Collagen material for repairing peripheral nerve injury containing two factors and preparation method thereof

A technology for peripheral nerve injury and collagen material, which is applied in the field of medical materials to achieve the effects of promoting expression, increasing the diameter of the myelin sheath and the thickness of the myelin sheath, and providing good technical support.

Active Publication Date: 2015-08-19
INST OF GENETICS & DEVELOPMENTAL BIOLOGY CHINESE ACAD OF SCI
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no research on the role of collagen scaffold materials combined with two factors in peripheral nerve injury repair.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Collagen material for repairing peripheral nerve injury containing two factors and preparation method thereof
  • Collagen material for repairing peripheral nerve injury containing two factors and preparation method thereof
  • Collagen material for repairing peripheral nerve injury containing two factors and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0074] Embodiment 1, the preparation of the collagen support of repairing peripheral nerve injury

[0075] 1. Preparation of Collagen Scaffolds Containing Dual Factors for Functional Repair of Peripheral Nerve Injury

[0076] 1. Preparation of Collagen Tubes

[0077] According to the radius of the nerve injury site to be repaired, find a mold with the same radius, choose glass or plastic as the mold, cut the collagen film into an appropriate size, soak it in triple distilled water for 2 minutes to make the collagen film soft, and wrap the collagen film around the mold Wrap 5 / 4 circles, wrap it with liquid collagen, and let it dry overnight ( figure 1 Middle A). room temperature (25 ℃ overnight (12 hours) cross-linking, after cross-linking, the collagen tube was removed from the mold, lyophilized, and irradiated for later use ( figure 1 Middle B and C).

[0078] 2. Preparation of collagen materials containing two factors for repairing peripheral nerve injuries

[0079] 100...

Embodiment 2

[0094] Example 2. Application of Peripheral Nerve Injury Function Repair Collagen Scaffold to Treat Long-distance Transverse Nerve Injury in Minipigs

[0095] 1. Prepare a long-distance (3.5cm) facial nerve transection injury model in minipigs, and bridge the peripheral nerve injury function repair collagen scaffold material at both ends of the nerve injury

[0096] First, a model of facial nerve transection injury in minipigs was prepared. Select 8 13-month-old miniature pigs (China Agricultural University), with a body weight of about 40-45 kg. After muscle anesthesia, the facial nerves on both sides of the pigs were cut free by 3.5 cm to make a long-distance facial nerve injury model of miniature pigs ( figure 2 Middle A).

[0097] Then, 6 of the miniature pigs were sutured to bridge the four kinds of collagen scaffolds prepared in Example 1 at the proximal end and the distal end of the nerve injury ( figure 2 In middle B), three sets of replicates were set up for each ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a collagen material for repairing peripheral nerve injury. The method comprises the following step: co-incubating a ciliary neurotrophic factor with a collagen binding domain (CBD-CNTF), a basic fibroblast growth factor with a collagen binding domain (CBD-bFGF) and an orderly collagen material to obtain a collagen material for repairing the peripheral nerve injury. According to the preparation method, two factors CBD-CNTF and CBD-bFGF are simultaneously crosslinked to the orderly collagen scaffold material, and the action of the double-factor peripheral nerve injury repairing collagen material in long-cross-section nerve injury repairing can be evaluated by establishing an animal peripheral nerve-facial nerve long cross-section injury model. Results prove that compared with single factor CBD-CNTF or CBD-bFGF functional collagen scaffold material, the double-factor peripheral nerve injury repairing collagen material can be used for better promoting regeneration of facial nerves and restoration of functions, and has a more important realistic guiding magnificence to application of clinical peripheral nerve injury repairing in the future.

Description

technical field [0001] The invention belongs to the field of medical materials, and relates to a collagen material for repairing peripheral nerve damage, in particular to a collagen material for repairing peripheral nerve damage containing two factors and a preparation method thereof. Background technique [0002] Peripheral nerve injury is one of the common diseases in clinical practice. The current clinical application of direct stump suture technique or autologous nerve transplantation cannot fully solve the clinical difficulties due to its application limitations. With the development of tissue engineering, the use of tissue engineering methods to promote nerve regeneration to repair peripheral nerve injury has become a research hotspot. [0003] Collagen scaffold material can bridge the growth of axons and play a role in guiding the growth of axons. Collagen is a biomaterial widely used in tissue engineering because of its low immunogenicity, good biocompatibility and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/24A61L27/36
Inventor 戴建武崔熠侯祥林肖志峰陈冰
Owner INST OF GENETICS & DEVELOPMENTAL BIOLOGY CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com