A kind of preparation method of fiber reinforced foam concrete

A foam concrete and fiber-reinforced technology, applied in ceramic products, applications, household appliances, etc., can solve the problems of large shrinkage, easy cracking, and low compressive strength of thermal insulation materials, so as to improve crack resistance, increase toughness and wear resistance , the effect of low dry density

Active Publication Date: 2016-04-13
SHENYANG JIANZHU UNIVERSITY
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the problems of large shrinkage, low compressive strength and easy cracking of existing foam concrete external wall insulation materials, and to provide a safe, durable, feasible and low-cost fiber-reinforced foam concrete. Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of fiber reinforced foam concrete, its component is:

[0032] Raw material mass g

[0033] (1) Cementitious material

[0034] Rapid hardening sulfoaluminate cement 980~990

[0035] (2) Water 550~650

[0036] (3) Additives

[0037] Fiber 10~20

[0038] (4) Foam: the volume (liter) accounts for 750% of the volume of the added water.

[0039] Its preparation process is:

[0040] 1. Selection of raw materials: The fast-hardening sulfoaluminate cement is 42.5R fast-hardening sulfoaluminate cement produced by Tangshan Jidong Cement Co., Ltd.; the foaming agent is HT composite foam from Henan Huatai Building Materials Development Co., Ltd. agent; what the fiber selects is the 3mm polypropylene fiber produced by Liaoyang Juxin Fiber Co., Ltd.

[0041] 2. Pour the quick-hardening sulphoaluminate cement and fiber into the mixing pot, stir slightly (low speed, to make the material uniform), add water, continue stirring at low speed (50-100r / min) for 2 minutes, then h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing fiber-enhanced foam concrete, wherein mekralon is added for preparing the foam concrete, thereby enhancing rupture strength of the foam concrete and reducing contraction. The fiber-enhanced foam concrete is prepared by the following components by weight: 980-990g of sulphoaluminate early strength cement, 10-20g of fiber, and 550-650g of water, wherein the volume (ml) of the foam is 600-900% that of the added water. The method comprises: dispersing the mekralon in the sulphoaluminate early strength cement based on the formula amounts, stirring in a cement paste mixer, stewing for 20min after uniformly stirring cement slurry, and then adding foam, to form the uniformly-mixed slurry; and forming, maintaining in a standard maintaining case, and then detecting rupture strength and contraction value thereof. The rupture strength is greatly raised, and most reaches 1.45 times that without adulteration, and toughness is greatly improved.

Description

technical field [0001] The invention relates to a light-weight external thermal insulation material for building exterior walls, in particular to a preparation method for a light-weight fiber-reinforced foamed concrete with good thermal insulation and fireproof performance that can meet certain strength requirements. Background technique [0002] With the vigorous development of the construction industry, the safety of building materials has also received increasing attention. External thermal insulation materials for building exterior walls must not only have the effect of building energy conservation, but also have excellent fire and flame retardant properties. In view of the frequent occurrence of building fire accidents, the key issue of how to safely apply external thermal insulation materials for exterior walls was raised. Foamed concrete, as a new type of inorganic fireproof and thermal insulation material, not only has the performance of ordinary organic thermal ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B16/06C04B38/02
Inventor 王晴吴陶俊刘锁李明泽蒋威
Owner SHENYANG JIANZHU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka