Recoverable environmental protection type material of rubber, and application

A rubber material and environment-friendly technology, applied in the field of recyclable and environment-friendly rubber materials, can solve the problems of non-recyclable materials, unfavorable environmental protection, garbage accumulation, etc., and achieve the effects of preventing soil erosion, saving energy, and good cushioning performance

Inactive Publication Date: 2006-12-06
徐维维
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the materials used in some existing facilities and the production of facilities still all adopt the old model of the 1950s, such as covering a large area of ​​land, it is known to use lawn covering, and the protection of lawn mostly adopts perforated Cement bricks; another example is planted trees. In order to protect the roots of the trees, the protective measures are to cover the soil of the roots with pebbles, or prefabricated plates with cement, and some use iron devices; in addition, the biggest defect of the above materials and products Yes, the materials are not recyclable, which will cause the accumulation of garbage, which is not conducive to environmental protection. If the construction is not done well, the iron device can also cause harm to the human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Take 70 kg of reclaimed rubber, 3.5 kg of vulcanizing agent, 0.25 kg of fast accelerator (TT), 2 kg of anti-aging agent (MB), 1.5 kg of accelerator (M), 3.5 kg of zinc oxide, 0.9 kg of stearic acid, and 5 kg of fiber kg, adhesive 15.35 kg.

[0018] The preparation method is as follows: mixing reclaimed rubber (waste car tires, bicycle tires or bicycle tires) with various ingredients; It can be made into different patterns according to needs, and models of different specifications, such as patterns composed of landscapes, patterns composed of various plant shapes, etc.; after cooling, the mold is released, and then sprayed to make it into a tree mat for protecting the soil at the root of the tree.

Embodiment 2

[0020] Take 83 kg of reclaimed rubber, 1.5 kg of vulcanizing agent, 0.05 kg of fast accelerator (TT), 1 kg of anti-aging agent (MB), 0.85 kg of accelerator (M), 1.5 kg of zinc oxide, 0.1 kg of stearic acid, and 2 kg of fiber kg, adhesive 10 kg.

[0021] The preparation method is as follows: mixing reclaimed rubber (waste car tires, bicycle tires or bicycle tires) with various ingredients; Models of different patterns and specifications can be prepared according to needs, such as squares, circles, hexagons, triangles, etc. made of geometric figures, or patterns made of landscapes, patterns made of abstract animals, and models made of various plant shapes. Pattern molds, etc.; after cooling, the molds are released, and then sprayed to make grass turns for protecting the lawn.

Embodiment 3

[0023] Take 70.85 kg of reclaimed rubber, 2.5 kg of vulcanizing agent, 0.15 kg of fast accelerator (TT), 1.5 kg of anti-aging agent (MB), 1 kg of accelerator (M), 2.5 kg of zinc oxide, 0.5 kg of stearic acid, and 3 kg of fiber kg, adhesive 18 kg.

[0024] The preparation method is as follows: mixing reclaimed rubber (waste car tires, bicycle tires or bicycle tires) with various ingredients; Prepare different shapes and different specifications according to needs, such as strip shape, backrest shape, etc., after cooling, release the mold, and then spray paint to make it into a chair for public places.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention discloses a recoverable and environmentally friendly rubber composition, which comprises: recovered rubber 70-83 wt.%, vulcanizing agent 1.5-3.5 wt.%, promoter 0.05-0.25 wt.%, anti-aging agent 1-2 wt.%, accelerator 0.5-1.5 wt.%, zinc oxide 1.5-3.5 wt.%, stearic acid 0.1-0.9 wt.%, fiber 2-5 wt.% and adhesive 10-20 wt.%. The rubber composition can be applied to manufacture mats for trees and lawns, and benches and dustbins in public places. The rubber composition has such advantages as good cushioning property, low weight and no damage to human body when impacted and can be recycled, thus is environmentally friendly.

Description

technical field [0001] The invention relates to a rubber material and its application, more specifically, the invention relates to a recyclable and environment-friendly rubber material and various applications of the material. Background technique [0002] With the rapid development of my country's economic construction, urban construction has been further accelerated, roads and bridges have been continuously expanded, and various public facilities have been used more and more. However, the materials used in some existing facilities and the production of facilities still all adopt the old model of the 1950s, such as covering a large area of ​​land, it is known to use lawn covering, and the protection of lawn mostly adopts perforated Cement bricks; another example is planted trees. In order to protect the roots of the trees, the protective measures are to cover the soil of the roots with pebbles, or prefabricated plates with cement, and some use iron devices; in addition, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More