Hexabromodiphenyl ether PEN fibers and preparation method thereof

A technology of hexabromoether and fiber, applied in the field of hexabromoether PEN fiber and its preparation, can solve problems such as no reports on hexabromoether PEN fiber, and achieves less addition, good thermal stability and good flame retardant effect Effect

Inactive Publication Date: 2011-05-04
翟育明
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] At present, there is no report of PEN fiber with hexabromoether as a flame retardant

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1. The composition of hexabromoether PEN masterbatch

[0031] Hexabromoether 1%

[0032] Compatibilizer 0.1%

[0033] PEN slice 98.9%

[0034] The model of described hexabromoether is Doher 804, as the flame retardant of PEN fiber;

[0035] Described compatibilizer is white oil;

[0036] Two, the preparation method of hexabromoether PEN masterbatch

[0037] A preparation method of hexabromoether PEN fiber masterbatch, the specific steps of which are as follows: hexabromoether and PEN are blended and then granulated, wherein the blending time is 1-3h, and the temperature is 200-300 DEG C to obtain six Bromoether PEN fiber masterbatch;

[0038] 3. The composition of hexabromoether PEN fiber raw materials

[0039] Hexabromoether PEN fiber masterbatch 2%

[0040] PEN slices 98%

[0041] Four, the preparation method of hexabromoether PEN fiber

[0042] A preparation method of hexabromoether PEN fiber, the specific steps of which are as follows: mixing hexabromoether...

Embodiment 2

[0044] 1. The composition of hexabromoether PEN masterbatch

[0045] Hexabromoether 3%

[0046] Compatibilizer 0.5%

[0047] PEN slice 96.5%

[0048] Two, the preparation method of hexabromoether PEN masterbatch

[0049] A preparation method of hexabromoether PEN fiber masterbatch, with embodiment 1;

[0050] 3. The composition of hexabromoether PEN fiber raw materials

[0051] Hexabromoether PEN fiber masterbatch 4%

[0052] PEN slices 96%

[0053] Four, the preparation method of hexabromoether PEN fiber

[0054] A preparation method of hexabromoether PEN fiber is the same as Example 1.

Embodiment 3

[0056] 1. The composition of hexabromoether PEN masterbatch

[0057] Hexabromoether 5%

[0058] Compatibilizer 0.5%

[0059] PEN slice 94.5%

[0060] Two, the preparation method of hexabromoether PEN masterbatch

[0061] A preparation method of hexabromoether PEN fiber masterbatch, with embodiment 1;

[0062] 3. The composition of hexabromoether PEN fiber raw materials

[0063] Hexabromoether PEN fiber masterbatch 5%

[0064] PEN slices 95%

[0065] Four, the preparation method of hexabromoether PEN fiber

[0066] A preparation method of hexabromoether PEN fiber is the same as Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to hexabromodiphenyl ether polythy-lene naphtalate (PEN) fibers and a preparation method thereof. The hexabromodiphenyl ether PEN fibers are prepared from the following raw materials in percentage by mass: 1 to 10 percent of hexabromodiphenyl ether PEN masterbatch and the balance of PEN slices, wherein the hexabromodiphenyl ether PEN masterbatch is prepared from the following raw materials in percentage by mass: 1 to 10 percent of hexabromodiphenyl ether, 0.1 to 1 percent of compatilizer and the balance of PEN slices. The invention has the advantages that: a flame retardant has good performance and flame retardancy; the hexabromodiphenyl ether PEN fibers can be prepared by the conventional process easily and conveniently; and the hexabromodiphenyl ether PEN fibers have a wide application range.

Description

【Technical field】 [0001] The invention relates to the technical field of flame-retardant fibers, in particular to a hexabromoether PEN (polytrimethylene terephthalate) fiber and a preparation method thereof. 【Background technique】 [0002] Generally, flame retardants can be divided into two categories: organic flame retardants and inorganic flame retardants according to their chemical composition. Organic flame retardants are divided into two series: phosphorus series and halogen series. The former is mostly liquid at room temperature, has a large amount of smoke and is toxic, and requires a large amount of H and O elements in the flame-retardant structure to be dehydrated to form a carbonized layer, so its application is greatly limited. Halogen flame retardants mainly include chlorine and bromine. In terms of usage, brominated flame retardants are more commonly used. This is mainly due to the relatively low corrosiveness and toxicity of bromide after thermal decompositi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/07
Inventor 翟育明
Owner 翟育明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap