A kind of non-woven writing paper and preparation method thereof

Abstract

A method for preparing non-woven writing paper, the preparation method comprising the following steps: preparing materials: mixing polyester fibers or mixed fibers containing more than 80 wt% polyester fibers; carding into a web: carding fiber pairs; The fibers are interlaced to form a polyester fiber web, sizing: sizing the polyester fiber web, and the slurry is prepared from adhesives, waterproofing agents and water; drying: drying the sized polyester fiber web to obtain non-woven writing paper . The above technical proposal adopts polyester fiber as a raw material to prepare non-woven writing paper. When the non-woven writing paper is 60g, the thickness is 34-38mm (100 sheets), the paper surface is flat, the paper has toughness, and it is not easy to seep through during the writing process.

Description

technical field

[0001] The invention relates to the field of papermaking, in particular to a non-woven writing paper and a preparation method thereof. Background technique

[0002] Non-woven fabric, also known as non-woven fabric, refers to the cloth made without traditional spinning, weaving or knitting. It is a new type of fiber product with soft, breathable and planar structure, which is formed into a net, then consolidated by spunlace, needle punching or hot rolling, and finally finished.

[0003] The thickness of the existing writing paper is limited. Since the wood fiber has good water absorption, the ink is easy to penetrate, and the paper is thin and lacks texture. Calligraphy works to be preserved need to be thickened and mounted. Simultaneously its main raw material wood fiber resource is limited, the price is higher. With the current economic development in my country, there are more and more discarded fabrics and chemical polyester fibers, and chemical fiber re...

Examples

Embodiment 1

[0023] Embodiment 1 A kind of preparation of non-woven writing paper

[0024] Raw materials: mixing 65 parts by mass of low-denier polyester fibers of 33-38DTEX;

[0025] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0026] Sizing: sizing the polyester fiber web with sizing, which is prepared by 30 parts by mass of soft adhesive, 4 parts by mass of hard adhesive, 1 part by mass of water repellent and 35 parts by mass of water;

[0027] Drying: Dry the sized polyester fiber web at 200° C. for 30 minutes to obtain non-woven writing paper.

[0028] In this embodiment, the SHD soft adhesive of Transfar Chemical is used as the soft adhesive, the 351HA hard adhesive of Transfar Chemical is used as the hard adhesive, and the FS01 waterproofing agent of Transfar Chemical is used as the waterproofing agent.

[0029] The slurry mixed with soft and hard binders will bind the fibers and reinforce the writing paper at the sam...

Embodiment 2

[0030] Embodiment 2 A kind of preparation of non-woven writing paper

[0031] Raw materials: mixing 60 parts by mass of low-denier polyester fibers of 33-38DTEX;

[0032] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0033] Sizing: sizing the polyester fiber web with sizing, the sizing is prepared by 25 parts by mass of soft adhesive, 3 parts by mass of hard adhesive, 1 part by mass of water repellent plus 24 parts by mass of water;

[0034] Drying: Dry the sized polyester fiber web at 220° C. for 30 minutes to obtain non-woven writing paper.

Embodiment 3

[0035] Embodiment 3 A kind of preparation of non-woven writing paper

[0036] Material preparation: mixing 80 parts by mass of low-denier polyester fiber of 33-38DTEX;

[0037] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0038] Sizing: sizing the polyester fiber web with sizing, the slurry is prepared from 35 parts by mass of soft adhesive, 5 parts by mass of hard adhesive, 2 parts by mass of water repellent and 50 parts by mass of water;

[0039] Drying: drying the sized polyester fiber web at 180° C. for 60 minutes to obtain non-woven writing paper.

technical field

[0001] The invention relates to the field of papermaking, in particular to a non-woven writing paper and a preparation method thereof. Background technique

[0002] Non-woven fabric, also known as non-woven fabric, refers to the cloth made without traditional spinning, weaving or knitting. It is a new type of fiber product with soft, breathable and planar structure, which is formed into a net, then consolidated by spunlace, needle punching or hot rolling, and finally finished.

[0003] The thickness of the existing writing paper is limited. Since the wood fiber has good water absorption, the ink is easy to penetrate, and the paper is thin and lacks texture. Calligraphy works to be preserved need to be thickened and mounted. Simultaneously its main raw material wood fiber resource is limited, the price is higher. With the current economic development in my country, there are more and more discarded fabrics and chemical polyester fibers, and chemical fiber re...

Examples

Embodiment 1

[0023] Embodiment 1 A kind of preparation of non-woven writing paper

[0024] Raw materials: mixing 65 parts by mass of low-denier polyester fibers of 33-38DTEX;

[0025] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0026] Sizing: sizing the polyester fiber web with sizing, which is prepared by 30 parts by mass of soft adhesive, 4 parts by mass of hard adhesive, 1 part by mass of water repellent and 35 parts by mass of water;

[0027] Drying: Dry the sized polyester fiber web at 200° C. for 30 minutes to obtain non-woven writing paper.

[0028] In this embodiment, the SHD soft adhesive of Transfar Chemical is used as the soft adhesive, the 351HA hard adhesive of Transfar Chemical is used as the hard adhesive, and the FS01 waterproofing agent of Transfar Chemical is used as the waterproofing agent.

[0029] The slurry mixed with soft and hard binders will bind the fibers and reinforce the writing paper at the sam...

Embodiment 2

[0030] Embodiment 2 A kind of preparation of non-woven writing paper

[0031] Raw materials: mixing 60 parts by mass of low-denier polyester fibers of 33-38DTEX;

[0032] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0033] Sizing: sizing the polyester fiber web with sizing, the sizing is prepared by 25 parts by mass of soft adhesive, 3 parts by mass of hard adhesive, 1 part by mass of water repellent plus 24 parts by mass of water;

[0034] Drying: Dry the sized polyester fiber web at 220° C. for 30 minutes to obtain non-woven writing paper.

Embodiment 3

[0035] Embodiment 3 A kind of preparation of non-woven writing paper

[0036] Material preparation: mixing 80 parts by mass of low-denier polyester fiber of 33-38DTEX;

[0037] Carding into a web: Carding the prepared fibers; interlacing the carded fibers into a polyester fiber web,

[0038] Sizing: sizing the polyester fiber web with sizing, the slurry is prepared from 35 parts by mass of soft adhesive, 5 parts by mass of hard adhesive, 2 parts by mass of water repellent and 50 parts by mass of water;

[0039] Drying: drying the sized polyester fiber web at 180° C. for 60 minutes to obtain non-woven writing paper.