Ag-Mo-RE high-strength heat resisting aluminum alloy material using C as modificator and preparation method thereof

An aluminum alloy material, ag-mo-re technology, applied in the field of aluminum alloy materials and its preparation, can solve the problems of extensive melt treatment process, low product yield, poor reusability of waste materials and slag materials, etc.

Inactive Publication Date: 2011-04-20
GUIZHOU HUAKE ALUMINUM MATERIAL ENG TECH RES
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0032] The technical problem to be solved by the present invention is to solve the existing problems in the field of high-strength aluminum alloys, such as extensive melt treatment process, poor quality, large thermal cracking tendency, poor casting performance, low product yield, low high-temperature strength, waste materials and slag recycling. For technical problems such as poor usability, guided by high-quality melt, solid solution and phase diagram theory, using C element as a high-efficiency modifier, by optimizing the alloy main element Cu, Mn and rare earth element formula, reducing the quasi-solid phase temperature range of the alloy, and solving the problem of casting The general problem of high thermal cracking tendency and low high-temperature strength of products (including instantaneous strength and durable strength); the low-cost multi-element microalloying element formula is preferred for the cultivation and fine-graining of high-temperature phases and strengthening phases in solid solutions Create material basic conditions; and optimize smelting and heat treatment technology to realize sufficient cultivation of high-temperature phase and strengthening phase in solid solution and full play of fine-graining effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ag-Mo-RE high-strength heat resisting aluminum alloy material using C as modificator and preparation method thereof
  • Ag-Mo-RE high-strength heat resisting aluminum alloy material using C as modificator and preparation method thereof
  • Ag-Mo-RE high-strength heat resisting aluminum alloy material using C as modificator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0113] Example 1: Cu-1.0%, characteristic microalloying elements-Ag, Mo, basic microalloying rare earth elements-lanthanum La, high-efficiency modification elements-C

[0114] (1) Weigh the various alloying elements required according to the ingredient calculation table, as follows.

[0115]

[0116] (2) Add an appropriate amount of aluminum ingots to the melting furnace, heat it to melt it completely and keep it warm at 700-800°C; in order to prevent the melt from inhaling too much air, the melting process should be as short as possible in a closed environment Finish.

[0117] (3) Add Al-Mn, Al-Ti, Al-Ag, Al-Mo, Al-Zr master alloy or mixed metal additives (including salt compounds) according to the formula ratio, and then add Cu pure metal and Al-Cd master alloy or mixed metal additives, then add C and rare earth element La, and stir evenly.

[0118] Mixed metal additives refer to cake-shaped or massive non-sintered powder metallurgy products for adding and adjusting all...

Embodiment 2

[0124] Example 2: Cu-4.2%, characteristic microalloying elements-Ag, Mo, basic microalloying rare earth elements La, Ce mixed rare earth, high-efficiency modification element-C

[0125] (1) Weigh the various alloying elements required according to the ingredient calculation table, as follows.

[0126]

[0127]

[0128] (2) Add an appropriate amount of aluminum ingots to the melting furnace, heat it to melt it completely and keep it warm at 700-800°C; in order to prevent the melt from inhaling too much air, the melting process should be as short as possible in a closed environment Finish.

[0129] (3) Add Al-Mn, Al-Ti, Al-Ag, Al-Mo, Al-Zr master alloy or mixed metal additives (including salt compounds) according to the formula ratio, and then add Cu pure metal and Al-Cd master alloy or mixed metal additives, then add C and rare earth elements La, Ce mixed rare earth, and stir evenly.

[0130] Mixed metal additives refer to cake-shaped or massive non-sintered powder meta...

Embodiment 3

[0136] Example 3: Cu-5.1%, characteristic microalloying elements-Ag, Mo, basic microalloying rare earth element europium Eu, high-efficiency modification element-C

[0137] (1) Weigh the various alloying elements required according to the following ingredient calculation table, as follows.

[0138]

[0139] (2) Add an appropriate amount of aluminum ingots to the melting furnace, heat it to melt it completely and keep it warm at 700-800°C; in order to prevent the melt from inhaling too much air, the melting process should be as short as possible in a closed environment Finish.

[0140] (3) Add Al-Mn, Al-Ti, Al-Ag, Al-Mo, Al-Zr master alloy or mixed metal additives (including salt compounds) according to the formula ratio, and then add Cu pure metal and Al-Cd master alloy or mixed metal additives, then add C and rare earth element europium Eu, and stir evenly.

[0141] Mixed metal additives refer to cake-shaped or massive non-sintered powder metallurgy products for adding a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an Ag-Mo-RE high-strength heat resisting aluminum alloy material using C as a modificator and a preparation method thereof. The Ag-Mo-RE high-strength heat resisting aluminum alloy material using C as the modificator comprises the following components in percentage by weight: 1.0-10.0% of Cu, 0.05-1.5% of Mn, 0.01-0.5% of Cd, 0.01-0.5% of Ti, 0.0001-0.15% of C, 0.01-1.0% of Zr, 0.01-1.0% of Ag, 0.01-1.0% of Mo, 0.05-5% of RE, and the balance of A1. In the invention, a high-quality fondant, a solid solution and a phase diagram theory are used as instructions; the quasi solid-phase temperature range of the alloy is reduced through the preference of the main elements such as Cu, Mn and RE of the alloy, thereby solving the problems of large hot crack tendency during the casting, low high-temperature strength of the product and the like; and multi-element micro-alloyed elements are preferred so that the high-strength heat resisting aluminum alloy material is developed finally.

Description

technical field [0001] The invention relates to an aluminum alloy material and a preparation method thereof, in particular to a C-modified Ag-Mo-RE high-strength heat-resistant aluminum alloy material and a preparation method thereof. Background technique [0002] Aluminum alloy is a relatively young metal material, which only began to be used industrially in the early 20th century. During World War II, aluminum was mainly used in the manufacture of military aircraft. After the war, due to the sharp decrease in the demand for aluminum in the military industry, the aluminum industry began to develop civilian aluminum alloys, expanding its application scope from the aviation industry to the construction industry, container packaging industry, transportation industry, electric power and electronics industry, Various sectors of the national economy such as machinery manufacturing and petrochemicals are applied to people's daily lives. At present, aluminum is used in a large am...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(China)
IPC IPC(8): C22C21/00C22C21/12C22C1/02C22C1/03C22C1/06C22F1/04C22F1/057
Inventor张中可车云陈新孟门三泉李祥曹跃清胥光酉李荣华
OwnerGUIZHOU HUAKE ALUMINUM MATERIAL ENG TECH RES