Abstract

The invention relates to high-permeability super black decorated base paper and a preparation method of the high-permeability super black decorated base paper, and belongs to the technical field of decoration base paper. The preparation method is characterized by comprising the following steps: taking pulp mixed from bleached softwood pulp and bleached hardwood pulp according to the mass ratio of 1:(3.6-4.4) as a main raw material; reducing the beating degree of bleached wood pulp to 32 SR, enabling the mass concentration to reach 4%, and then pumping into a repulping pond for later use; directly adding a black pigment to the repulping pond, wholly substituting kaoline for titanium dioxide to prepare the decorated base paper with a black and shiny color, the fluorescent whiteness of 6%-8%, the basis weight of 70-90g / m<2>, the ash content of 10%-15%, the wet strength of 6.5-9N, the dry strength of 35-50N, the water absorption of 20-35mm / 10 minutes and the air permeability of 15-20s / 100ml. The high-permeability super black decorated base paper disclosed by the invention has the advantages of uniformity in coloring, good covering power, high air permeability, low basis weight and high paper output ratio; a processed decorating plate is high in stereoscopic impression, pure and bright in color and luster, green and environmental-friendly without white patterns.

Description

technical field [0001] The invention discloses a high-permeability ultra-black decorative base paper, which belongs to the technical field of black decorative base paper. Background technique [0002] Decorative base paper is a kind of decorative material developed with the rapid development of my country's wood-based panel industry and furniture manufacturing industry. After decades of development, decorative paper products have different textures and colors, and their properties such as wear resistance, heat resistance, scratch resistance, cigarette burning resistance, and pollution resistance are superior to those of wood-based panels. The board has an obvious protective effect. The quality of low-end decorative paper products is unstable, and the color fastness to light is generally poor, generally in the 2~3 level, with low hiding performance, poor printing performance and batch stability, especially the color stability, and the color difference between batches is larg...

AI Technical Summary

Problems solved by technology

The quality of low-grade decorative paper products is unstable, and the color fastness to light is generally poor, generally at level 2~3, with low covering performance, poor printing performance and batch stability, especially the color stability, and the color difference between batches is large

Moreover, the decorative base paper currently used as a decorative material has the problem of excessive paper basis weight in order to ensure higher strength ordinary sheets. The paper basis weight of decorative base paper is generally 90~130g / m 2

The base paper has a large basis weight, resulting in high production costs

[0003] The high-permeability ultra-black decorative base paper of the present invention is a high-grade product of decorative base paper, which can replace the ordinary black decorative base paper currently sold. The ordinary black decorative base paper has poor permeability during dipping processing, and the color becomes gray and black after pressing. Not enough, the pattern is uneven during printing and the color is not bright, and the ordinary black decorative base paper produced by the current process has always had the problem of white dust on the surface of the black paper

No good solution has been found at home and abroad, and there are no relevant literature reports