960MPa-yield-strength low-yield-ratio maritime work steel plate and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A yield strength, 960mpa technology, applied in the field of low yield ratio marine steel plates with a yield strength of 960MPa and its preparation, can solve the problems of poor structure uniformity and performance stability, uneven structure, grain refinement, etc. The effect of improving toughness and corrosion resistance, small fluctuation of performance and uniform structure
Inactive Publication Date: 2022-02-01
北京科技大学烟台工业技术研究院
View PDF10 Cites 5 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, due to the small reduction amount of large thickness steel plate, it will lead to limited grain refinement, resulting in uneven structure in the thickness direction of the plate, and finally lead to a large difference in mechanical properties in the direction of plate thickness
The traditional quenching and tempering heat treatment (quenching + high temperature tempering) has certain advantages in the production of steel plates with higher requirements for performance stability and uniformity, but after quenching of hot rolled steel plates, the grain refinement degree is limited, and high temperature tempering will lead Yield ratio increases, unable to meet engineering applications that require low yield ratio
[0005] To sum up, there are many deficiencies in the existing marine steels with a yield strength of 960 MPa, such as poor microstructure uniformity, poor performance stability, and high yield ratio.
To achieve yield strength R at the same time eH ≥960MPa, tensile strength R m ≥1100MPa, yield strength ratio YR≤0.95, elongation after fracture A≥12% and -40°C impact toughness ≥69J comprehensive performance requirements, and have good structure uniformity and performance stability, the existing alloy composition design and the process route has been difficult to meet
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0045] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the drawings in the embodiments of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.
[0046] It should be noted that the terms "include" and "have" and any variations thereof in the embodiments of the present invention and the drawings are intended to cover non-exclusive inclusion. For example, a process, method, system, product or device comprising a series of steps or units is not limited to the listed steps or units, but optionally also includes steps or units that are not listed, or optionally further includes For other steps or units inhe...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
yield strength
aaaaa
aaaaa
yield strength
aaaaa
aaaaa
tensile strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a 960MPa-yield-strength low-yield-ratio maritime work steel plate and a preparation method thereof. The steel plate comprises the following chemical components in percentage by mass: 0.10 to 0.20 percent of C, 0.10 to 0.30 percent of Si, 1.00 to 1.50 percent of Mn, less than or equal to 0.010 percent of P, less than or equal to 0.005 percent of S, 0 to 0.50 percent of Cu, 0.20 to 0.60 percent of Cr, 0.50 to 3.00 percent of Ni, 0.20 to 0.80 percent of Mo, 0.20 to 1.00 percent of Co, 0 to 0.050 percent of Nb, 0.020 to 0.100 percent of V, 0.005 to 0.015 percent of Ti, 0.0005 to 0.0020 percent of B and the balance of Fe and inevitable impurities, and the carbon equivalent CEV is less than or equal to 0.75 percent. Based on the components, the medium-thickness steel plate with high strength and toughness and low yield ratio is prepared through smelting, controlled rolling and controlled cooling processes and (alpha+gamma) two-phase region annealing, complete austenitizing quenching and medium-low temperature tempering treatment processes. According to the prepared steel plate, the yield strength ReH is larger than or equal to 960 MPa, the tensile strength Rm is larger than or equal to 1100 MPa, the yield ratio YR is smaller than or equal to 0.95, the percentage elongation after fracture A is larger than or equal to 12%, and the impact toughness at the temperature of -40 DEG C is larger than or equal to 69 J. Compared with an existing 960MPa-grade medium-thickness steel plate, the product has good matching of strength, plasticity and toughness and low yield ratio, and is suitable for medium-thickness steel plate production.
Description
technical field [0001] The invention relates to the technical field of iron and steel materials, in particular to a steel plate for marine engineering with a yield strength of 960 MPa and a low yield strength ratio and a preparation method thereof. Background technique [0002] With the vigorous investment in national infrastructure construction in recent years, high-strength structural steel has been widely used in construction machinery, mining, hoisting mine trucks, offshore platforms, etc. Therefore, the use of high-strength structural steel Higher requirements are put forward for mechanical properties. Not only is it required to have high strength to meet the requirements of lightweight structures, but it should also have low yield ratio, excellent low-temperature toughness, weldability and corrosion resistance, etc., to meet the requirements of safety, reliability and longevity of steel structures. [0003] The demand trend of 960MPa high-strength marine steel with go...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.