A kind of ceramic glazed tile surface anti-skid agent and preparation method thereof

A technology of ceramic glaze and anti-slip agent, applied in anti-fouling/underwater coatings, paints containing biocides, coatings, etc. Friction coefficient, the effect of increasing friction

Active Publication Date: 2022-06-24
上海世卿防滑防护科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the problem that the existing anti-slip agent is easy to be worn after long-term use, and the uneven structure on the surface of the brick body is not easy to clean, the invention provides an anti-slip agent on the surface of ceramic glazed tiles and a preparation method thereof, so that the anti-slip agent and The surface of ceramic glazed tiles is effectively combined to play a good anti-slip effect and has a good sterilization effect at the same time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic glazed tile surface anti-skid agent and preparation method thereof
  • A kind of ceramic glazed tile surface anti-skid agent and preparation method thereof
  • A kind of ceramic glazed tile surface anti-skid agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] This embodiment provides an anti-slip agent on the surface of a ceramic glazed tile, wherein the anti-slip agent is painted on the glaze layer of the ceramic glazed tile.

[0014] A surface anti-slip agent for ceramic glazed tiles, which is composed of a solvent, particles dispersed in the solvent, and dispersants, auxiliary agents, surfactants and fluoride salts dissolved in the solvent;

[0015] Among them, the parts by weight of each component are: 4 parts of particles, 2 parts of dispersant, 2 parts of auxiliary agent, 13 parts of surfactant, 14 parts of fluoride salt, and the balance is solvent.

[0016] Wherein, the solvent is water, the particles are nano titanium dioxide, the dispersant is polyvinyl alcohol, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride.

[0017] Wherein, the preparation method of surfactant is:

[0018] S1: Add 150 mL of low-hydrogen silicone oil and 100 mL of trans-3-pente...

Embodiment 2

[0038] This embodiment provides an anti-slip agent on the surface of a ceramic glazed tile, wherein the anti-slip agent is painted on the glaze layer of the ceramic glazed tile.

[0039] A surface anti-slip agent for ceramic glazed tiles, which is composed of a solvent, particles dispersed in the solvent, and dispersants, auxiliary agents, surfactants and fluoride salts dissolved in the solvent;

[0040] Among them, the parts by weight of each component are: 10 parts of particles, 7 parts of dispersant, 9 parts of auxiliary agent, 21 parts of surfactant, 22 parts of fluoride salt, and the balance is solvent.

[0041] Wherein, the solvent is water, the particles are nano-titanium dioxide, the dispersing agent is sodium polyacrylate and ethyl acetate, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride.

[0042] Wherein, the preparation method of surfactant is:

[0043] S1: Add 150 mL of low-hydrogen silicone oil ...

Embodiment 3

[0058] This embodiment provides an anti-slip agent on the surface of a ceramic glazed tile, wherein the anti-slip agent is painted on the glaze layer of the ceramic glazed tile.

[0059] A surface anti-slip agent for ceramic glazed tiles, which is composed of a solvent, particles dispersed in the solvent, and dispersants, auxiliary agents, surfactants and fluoride salts dissolved in the solvent;

[0060] Among them, the parts by weight of each component are: 4 parts of particles, 2 parts of dispersant, 2 parts of auxiliary agent, 13 parts of surfactant, 14 parts of fluoride salt, and the balance is solvent.

[0061] Wherein, the solvent is water, the particles are nano titanium dioxide, the dispersant is diethylene glycol dimethyl ether, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride.

[0062] Wherein, the preparation method of surfactant is:

[0063] S1: Add 150 mL of low-hydrogen silicone oil and 100 mL o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of anti-slip materials, and in particular relates to an anti-slip agent for the surface of ceramic glazed tiles and a preparation method thereof. It is composed of solvent and particles dispersed in the solvent, as well as dispersant, auxiliary agent, surfactant and fluoride salt dissolved in the solvent. The solvent is water, the particles are nano-titanium dioxide, and the dispersant is polyvinyl alcohol, sodium polyacrylate, One or more of ethyl acetate and diethylene glycol dimethyl ether are mixed, the auxiliary agent is a mixture of silicon dioxide and triethanolamine, and the fluoride salt is potassium fluoride. After being treated with the anti-slip agent prepared by the invention, the anti-slip agent can be effectively combined with the surface of the ceramic glazed tiles to play a good anti-slip effect and have a good sterilization effect at the same time.

Description

technical field [0001] The invention relates to the technical field of anti-slip materials, in particular to a surface anti-slip agent for ceramic glazed tiles and a preparation method thereof. Background technique [0002] With the improvement of the production technology of ceramic floor tiles, they are welcomed by people because of their better decorative effect, but the surface of these products is very smooth. At present, anti-slip tiles are mainly applied to the tile body by applying anti-slip agent, corrosive agent or high-temperature printing glaze. The surface is formed with an uneven structure, but the applied anti-slip layer will gradually wear away with the prolongation of use time, thus losing the anti-slip effect. The integrity and decorative effect of the glaze layer on the surface of the ceramic tile, and the texture is not easy to clean, and long-term use will cause harm to people's health. Therefore, it is necessary to develop floor tile products with envir...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/14C09D7/61C09D7/63C09D7/65
CPCC09D5/14C09D7/61C09D7/63C09D7/65
Inventor 王永生
Owner 上海世卿防滑防护科技有限公司