is prepared from an adhesive, a waterproof agent and water; and drying: drying the sized polyester fiber net to obtain the non-woven fabric writing paper. According to the technical scheme, the non-woven fabric writing paper is prepared by taking polyester fibers as raw materials. When the weight of the non-wovenfabric writing paper is 60 g, the thickness of the non-woven fabric writing paper is 34-38 mm (100 pieces), the paper surface is smooth, the paper has toughness, and permeation is not likely to happen in the writing process.

Description

technical field [0001] The invention relates to the field of papermaking, in particular to a non-woven writing paper and a preparation method thereof. Background technique [0002] Non-woven fabric, also known as non-woven fabric, refers to the cloth made without traditional spinning, weaving or knitting. It is a new type of fiber product with soft, breathable and planar structure, which is formed into a net, then consolidated by spunlace, needle punching or hot rolling, and finally finished. [0003] The thickness of the existing writing paper is limited. Since the wood fiber has good water absorption, the ink is easy to penetrate, and the paper is thin and lacks texture. Calligraphy works to be preserved need to be thickened and mounted. Simultaneously its main raw material wood fiber resource is limited, the price is higher. With the current economic development in my country, there are more and more discarded fabrics and chemical polyester fibers, and chemical fiber re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/00D21F13/00
CPCD21H27/00D21F13/00
Inventor 卢伟新禹亚奇张自浩卢艳艳
Owner 温州新宇无纺布有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap