Hemp colored stone coating with high adhesiveness

A technology of adhesion and color stone, applied in the direction of coating, etc., can solve the problem of low adhesion

Pending Publication Date: 2022-05-13
铁壁金钢(福建)新材料科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In terms of coating selection, hemp colored stone paint is the most widely used paint in China. Hemp colored stone paint includes base paint, granulation liquid and continuous phase. At present, the main construction method is to spray hemp colored stone paint with sp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023]A kind of high adhesion of hemp color stone coating, the basic paint of the hemp color stone paint comprises the following weight percentage of the components: deionized water 20.2%, dispersant 0.2%, defoamer 0.4%, film forming additive 0.8, titanium dioxide 2%, kaolin 0.8%, cellulose 1.5%, neutralizing agent 0.2%, silicon propylene emulsion 30%, preservative 0.4%, propylene glycol 0.8%, associated thickener 0.5%, 70 ~ 90 mesh sandstone 40%, 10wt% protective glue solution 8%, Fibre 2%.

[0024] The weight ratio between hydrophobic modified hydroxyethyl cellulose and hydroxyethyl cellulose is (0.8-1.5) :(1.5-2), hydrophobic modified hydroxyethyl cellulose is BERMOCOLL EBS-481FQ, BERMOCOLL-EHM500 or NATROSOL HE-10K; the hydroxyethyl cellulose is NATROSOL-250HHBR or TYLOSE-HS 100000YP2.

[0025] A basic paint preparation method for hemp color stone coating with high adhesion further comprises the following steps:

[0026] Deionized water, dispersant and defoamer are mixed toge...

Embodiment 2

[0032] A kind of high adhesion of hemp color stone coating, the basic paint of the hemp color stone paint comprises the following weight percentage of the components: deionized water 20.2%, dispersant 0.2%, defoamer 0.4%, film forming additive 0.8, titanium dioxide 2%, kaolin 0.8%, cellulose 1.5%, neutralizing agent 0.2%, silicon propylene emulsion 30%, preservative 0.4%, propylene glycol 0.8%, associated thickener 0.5%, 70 ~ 90 mesh sandstone 40%, 10wt% protective glue solution 8%, Fibre 2%.

[0033] The weight ratio between hydrophobic modified hydroxyethyl cellulose and hydroxyethyl cellulose is (0.8-1.5) :(1.5-2), hydrophobic modified hydroxyethyl cellulose is BERMOCOLL EBS-481FQ, BERMOCOLL-EHM500 or NATROSOL HE-10K; the hydroxyethyl cellulose is NATROSOL-250HHBR or TYLOSE-HS 100000YP2.

[0034] A basic paint preparation method for hemp color stone coating with high adhesion further comprises the following steps:

[0035] Deionized water, dispersant and defoamer are mixed toge...

Embodiment 3

[0041] A kind of high adhesion of hemp color stone coating, the basic paint of the hemp color stone paint comprises the following weight percentage of the components: deionized water 19.2%, dispersant 0.2%, defoamer 0.4%, film forming additive 0.8, titanium dioxide 2%, kaolin 0.8%, cellulose 1.5%, neutralizing agent 0.2%, silicon propylene emulsion 30%, preservative 0.4%, propylene glycol 0.8%, associated thickener 0.5%, 70 ~ 90 mesh sandstone 42%, 10wt% protective glue solution 8%, Fibre 2%.

[0042] The weight ratio between hydrophobic modified hydroxyethyl cellulose and hydroxyethyl cellulose is (0.8-1.5) :(1.5-2), hydrophobic modified hydroxyethyl cellulose is BERMOCOLL EBS-481FQ, BERMOCOLL-EHM500 or NATROSOL HE-10K; the hydroxyethyl cellulose is NATROSOL-250HHBR or TYLOSE-HS 100000YP2.

[0043] A basic paint preparation method for hemp color stone coating with high adhesion further comprises the following steps:

[0044]Deionized water, dispersant and defoamer are mixed toge...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of coatings, and discloses a hemp colored stone coating with high adhesiveness. A basic paint of the hemp colored stone coating comprises the following components in percentage by weight: 17.2 to 20.9 percent of deionized water, 0.1 to 0.2 percent of a dispersing agent, 0.2 to 0.4 percent of a defoaming agent, 0.5 to 1 percent of a coalescing agent, 1 to 2 percent of titanium dioxide, 0.2 to 1 percent of kaolin, 1 to 2 percent of cellulose, 0.1 to 0.3 percent of a neutralizing agent, 20 to 30 percent of silicone acrylic emulsion, 0.2 to 0.5 percent of a preservative, 0.5 to 1 percent of propylene glycol, 0.3 to 0.6 percent of an associate thickener and 30 to 40 percent of 70 to 90-mesh gravel; the base paint comprises the following components in percentage by weight: 5-10% of a 10wt% protective glue water solution and 1-2% of cellulose, the cellulose is a mixture of hydrophobic modified hydroxyethyl cellulose and hydroxyethyl cellulose, and the viscosity (1% of the water solution) of the hydrophobic modified hydroxyethyl cellulose is 0.5-1.5 thousand mPa.s. The base paint prepared by the process disclosed by the invention is applied to the prepared hemp colored stone coating, and the coating has the advantages of high hardness, high wear resistance, high wear resistance and the like. The hemp colored stone coating has high strength, toughness and adhesiveness.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a high-adhesive hemp colored stone coating and a preparation method thereof. Background technique [0002] Paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin or oil or emulsion, with or without adding pigments, fillers, and adding corresponding additives , a viscous liquid formulated with organic solvents or water to form a functional protective layer. [0003] In terms of coating selection, hemp colored stone paint is the most widely used paint in China. Hemp colored stone paint includes base paint, granulation liquid and continuous phase. At present, the main construction method is to spray hemp colored stone paint with spray gun. On the surface of the object to be protected, what the spray gun generally selects is a water-in-sand spray gun and a real ston...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D7/61C09D7/65
CPCC09D143/04C09D7/61C09D7/65C08K2201/014C08K2201/005C08L2205/025C08L1/284C08K3/34
Inventor 肖守地
Owner 铁壁金钢(福建)新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap