Holmium-based multiple-ligand rubber vulcanization accelerator and preparation method thereof

A rubber vulcanization and multi-ligand technology, which is applied in the synthesis field of holmium-based multi-ligand vulcanization accelerators, can solve problems such as poor solubility, and achieve the effects of simplified process, good vulcanization flatness, and simple and easy preparation method

Active Publication Date: 2014-05-28
BEIJING UNIV OF CHEM TECH
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of accelerator effectively improves the disadvantage of poor solubility in rubber of traditional vulcanization accelerator systems, simplifies the feeding process, and is clean and pollution-free

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Holmium-based multiple-ligand rubber vulcanization accelerator and preparation method thereof
  • Holmium-based multiple-ligand rubber vulcanization accelerator and preparation method thereof
  • Holmium-based multiple-ligand rubber vulcanization accelerator and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

Embodiment 2

Embodiment 3

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a holmium-based multiple-ligand rubber vulcanization accelerator and a preparation method thereof. A rare earth element in synthesis is holmium comprising four ligands, the ligands 1 and 2 are accelerator groups having excellent vulcanizing and accelerating effects, the ligand 3 is palmitic acid capable of accelerating solubility of the accelerator in a sizing material, and the ligand 4 is alpha-methylacrylic acid capable of forming strong ligands together with the rare earth element. The method is simple, convenient and easy, and does not require protection of inert gas, conditions during the preparation process are moderate, and no harmful gases can be generated. The multiple-ligand rare earth vulcanization accelerator has a good solubility in rubber, the vulcanizing and scorching time is long, the vulcanization curve is excellent in flatness, and toxin, odour and pollution are avoided. The accelerator can replace a conventionally used zinc oxide, octadecanoic acid and accelerator combined-use system and can be applied to high-performance tires and other rubber products.

Description

technical field [0001] The invention relates to a synthesis method of a holmium-based multi-ligand vulcanization accelerator and research on its vulcanization acceleration effect. This accelerator does not need zinc oxide and stearic acid as an activator, and has the advantages of saving the feeding process, clean and pollution-free, good vulcanization flatness, and easy to uniformly disperse in rubber. The rubber composite material prepared by using this accelerator has the advantages of Good performance uniformity. Background technique [0002] The vulcanization system of rubber is a complete vulcanization system composed of accelerators, activators, and vulcanizing agents. Among them, the accelerator is a chemical substance that can shorten the vulcanization time, lower the vulcanization temperature, reduce the amount of vulcanizing agent, and improve and improve the physical and mechanical properties and chemical stability of the vulcanized rubber. Just because acceler...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K5/00C07F5/00C08L9/06
Inventor 刘力杜一诗摆音娜胡水温世鹏
Owner BEIJING UNIV OF CHEM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com