Non-oriented silicon steel and production method thereof

A technology of oriented silicon steel and its production method, which is applied in the field of non-oriented silicon steel and its production, can solve the problems of non-uniform magnetic properties of non-oriented silicon steel coils and increase production costs, and achieve excellent magnetic properties, best magnetic properties, and consistent magnetic properties Effect

Active Publication Date: 2021-09-17
INST OF RES OF IRON & STEEL JIANGSU PROVINCE +2
View PDF13 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004]Aiming at the problems existing in the prior art, the purpose of the present invention is to provide a non-oriented silicon steel and its production method, without significantly increasing the production cos...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Non-oriented silicon steel and production method thereof
  • Non-oriented silicon steel and production method thereof
  • Non-oriented silicon steel and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0038] One embodiment of the present invention provides a non-oriented silicon steel and a production method of the non-oriented silicon steel. In the chemical composition of the non-oriented silicon steel, the Si content is 0.8-1.1% by mass percentage, and the Mn content is 0.2-0.4% by mass percentage. Prepared by continuous acid rolling, finished annealing, cooling, coating and finishing. That is, the production method includes the steps of steelmaking, slab casting, hot rolling, normalization, acid continuous rolling, finished product annealing, cooling, coating and finishing in sequence. The production method is described in detail below in accordance with the following steps.

[0039] Step 1) Steelmaking is carried out according to the Si mass percentage of 0.8-1.1% and the Mn mass percentage of 0.2-0.4% in the chemical composition, and Sn and Sb are not added during the steel-making process, and a cast slab is prepared.

[0040] This step 1 is the steelmaking process a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Lengthaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses non-oriented silicon steel and a production method thereof. The production method comprises the following steps that steelmaking is carried out according to 0.8%-1.1% of Si and 0.2%-0.4% of Mn without adding Sn or Sb, and a blank is prepared; the casting blank is heated to 1060-1120 DEG C and subjected to heat preservation for 150 min or above, then the casting blank is rolled into an intermediate blank with the thickness of 40-45 mm, and a hot-rolled coiled plate with the thickness of 3.00+/-0.25 mm is obtained through finish rolling and coiling, wherein the initial rolling temperature of finish rolling is less than or equal to 872 DEG C+1000*(11*[Si]-14*[Mn] +21*[Al]), and the finish rolling temperature of finish rolling is less than or equal to 820 DEG C, and the coiling temperature is less than or equal to 560 DEG C; normalizing and acid continuous rolling are carried out to obtain a cold hard coil with the thickness of 0.500+/-0.005 mm, wherein the normalizing temperature is 850-900 DEG C; and the annealing temperature of a finished product is 820-880 DEG C, and cooling, coating and finishing are carried out after annealing to obtain the non-oriented silicon steel.

Description

technical field [0001] The invention belongs to the technical field of iron and steel material preparation, and relates to a non-oriented silicon steel and a production method thereof. Background technique [0002] Non-oriented silicon steel is the iron core material of the motor and generator rotor working in the rotating magnetic field, and its quality stability is of great significance for improving the quality level of the motor. The Si content of low- and medium-grade non-oriented silicon steel is controlled at 0.5% to 1.7%. The existing general production process is generally steelmaking-slab casting-hot rolling-acid rolling-annealing-coating and finishing. Among them, equiaxed ferrite + deformed ferrite is obtained in the hot rolling process, and the ferrite grain size and the proportion of equiaxed ferrite are significantly affected by the rolling temperature and coiling temperature in the hot rolling process; However, due to the rapid heat dissipation from the head...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14C22C38/16C22C38/20C22C38/26C22C38/28C22C38/42C22C38/48C22C38/50C22C33/04C21D8/02
CPCC22C38/02C22C38/04C22C38/12C22C38/14C22C38/26C22C38/28C22C38/16C22C38/20C22C38/42C22C38/48C22C38/50C22C38/06C22C38/001C22C33/04C21D8/0205C21D8/0226C21D8/0263
Inventor 岳重祥陆佳栋吴圣杰钱红伟
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products