Pressure cooling process of segmented reinforcing type parts of hot forming steel pipe, and die servo device

A segmented strengthening and hot forming technology, applied in the field of high-strength steel stamping, can solve problems such as complex structure, and achieve the needs of unified and simplified processing technology, and the effect of simple structure

Inactive Publication Date: 2014-05-14
WUXI LANGXIAN LIGHTWEIGHT TECH CO LTD
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0018] In terms of mold structure, this technology requires a heating device inside the active punch and die, so the structure is complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pressure cooling process of segmented reinforcing type parts of hot forming steel pipe, and die servo device
  • Pressure cooling process of segmented reinforcing type parts of hot forming steel pipe, and die servo device
  • Pressure cooling process of segmented reinforcing type parts of hot forming steel pipe, and die servo device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] Such as Figure 3-Figure 5 As shown, the workpiece is 2.0mm thick, 150mm wide, and 1000mm long. The workpiece product requirement is f 6 The corresponding product area is HS400 soft area, and the rest are hard area HS1150. The concrete preparation process schematic diagram of this method, wherein:

[0061] figure 1 In its original state, according to figure 1 It can be seen that the device for realizing this method includes: upper mold 1, lower mold 2, upper mold in-mold servo cylinder 3, lower mold in-mold servo cylinder 4, upper mold pressing core 5, lower mold pressing core 6, upper slider 7 of the press , Press lower table 8, mold mandrel 9.

[0062] The upper mold 1 covers the range of HS1150 in the hard area of ​​the product, and the material is high-quality mold steel SKD61;

[0063] The upper mold pressing material core 5 covers the product soft zone HS400 range, and the material is high-quality mold steel SKD61;

[0064] The lower mold pressing material ...

Embodiment 2

[0081] Such as Figure 3-Figure 5 As shown, the workpiece is 2.0mm thick, 150 wide, 1000 long hot-formed boron steel workpiece section forming and quenching diagram. The workpiece product requirement is f 6 The corresponding product area is HS400 soft area, f 8 except f 6 Outside the area is the soft area HS700, and the rest of the product area is the hard area HS1150. .

[0082] This method realizes the device such as figure 1 shown, where:

[0083] The upper mold 1 covers all areas of the product soft area HS700 and hard area HS1150, and the material is high-quality die steel SKD61;

[0084] The upper mold pressing material core 5 covers all areas of the soft area HS700 of the product, and the material is high-quality mold steel SKD61;

[0085] The lower mold pressing material core 6 covers all areas of the product soft zone HS400 and soft zone HS700, and the material is high-quality mold steel SKD61;

[0086] The lower mold 2 covers all areas of the hard area HS1150...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
plasticityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pressure cooling process of segmented reinforcing type parts of a hot forming steel pipe, and a die servo device. Through a servo cylinder device in a die, the magnitude of pressure keeping loading force borne by a workpiece and time for bearing the pressure keeping loading force by the workpiece are controlled according to the design requirements, and therefore the cooling speed of each sub-area is controlled, and the different physical properties of the sub-areas of a tubular product are obtained. Required material characteristics can be achieved for any area according to the design requirements, no additional die heating device needs to be arranged, and production cost and procedure complexity are greatly reduced.

Description

technical field [0001] The invention relates to a method in the technical field of high-strength steel stamping, in particular to a pressure cooling process and a mold servo device for segmentally strengthened hot-formed steel pipe parts with a strength of about 1500MP. Background technique [0002] As a new type of ultra-high-strength hot-formed steel pipe for automobiles, boron steel pipes for automobiles provide the possibility for segmental strengthening technology—the same part can adopt different heat treatment processes in different regions of the part according to the needs of automobile design, so as to obtain different strength and plasticity. The production process of the soft zone technology for hot-formed boron steel materials is divided into 4 stages: [0003] 1) Heating: heating the boron steel pipe to the temperature required for heat treatment; [0004] 2) Transmission: transfer the boron steel pipe to the mold to be punched; [0005] 3) Forming: Stamping...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21D37/16B30B15/14C21D1/673
Inventor 陈扬
Owner WUXI LANGXIAN LIGHTWEIGHT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com