Method for manufacturing gold tailings ash aggregates
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of gold tailings and manufacturing methods, applied in the field of building materials manufacturing, can solve the problems of gold tailings powder ceramsite blank, loss of life and property, pollution of the environment, etc.
Active Publication Date: 2012-06-20
范峪铭
View PDF5 Cites 8 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, there are few studies on the utilization of gold tailings powder, and the sintering of gold tailings powder ceramsite is still blank.
[0003] Gold tailings powder is the solid waste discharged by the gold production industry. It is mostly piled up in mountains, rivers and rivers, occupying land and polluting the environment. Some of them will cause major accidents and cause great losses to people's lives and properties.
In the past, tailings powder was used as a raw material for the production of glass-ceramic products, but its development scale was limited, and there were few ways to utilize gold tailings powder. How to use it on a large scale is a new subject that needs to be studied and solved urgently.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0023] Weight ratio: gold tailings powder 90%;
[0024] Coal powder 10%;
[0025] Manufacturing process:
[0026] 1. Dry the gold tailings powder first, and use a 0.30mm square hole sieve to sieve;
[0027] 2. Separately measure gold tailings powder and coal powder below 0.3mm after sieving;
[0028] 3. Put the measured two materials into the blender, first dry stir for about 2 minutes, then add 1 / 2 of water, and then wet stir for about 2 minutes;
[0029] 4. Send the stirred gold tailings powder mixture into the ball forming plate, add 1 / 2 of water, and rotate into balls;
[0030] 5. Put the gold tailings powder ceramsite raw meal balls into the static continuous ceramsite sintering kiln for roasting, the sintering temperature is 1220℃~1350℃, the sintering time is 2.0~2.5 hours, the gold tailings powder ceramsite raw meal balls are sintered In the kiln, it goes through three process stages of preheating, sintering and cooling in sequence, and cools down to below...
Embodiment 2
[0034] Weight ratio: gold tailings powder 92%;
[0035] Coal powder 8%;
[0036] Manufacturing process:
[0037] 1. Dry the gold tailings powder first, and use a 0.30mm square hole sieve to sieve;
[0038] 2. Measure the sieved gold tailings powder and coal powder below 0.3mm respectively;
[0039] 3. Put the measured two materials into the blender, first dry stir for about 2 minutes, then add 1 / 2 of water, and then wet stir for about 2 minutes;
[0040] 4. Send the stirred gold tailings powder wet mixture into the ball forming plate, add 1 / 2 of water, and rotate into balls;
[0041] 5. Put the gold tailings powder ceramsite raw meal balls into the static continuous ceramsite sintering kiln for roasting, the sintering temperature is 1220℃~1350℃, the sintering time is 2.0~2.5 hours, the gold tailings powder ceramsite raw meal balls are sintered In the kiln, it goes through three process stages of preheating, sintering and cooling in sequence, and cools down to bel...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention relates to a method for manufacturing gold tailings ash aggregates, which comprises materials and proportions, as well as a manufacturing process flow. The materials comprise 90 to 92 percent of gold tailings ash and 8 to 10 percent of pulverized coal. The process flow comprises the following steps of: baking the gold tailings ash, screening, and measuring; measuring the pulverized coal; conveying the gold tailings ash and the pulverized coal into a stirrer to be stirred in a dry state for about 2 minutes; adding half amount of water, and stirring in a wet state for about 2 minutes; feeding the stirred wet ash material into a balling pan, and adding the rest half amount of water to produce balls; putting raw gold tailings ash aggregate balls into a static continuous aggregate sintering kiln for roasting; and discharging from the kiln, cooling, crushing and separating. The method is characterized in that: the gold tailings ash and the pulverized coal are respectively measured after the gold tailings ash is baked and screened, are stirred in the stirrer in the dry state and the wet state and pelletized by adding water; the raw gold tailings ash aggregate balls are sentto the sintering kiln for being roasted; and the gold tailings ash has the advantages of high waste utilization, high aggregate strength and low water absorption rate through three sintering process steps, namely preheating, sintering and cooling.
Description
technical field [0001] The invention relates to the technical field of building material manufacturing, specifically a method that utilizes gold tailings powder in industrial waste slag as the main raw material, and a small amount of coal powder (or coal gangue powder or fly ash with high loss on ignition) as the secondary raw material. A method for manufacturing gold tailing powder ceramsite. Background technique [0002] Since the 1950s, Britain was the first in the world to use industrial waste residue-fly ash to produce fly ash ceramsite. my country built two production lines for sintered fly ash ceramsite in Tianjin Silicate Products Factory and Lanzhou in 1964, and reached a production climax in the 1970s and 1980s. It's at a standstill for a number of reasons. Until the 1990s, the climax of comprehensive utilization of fly ash was set off. my country is a large coal-producing country and a large coal-fired power generation country. The proportion of coal for heating ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).