Boron-modified H-shape steel having well low-temperature impact flexibility and preparation method thereof

A low-temperature impact toughness and section steel technology, applied in the field of H-section steel, can solve the problems of process performance and service performance damage, inclusion cracks, and increase of inclusion particles.

Inactive Publication Date: 2010-09-15
SHANDONG IRON & STEEL CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Increase the inclusion particles, which is easy to cause inclusion cracks, which will damage the process performance and service performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Boron-modified H-shape steel having well low-temperature impact flexibility and preparation method thereof
  • Boron-modified H-shape steel having well low-temperature impact flexibility and preparation method thereof
  • Boron-modified H-shape steel having well low-temperature impact flexibility and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention is based on Q345 H-shaped steel that does not require special heat treatment, and in consideration of actual steelmaking control ability and product quality, by adding boron and optimizing steel composition, a H-shaped steel with good low-temperature impact toughness is obtained. The technical scheme is as follows:

[0019] A boron-added Q345 H-shaped steel with good low-temperature impact toughness, the steel composition weight percentage is as follows (%):

[0020] C 0.08~0.20, Mn 1.00~1.60, Si 0.10~0.55, P≤0.025, S≤0.025, Nb 0.015~0.035, B 0.0005~0.0012, and the balance is Fe and trace impurities.

[0021] Preferably, a kind of boron-added Q345H type steel, the weight percentage of steel composition is as follows (%):

[0022] C 0.10~0.18, Mn 1.00~1.40, Si 0.10~0.40, P≤0.015, S≤0.015, Nb 0.015~0.030, B 0.0005~0.0010, the balance is Fe and trace impurities.

[0023] Further preferably, a kind of boron-added Q345H type steel, the weight percentag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a boron-modified H type steel having good low-temperature impact toughness and the preparing method thereof. The steel is composed of 0.08 to 0.20 by weight percentage of C, 1.00 to 1.60 by weight percentage of Mn, 0.10 to 0.55 by weight percentage of Si, no more than 0.25 by weigh percentage of P, no more than 0.025 by weight percentage of S, 0.015 to 0.035 by weight percentage of Nb, 0.0005 to 0.0012 by weight percentage of B, and the balance Fe and trace impurity. During melting process, the gas content is controlled: no more than 0.004% of N, and no more than 0.0085% of O. According to the invention, the low-temperature impact toughness of Q345 H type steel is greatly improved; compared with Chinese standard, -40 DEG C AKV has a large surplus, the product quality is easy to be guaranteed; the Q345 H type steel can also be applied to regions having more severe condition.

Description

technical field [0001] The invention relates to an H-shaped steel used as a building component, in particular to a boron-added Q345 H-shaped steel with good low-temperature impact toughness and a preparation method thereof. technical background [0002] Hot-rolled H-shaped steel is a new type of economical construction steel, which is widely used in high-rise buildings, factories, bridges, ships, lifting and transportation machinery, equipment foundations, supports, foundation piles and other fields. The product has economical and reasonable cross-sectional shape, mechanical properties Good features. Compared with I-beam, H-beam section modulus is larger. Under the same bearing conditions, it can save 10-15% of metal. Because the inside and outside of the legs are parallel, and the legs are at right angles, they can be assembled into components, which can be Save welding and riveting workload up to 25%. Compared with the concrete structure, the H-shaped steel structure can ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/12
Inventor 任浩陶登奎王作成张公海高俊庆赵修领崔国涛董昌兴王学新冯伟刘军
Owner SHANDONG IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com