A kind of preparation method of composite metal coating foam metal material

A foam metal and composite metal technology, applied in metal material coating process, coating, liquid chemical plating and other directions, can solve problems such as material failure, and achieve the effect of fast deposition, simple experimental process and easy operation.

Active Publication Date: 2021-09-21
CENT SOUTH UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The nickel-iron foam metal material prepared by this method will be exposed to the corrosive medium when the surface anti-corrosion layer is corroded in acid, alkali and other corrosive medium environments, resulting in material failure.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of composite metal coating foam metal material
  • A kind of preparation method of composite metal coating foam metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Such as figure 1 Shown, a kind of preparation method of composite metal coating foam metal material may further comprise the steps:

[0036] (1) Degreasing, acidifying, sensitizing and activating the polyurethane foam (15cm×10cm×1cm) to obtain the modified polyurethane foam; wherein, the degreasing treatment is to remove the polyurethane foam with a potassium hydroxide solution with a concentration of 50g / L The oil pollution, the degreasing time is 20min, and the temperature is 70°C. Acidification treatment is to treat the polyurethane foam after degreasing in 1g / L oxalic acid solution for 20min, and then wash it to neutral with deionized water to obtain the polyurethane foam after pickling; sensitization treatment is to treat the polyurethane foam after pickling Treat it in a mixed solution of stannous chloride 5g / L and hydrochloric acid 5ml / L for 15 minutes, and then wash it with deionized water until neutral to obtain a sensitized polyurethane foam; The final polyure...

Embodiment 2

[0044] A method for preparing a composite metal-coated metal foam material, comprising the following steps:

[0045] (1) Degreasing, acidifying, sensitizing and activating the polyurethane foam (15cm×10cm×1cm) to obtain the modified polyurethane foam; wherein, the degreasing treatment is to remove the polyurethane foam with a potassium hydroxide solution with a concentration of 100g / L The oil pollution, the degreasing time is 10min, and the temperature is 70°C. Acidification treatment is to treat the polyurethane foam after degreasing in 3g / L oxalic acid solution for 20min, and then wash it to neutral with deionized water to obtain the polyurethane foam after pickling; sensitization treatment is to treat the polyurethane foam after pickling Treat it in a mixed solution of stannous chloride 8g / L and hydrochloric acid 10ml / L for 10 minutes, then wash it with deionized water until neutral to obtain a sensitized polyurethane foam; The final polyurethane foam was processed in 100m...

Embodiment 3

[0053] A method for preparing a composite metal-coated metal foam material, comprising the following steps:

[0054] (1) Degreasing, acidifying, sensitizing and activating the polyurethane foam (15cm×10cm×1cm) to obtain the modified polyurethane foam; wherein, the degreasing treatment is to remove the polyurethane foam with a potassium hydroxide solution with a concentration of 120g / L The oil stain, the degreasing time is 5min, and the temperature is 75°C. Acidification treatment is to treat the polyurethane foam after degreasing in 5g / L oxalic acid solution for 10min, and then wash it to neutral with deionized water to obtain the polyurethane foam after pickling; sensitization treatment is to treat the polyurethane foam after pickling Treat it in a mixed solution of stannous chloride 10g / L and hydrochloric acid 10ml / L for 10 minutes, then wash it with deionized water until neutral to obtain a sensitized polyurethane foam; The final polyurethane foam was processed in 200mg / mL...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a foamed metal material with composite metal plating, which comprises the following steps: (1) modified polyurethane foam; (2) configuring electroless plating solution A, electroplating solution and electroless plating solution B; (3) electroless plating (4) electroplating; (5) heat treatment; (6) heat reduction treatment; (7) electroless plating solution, that is, to obtain the composite metal coating foam metal material. The invention adopts the method of combining chemical plating and electroplating, and the composite metal coating foam metal material coating prepared is bright and compact, with controllable metal content and coating thickness, certain strength, large specific surface area, good oxidation resistance and corrosion resistance. .

Description

technical field [0001] The invention belongs to the field of composite materials, and in particular relates to a method for preparing foamed metal materials. Background technique [0002] Nickel-iron metal foam material, as a rapidly developing structural and functional material, is widely used in catalysts and catalyst carriers, high-temperature liquid filters, heat exchangers and other functional materials, and can also be used as structural materials in automobiles, construction and other fields. However, the preparation method of the traditional nickel-iron foam material is usually to perform electroless plating or electroplating on the polyurethane sponge through pretreatment steps such as degreasing, pickling, sensitization, and activation, and to plate nickel-iron and other alloy layers on the surface of the foam material. Thus, nickel-iron foam metal is prepared. The nickel-iron foam metal material prepared by this method will be exposed to the corrosive medium afte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C18/36C23C18/30C25D3/56C23C28/02
CPCC23C18/285C23C18/30C23C18/36C23C28/021C23C28/023C25D3/562
Inventor 甘雪萍赵琪刘晨虹李周周科朝
Owner CENT SOUTH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com