Room-temperature type power insulator anti-fouling flashover paint, preparation method thereof and power insulator

A technology of anti-fouling flashover coatings and insulators, applied in the field of coatings, can solve the problems of decreased migration speed of coating hydrophobicity and inability to eradicate them

Active Publication Date: 2015-05-20
MAINTENANCE COMPANY OF STATE GRID XINJIANG ELECTRIC POWER COMPANY +1
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although this measure can improve the performance of the RTV coating, it cannot eradicate the above-mentioned defects, and will cause other adverse effects
For example, with the increase of silica, the hydrophobic migration speed of the coating will decrease significantly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Room-temperature type power insulator anti-fouling flashover paint, preparation method thereof and power insulator
  • Room-temperature type power insulator anti-fouling flashover paint, preparation method thereof and power insulator
  • Room-temperature type power insulator anti-fouling flashover paint, preparation method thereof and power insulator

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Mix 30 parts of block resin (produced by Shenzhen Taike Technology Co., Ltd., a typical resin with hydrophobic migration properties) and 70 parts of silicone acrylic resin, add an appropriate amount of butyl acetate to adjust the concentration of the mixture, Slowly stir and blend in a closed container for 5 hours, take out the product, and add 0.5 part of leveling agent to obtain a room temperature type anti-pollution flashover hard coating for electric power external insulation.

[0034] When in use, take out 100 parts of antifouling flash hard paint, add 0.1 part of zirconium isooctanoate, 0.1 part of dibutyltin dilaurate, 1 part of ethyl orthosilicate, stir well, adjust the viscosity with butyl acetate, Then it is used for spraying or brushing on the lower surface of the insulating part of the insulator, and the thickness of the coating is 0.01mm.

[0035] Such as figure 1 As shown, it is a cross-sectional view of the right half of the outer surface of an axisymmet...

Embodiment 2

[0037] Mix 50 parts of block resin (Shenzhen Taike Technology Co., Ltd.) with 50 parts of silicone acrylic resin, add an appropriate amount of solvent to adjust the concentration of the mixture, stir and blend slowly in a closed container at room temperature for 7 hours, take out the product, add leveling 2 parts to obtain room temperature type electric power external insulation anti-pollution flashover hard coating.

[0038] When using, take out 100 parts of antifouling flash hard paint, add 1 part of zirconium isooctanoate, 1 part of dibutyltin dilaurate, N-(ethylaminoethyl)-3-aminopropylmethyl dimethoxy 1 part of silane, 7 parts of tetraethyl orthosilicate, stir evenly, adjust the viscosity with butyl acetate, and then spray or brush on the lower surface of the insulating part of the insulator, and the coating thickness is 0.02mm.

Embodiment 3

[0040] Mix 70 parts of block resin (Shenzhen Taike Technology Co., Ltd.) with 30 parts of silicone acrylic resin, add an appropriate amount of solvent to adjust the concentration of the mixture, stir and blend slowly in a closed container at room temperature for 7 hours, take out the product, add leveling The antifouling flashover hard coating for room temperature electric power external insulation can be obtained by adding 5 parts of the agent.

[0041] When using, take out 100 parts of antifouling flash hard paint, add 2 parts of zirconium isooctanoate, 2 parts of dibutyltin dilaurate, N-(ethylaminoethyl)-3-aminopropylmethyl dimethoxy 2 parts of silane and 10 parts of tetraethyl orthosilicate are stirred evenly, and the viscosity is adjusted with butyl acetate, and then sprayed or brushed on the lower surface of the insulating part of the insulator, and the coating thickness is 0.5mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses room-temperature type power insulator anti-fouling flashover paint, a preparation method thereof and a power insulator. The paint comprises a hard paint and a room-temperature curing agent, wherein the hard paint comprises the following components: resin with hydrophobic migrating performance, silicone acrylic resin, a solvent and a leveling agent; and the room-temperature curing agent comprises the following components: a catalyst and ethyl orthosilicate. Compared with the prior art, the paint has excellent hardness, a self-cleaning property, hydrophobicity and curing performance.

Description

technical field [0001] The invention relates to coatings, in particular to a room temperature type power insulator anti-pollution flashover coating and a preparation method thereof, as well as a power insulator. Background technique [0002] Anti-pollution flashover room temperature vulcanized silicone rubber coating (RTV coating) has been widely used in the external insulation of power systems, which has prevented the occurrence of pollution flashover accidents to a certain extent. However, difficult defects are also exposed during use, which is manifested in the poor self-cleaning performance of the RTV coating. The surface of silicone rubber material has the characteristics of "oiliness", which is easier to absorb dirt than the surface of hard and smooth materials. After absorbing dirt, it is more difficult to clean the dirt on the surface of RTV under the action of natural wind and precipitation. Therefore, compared with the surface of glass and porcelain insulators, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/04C09D201/00C09D7/12C09D5/16H01B17/42H01B17/50
Inventor 王威何晓伟贾志东王黎明关志成
Owner MAINTENANCE COMPANY OF STATE GRID XINJIANG ELECTRIC POWER COMPANY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com