A kind of UV shielding nano-coating solution and its application on optical lens

An optical lens, ultraviolet technology, applied in the coating and other directions, can solve the problems of poor ultraviolet shielding effect, decreased ultraviolet shielding effect of lenses, etc., to avoid eye fatigue, strong ultraviolet protection, and good shielding effect.

Active Publication Date: 2021-12-14
深圳菲比特光电科技有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a UV shielding nano-coating solution and its Application on Optical Lenses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of UV shielding nano-coating solution and its application on optical lens

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] An ultraviolet shielding nano-coating solution, calculated in parts by weight, consists of the following components:

[0046] 50 parts of acrylic resin, 18 parts of dispersed silica sol, 5 parts of ultraviolet shielding agent, 3 parts of silane coupling agent, 3 parts of auxiliary agent and 35 parts of water;

[0047] Among them, the ultraviolet shielding agent is TiO 2 / porous organic carrier composite.

[0048] The dispersion medium of the dispersed silica sol is a mixture of ethanol and isopropanol.

[0049] The mass proportion of silica sol in the dispersed silica sol is 30%.

[0050] The pH of the dispersed silica sol is 9-10.

[0051] The auxiliaries include leveling agents, wetting agents, defoamers and coalescents.

[0052] The particle diameter of the silica sol is 20-50 nm.

[0053] The preparation method of described porous organic carrier is:

[0054] S1. Weigh 1,3,5-trimethylbenzene and dioxane into the reaction container, stir and mix until uniform, ...

Embodiment 2

[0071] An ultraviolet shielding nano-coating solution, calculated in parts by weight, consists of the following components:

[0072] 40 parts of acrylic resin, 10 parts of dispersed silica sol, 3 parts of ultraviolet shielding agent, 1 part of silane coupling agent, 0.05 parts of auxiliary agent and 20 parts of water;

[0073] Among them, the ultraviolet shielding agent is TiO 2 / porous organic carrier composite.

[0074] The dispersion medium of the dispersed silica sol is at least one of ethanol, isopropanol, acetone, and ethylene glycol methyl ether.

[0075] The mass proportion of silica sol in the dispersed silica sol is 20%.

[0076] The pH of the dispersed silica sol is 9-10.

[0077] The auxiliaries include leveling agents, wetting agents, defoamers and coalescents.

[0078] The particle diameter of the silica sol is 20-50 nm.

[0079] The preparation method of described porous organic carrier is:

[0080] S1. Weigh 1,3,5-trimethylbenzene and dioxane into the rea...

Embodiment 3

[0097] An ultraviolet shielding nano-coating solution, calculated in parts by weight, consists of the following components:

[0098] 60 parts of acrylic resin, 25 parts of dispersed silica sol, 8 parts of ultraviolet shielding agent, 5 parts of silane coupling agent, 8 parts of auxiliary agent and 50 parts of water;

[0099] Among them, the ultraviolet shielding agent is TiO 2 / porous organic carrier composite.

[0100] The dispersion medium of the dispersed silica sol is at least one of ethanol, isopropanol, acetone, and ethylene glycol methyl ether.

[0101] The mass proportion of silica sol in the dispersed silica sol is 40%.

[0102] The pH of the dispersed silica sol is 9-10.

[0103] The auxiliaries include leveling agents, wetting agents, defoamers and coalescents.

[0104] The particle diameter of the silica sol is 20-50 nm.

[0105] The preparation method of described porous organic carrier is:

[0106] S1. Weigh 1,3,5-trimethylbenzene and dioxane into the react...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
transmittivityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an ultraviolet shielding nano-coating solution, wherein the ultraviolet shielding nano-coating solution is calculated according to parts by weight and consists of the following components: 40-60 parts of acrylic resin, 10-25 parts of dispersed silica sol, and 3-25 parts of ultraviolet shielding agent 8 parts, 1-5 parts of silane coupling agent, 0.05-8 parts of auxiliary agent and 20-50 parts of water; among them, the ultraviolet shielding agent is TiO2 prepared by compounding nano-scale titanium dioxide and porous organic carrier 2 / porous organic carrier composite. Among them, the present invention uses an environmentally friendly "green" water-based coating solution that does not contain organic solvents. The main raw material is water-resistant and chemical-resistant acrylic resin. Combined with dispersed silica sol, a relatively uniform and dense film can be formed. Finally The obtained coating film not only has strong ultraviolet protection effect, but also has strong adhesion, wear resistance and light transmission performance to other visible light.

Description

technical field [0001] The invention relates to the field of optical lens coating liquid, in particular to an ultraviolet shielding nano coating liquid and its application on optical lens. Background technique [0002] Ultraviolet rays in sunlight, because the wavelength of ultraviolet rays is very short and the energy is quite high, it has great destructive power. In recent years, the damage of ultraviolet rays to human eyes has attracted more and more attention. The damage of ultraviolet rays to the human eye mainly depends on the wavelength of ultraviolet rays, radiation time, radiation intensity and the defense mechanism and ability of the human eye itself. The cornea and lens of the human eye are the eye tissues that are most often damaged by ultraviolet rays, such as common solar keratitis, corneal endothelial damage, solar cataract and other related eye diseases. In areas with strong light reflection, such as snow, plateaus, and asphalt roads, ultraviolet rays are af...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D7/62C03C17/00C03C17/32
CPCC09D133/04C09D7/62C03C17/009C03C17/32C08K2003/2241C08K2201/011C08K2201/005C08K3/36C08K9/12C08K3/22C08K9/02
Inventor 徐周洪金木
Owner 深圳菲比特光电科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka