Nitrile-butadiene rubber NBR gear cover sealing material and preparation method thereof
A technology of nitrile rubber and sealing material, applied in the field of rubber materials, can solve the problems of low production efficiency, inability to meet price requirements and high performance requirements, shorten vulcanization molding time, improve high and low temperature resistance and medium resistance, and improve resistance Effects of Ozone Properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0027] In the specific implementation process, refer to figure 1 The preparation method of the above-mentioned nitrile rubber NBR gear cover sealing material includes the following steps:
[0028] S1, according to the proportion of nitrile rubber N241, nitrile rubber N240S, zinc oxide, stearic acid, 2,2,4-trimethyl-1,2-dihydroquinoline polymer, N-isopropyl-N -Phenyl-p-phenylenediamine, 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, microcrystalline wax and microcrystalline wax OK1987 are added to the internal mixer and mixed for 20~ After 60 seconds, add carbon black N-774 and carbon black N-990 according to the proportion and mix to 85~90℃, add plasticizer TP-90B and mix to 93~97℃, add sulfur S-80, 4', 4-dithiobismorpholine, tetramethylthiuram disulfide and N-cyclohexyl-2-benzothiazole sulfenamide are mixed to 110~120℃, and the pieces are mixed to obtain the final rubber compound;
[0029] S2. The final rubber compound obtained from S1 is molded and vulcanized to obtain a nitril...
Example Embodiment
[0031] Example 1
[0032] A nitrile rubber NBR gear cover sealing material, the raw material of which comprises by weight:
[0033]
[0034] In Example 1, the method for preparing the above-mentioned nitrile rubber NBR gear cover sealing material includes the following steps:
[0035] S1, according to the proportion of nitrile rubber N241, nitrile rubber N240S, zinc oxide, stearic acid, 2,2,4-trimethyl-1,2-dihydroquinoline polymer, N-isopropyl-N -Phenyl-p-phenylenediamine, 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, microcrystalline wax and microcrystalline wax OK1987 are added to the internal mixer and mixed for 20 seconds , Then add carbon black N-774 and carbon black N-990 according to the ratio and mix to 90℃, add plasticizer TP-90B and mix to 97℃, add sulfur S-80, 4',4-dithiobis Morpholine, tetramethylthiuram disulfide and N-cyclohexyl-2-benzothiazole sulfenamide are mixed to 120°C, and the pieces are mixed to obtain the final rubber compound;
[0036] Among them, the top pl...
Example Embodiment
[0038] Example 2
[0039] A nitrile rubber NBR gear cover sealing material, the raw material of which comprises by weight:
[0040]
[0041]
[0042] In Example 2, the method for preparing the above-mentioned nitrile rubber NBR gear cover sealing material includes the following steps:
[0043] S1, according to the proportion of nitrile rubber N241, nitrile rubber N240S, zinc oxide, stearic acid, 2,2,4-trimethyl-1,2-dihydroquinoline polymer, N-isopropyl-N -Phenyl-p-phenylenediamine, 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline, microcrystalline paraffin and microcrystalline wax OK1987 are added to the internal mixer and mixed for 50 seconds , Then add carbon black N-774 and carbon black N-990 according to the ratio and ban it to 87℃, add plasticizer TP-90B and ban it to 95℃, add sulfur S-80, 4',4-dithiobis Morpholine, tetramethylthiuram disulfide and N-cyclohexyl-2-benzothiazole sulfenamide were mixed to 115°C, and the pieces were mixed to obtain the final rubber compound;
[0044] ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction