Manufacturing method of high performance hollow cellulose fibre

A cellulose fiber and manufacturing method technology, which is applied in the manufacture of hollow filaments, single-component cellulose rayon, and rayon, etc., can solve the problems of air permeability and moisture permeability, thermal insulation, poor drape and wrinkle resistance, fiber elasticity, The problems of poor thermal insulation and antistatic performance, low hollowness, etc., can achieve the effect of improving thermal insulation and antistatic performance, improving sweat absorption and perspiration performance, and good air permeability and moisture permeability.

Active Publication Date: 2007-12-19
潍坊欣龙生物材料有限公司
View PDF0 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The fiber holes in the current mesoporous fibers mostly extend along the fiber axis, the hollowness in the fiber is low, and the cross-sections of the fiber holes are also in various forms, such as round, flat, triangular, quadrangular, plum-shaped, etc. , and the number of holes on the cross-section is also four holes, seven holes, nine holes, etc., but the fiber holes in the fiber adopt such a fiber hole and distribution form, which is easy to cause the structure of the fiber hole distribution in the fiber to be single, and the strength is low. The wet modulus is low, the sweat-absorbing and sweat-wicking performance of the fiber is poor, and the elasticity, warmth and antistatic performance of the fiber are also poor, which leads to the breathability, moisture permeability, warmth retention, drape and The wrinkle resistance is poor, which affects people's use of it

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method of high performance hollow cellulose fibre

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] 1) Selection and configuration of blowing agent:

[0011] Foaming agent: Inorganic foaming agent Na 2 CO 3 ;

[0012] The configuration of the blowing agent solution: take Na 2 CO 3 Add 3Kg of solid to 30L of softened water, stir evenly to dissolve it for later use;

[0013] 2) Preparation of spun viscose: Alkali cellulose is prepared by using cellulose cotton pulp, and the prepared alkali cellulose is added to a yellowing machine for yellowing reaction, and after yellowing for 90 minutes, add 2% ( Relative to the weight of α-cellulose) the denaturant PEG-1500 reacts uniformly until the end of yellowing. After the yellowing is over, take the prepared inorganic foaming agent solution and add it to the yellowing machine with the foaming dose of 15% relative to the weight of α-cellulose and the yellowing dissolved water. After dissolving, mix, filter, and defoam , mature and make methyl fiber be 10.5% (mass), the spinning viscose of total alkali content (sodium hydro...

Embodiment 2

[0016] 1) Selection and configuration of blowing agent:

[0017] Foaming agent: Inorganic foaming agent NaHCO 3 ;

[0018] The configuration of the blowing agent solution: take NaHCO 3 Add 2.6Kg of solid to 30L of softened water, stir evenly to dissolve it for later use;

[0019] 2) Preparation of spinning viscose: Alkali cellulose is prepared by using cellulose cotton pulp and wood pulp, and the prepared alkali cellulose is added to a yellowing machine for yellowing reaction. After yellowing for 100 minutes, add 2.5 % (α-cellulose weight) denatured agent V32 reacted uniformly until the end of yellowing. After the yellowing is finished, the prepared inorganic foaming agent solution is added to the yellowing machine together with the yellowing dissolved water at a foaming dose of 20% relative to the weight of α-cellulose. After dissolving, it is mixed, filtered, and defoamed. , maturing and making methyl fiber 8.92% (mass), total alkali content (sodium hydroxide and sodium ...

Embodiment 3

[0022] 1) Selection and configuration of blowing agent:

[0023] Foaming agent: azodicarbonamide;

[0024] The configuration of the foaming agent solution: Take 2.0Kg of the foaming agent azodicarbonamide and add it to 30L of softened water, stir evenly to dissolve it for later use;

[0025] 2) Preparation of spinning viscose: use cellulose wood pulp to prepare alkali cellulose, take the prepared alkali cellulose and add it to a yellowing machine for yellowing reaction, after yellowing for 80 minutes, add 1.8% (relative to fiber prime weight) denaturant LV3 uniform reaction until the end of yellowing. After the yellowing is over, the prepared inorganic foaming agent solution is added to the yellowing machine with the foaming amount of 8.2% relative to the weight of α-cellulose and the yellowing dissolved water. After dissolving, it is mixed, filtered, and defoamed. , mature and make methyl fiber 9.02% (mass), the spinning viscose of sodium hydroxide content 6.94%;

[0026]3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
whitenessaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The present invention relates to a preparation method of high-performance hollow cellulose fiber. Said preparation method uses cellulose pulp as raw material and makes it undergo the processes of impregnation, xanthation, dissolution, filtration, defoaming and spin-forming so as to obtain the invented high-performance hollow cellulose fiber.

Description

technical field [0001] The invention relates to a fiber preparation method, in particular to a method for preparing high-strength hollow cellulose fibers from cellulose. Background technique Background technique [0002] Hollow fiber is an important special-shaped fiber with a cavity in the cross-section along the axial direction. The fiber with this hollow structure has specific properties and styles such as good warmth retention and bulkiness, so it has been widely used by people. From the beginning, it was mainly used as The wadding filler with warm and fluffy properties has been developed to be widely used as materials for membrane separation, filling, toy products, carpets, artificial fur, advanced wool-like fabrics, advanced non-woven products, etc., in industries such as textiles, clothing, medical treatment, and wastewater treatment Play an important role. The fiber holes in the current mesoporous fibers mostly extend along the fiber axis, the hollowness in the fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F2/08D01F2/10D01D5/24
Inventor 王乐军马君志马峰刚车红莲
Owner 潍坊欣龙生物材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com