A slope-type, iron-making furnace technology, applied in reduction iron-making process, integrated reduction iron-making furnace, reduction iron-making furnace and iron-making process field, can solve low production efficiency, hanging wall, uneven reaction of furnace materials And other issues

Inactive Publication Date: 2015-04-08
SHANDONG UNIV +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to improve the existing defects of the above-mentioned iron-making furnace, and provide a partial slope reduction iron-making furnace. Wall, low production efficiency and other problems, more conducive to large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Local slope type reduction ironmaking furnace and process
  • Local slope type reduction ironmaking furnace and process
  • Local slope type reduction ironmaking furnace and process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] Such as figure 1 The partial slope reduction ironmaking furnace shown (referred to as the reduction ironmaking furnace, the same below) includes a closed furnace body 1, and an exhaust port 2 for exhausting gas is provided on the furnace body. The exhaust port is located in the middle of the furnace body, close to The position of the last reduction chamber is equipped with an induced draft fan and other devices on the exhaust port to discharge the carbon dioxide in the furnace body. Four reduction chambers are arranged in sequence in the furnace body. Of course, the number of reduction chambers can be freely allocated in practical applications. Here only Taking a reduction furnace with four reduction chambers as an example to illustrate its structure, the four reduction chambers are independent. The top of the reduction chamber is provided with a feed port 4, and the bottom is provided with a discharge port 5. Both the feed port and the discharge port are located outsi...

Embodiment 2

[0062] The structure of the local slope reduction ironmaking furnace of the present invention can be adjusted appropriately on the basis of Embodiment 1, for example, the number of air extraction device and air supply device can be one, and one can also be arranged at each cavity, When only one is used, the air extraction device and the air delivery device are preferably installed at a position away from the exhaust port.

Embodiment 3

[0064] The structure of the local slope-type reduction ironmaking furnace of the present invention can be appropriately adjusted on the basis of Embodiment 1, for example, an air inlet can be arranged at the position above the baffle and below the baffle at each cavity.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a partial slope reduction ironmaking furnace and a reduction ironmaking process. The reduction chamber of the ironmaking furnace is designed with a partial slope. The reduction chamber includes a pre-reduction zone, a transition zone and a melting zone from top to bottom. , the pre-reduction zone and the melting zone are vertically located in the furnace body, and the transition zone is arranged obliquely, forming a fixed angle with the horizontal line of the furnace body; heat-resistant baffles are provided in each cavity, and the heat-resistant baffles Fixed on the furnace body, there is a gap between the heat-resistant baffle and the reduction chamber. The ironmaking furnace of the present invention can be flexibly adjusted for smelting reduction and direct reduction, can realize the recycling of carbon monoxide gas, and greatly reduces the cost, and adopts the ironmaking furnace for ironmaking to realize continuous production, stable operation, uniform heating of materials, and rapid reaction Completely, the phenomenon of material hanging on the wall is also effectively controlled, there is no problem of waste water treatment, it is friendly to the environment, and meets the requirements of green environmental protection and clean production.

Description

technical field [0001] The invention relates to a reduction ironmaking furnace and ironmaking process, in particular to an integrated reduction ironmaking furnace with a partial slope structure in the reduction chamber and a reduction ironmaking process using the ironmaking furnace, which belongs to iron ore smelting technology field. Background technique [0002] At present, the products refined from iron ore are mainly molten iron and sponge iron. The processes for refining iron ore into molten iron mainly include blast furnace method, direct reduction method, smelting reduction method, and plasma method. The smelting reduction method has attracted the attention of experts at home and abroad because of its advantages such as less environmental pollution, less investment, and short process. It is a major topic in the field of non-blast furnace ironmaking at present. At present, the production process of sponge iron is mainly the rotary hearth furnace method. The rotary h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C21B11/00C21B13/00
Inventor 胡丽娜李增元
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap