A kind of nano-type ultra-thin coating powder coating and preparation method thereof

A powder coating and nano-type technology, which is applied in the direction of powder coating, coating, polyester coating, etc., can solve the problems of ultra-thin performance, leveling spraying effect, poor development, and low production efficiency. and other problems, to achieve the effects of strong practicability, excellent dispersion performance, coating film density and water resistance

Inactive Publication Date: 2015-12-09
YANTAI BANGZHOU CHEM
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] ①The current ultra-fine powder coatings are pursuing thin coating performance, paying too much attention to the fineness of powder particle size, so the yield of finished products in the process of processing is low, the production efficiency is low, and it has not been well developed;
[0004] ②It is difficult to have both ultra-thin performance, leveling property and spraying effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nano-type ultra-thin coating powder coating and preparation method thereof
  • A kind of nano-type ultra-thin coating powder coating and preparation method thereof
  • A kind of nano-type ultra-thin coating powder coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A nano-type ultra-thin coating powder coating, the weight ratio of its raw materials is composed of the following table:

[0024] Formulation of table 2 the present invention forms

[0025]

[0026] Mix the raw materials uniformly in proportion, extrude and grind the finished product. Spraying with an electrostatic spray gun to obtain a film thickness of 38um and a spraying area of ​​18m 2 / Kg coating.

Embodiment 2

[0028] A nano-type ultra-thin coating powder coating, the weight ratio of its raw materials is composed of the following table:

[0029] Formulation of table 3 the present invention forms

[0030]

[0031] Mix the raw materials uniformly in proportion, extrude and grind the finished product. Spraying with an electrostatic spray gun to obtain a film thickness of 41um and a spraying area of ​​16.5m 2 / Kg coating.

Embodiment 3

[0033] A nano-type ultra-thin coating powder coating, the weight ratio of its raw materials is composed of the following table:

[0034] Formulation of table 3 the present invention forms

[0035]

[0036] Mix the raw materials uniformly in proportion, extrude and grind the finished product. Use an electrostatic spray gun to spray to obtain a film thickness of 45um and a spraying area of ​​15m 2 / Kg coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a nanometer ultrathin coat powdery coating. The nanometer ultrathin coat powdery coating is composed of 50-60 parts by weight of a resin, 5-10 parts by weight of a curing agent, 5-8 parts by weight of a leveling agent, 0.2-0.6 parts by weight of benzoin, 5-7 parts by weight of nanometer titanium-containing powder, 7-8 parts by weight of a filler and 18-22 parts by weight of a pigment. The coating is prepared through uniformly mixing the above raw materials according to proportions, extruding and grinding. The coating has an excellent dispersion performance, and allows a coat using the coating to have the advantages of good ultrathin spraying performance, improvement of various performances of the coat to different degrees, good leveling property, large spray area, and greatly improved coat compactness and water tolerance.

Description

technical field [0001] The invention relates to an ultra-thin powder coating, in particular to a nano-type ultra-thin coating powder coating and a preparation method thereof. Background technique [0002] At present, the powder coating industry is developing rapidly, focusing on environmental protection and energy saving. The research and development and application of ultra-thin coatings have also become the direction of industry development. The larger the spraying area, the lower the cost of use, but there are also the following problems: [0003] ①The current ultra-fine powder coatings are pursuing thin coating performance, paying too much attention to the fineness of powder particle size, so the yield of finished products in the process of processing is low, the production efficiency is low, and it has not been well developed; [0004] ② It is difficult to have both ultra-thin performance, leveling property and spraying effect. Contents of the invention [0005] The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D133/00C09D163/00C09D167/08C09D7/12C09D5/03
Inventor 周占斌刘晓明陈云
Owner YANTAI BANGZHOU CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com