Electrothermal copper-smelting slag depleted furnace

A slag smelting and electrothermal technology is applied in the field of copper smelting slag electrothermal dilution furnaces, which can solve the problems of large floor space and long process flow, and achieve the effects of reducing power consumption, reducing costs and improving dilution efficiency.

CN101839631AActive Publication Date: 2010-09-22CHINA ENFI ENGINEERING CORPORATION
0 Cites 19 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2010-09-22

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses an electrothermal copper-smelting slag depleted furnace, which comprises a furnace body, supports, an oxygen lance and electrodes; the furnace body comprises a furnace shell defining a furnace chamber and a refractory material layer arranged on the inner wall of the furnace shell, the furnace body is provided with a feed inlet for feeding copper-smelting slag and vulcanizing agent into the furnace chamber, a siphon inlet for discharging copper matte, a waste slag-discharging outlet, electrode plugholes, a smoke outlet and an oxygen lance plughole, wherein the oxygen lance plughole is formed at the bottom of the furnace shell; the furnace body is supported by the supports; the oxygen lance is plugged into the oxygen lance plughole; and the electrodes are plugged into the furnace body via the electrode plugholes. When the electrothermal copper-smelting slag depleted furnace is used for bottom-blowing electrothermal copper-smelting slag depletion, the copper content in waste slag can be reduced, and electricity consumption can be decreased.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to an electrothermal depletion furnace for copper smelting slag. Background technique

[0002] At present, in order to reduce the blowing load, large-scale copper smelters using advanced smelting technology all adopt higher copper matte grades, that is, the output copper matte grades are higher, and the copper content in the higher-grade copper matte is 50%. In the range of ~70%, the copper content of copper smelting slag fluctuates in the range of 2% ~ 8%.

[0003] In order to recover the copper in the copper smelting slag, the copper smelting slag is traditionally depleted by an electric furnace. The copper smelting slag is added to the electric furnace, and the copper smelting slag is heated by electrode heating so that the copper in the copper smelting slag settles in the form of copper matte. Come down and separate from the waste residue.

[0004] The furnace body of the traditional depleted electric furnace has a feeding p...

Examples

Embodiment Construction

[0042] The embodiments described below by referring to the figures are exemplary only for explaining the present invention and should not be construed as limiting the present invention.

[0043] Refer below Figure 1-3and 5-7 describe the electrothermal depletion of copper smelting slag according to one embodiment of the present invention.

[0044] Such as figure 1 As shown, the electrothermal depletion furnace for copper smelting slag according to an embodiment of the present invention includes a furnace body 1 , a support 4 , an oxygen lance 6 and an electrode 7 .

[0045] exist figure 1 In the example shown, the furnace body 1 of the electrothermal depletion furnace for copper smelting slag is a horizontal cylindrical vessel, but the present invention is not limited thereto. The furnace body 1 includes a furnace shell 1a defining a furnace, and a refractory material layer 1b provided on the inner wall of the furnace shell 1a. The furnace body 1 is formed with a feed por...