Porcelain prepared by combination of glass and ceramic and method thereof

Abstract

The invention provides porcelain prepared by the combination of glass and ceramic and a preparation method thereof. The porcelain comprises a porcelain pot and a glass fitting. The pot surface of the porcelain pot is provided with a recessed surface, and the glass fitting is mounted on the recessed surface. The glass fitting and the porcelain pot of the porcelain can be combined together firmly, and the porcelain has a good aesthetic feeling. The method comprises the following steps: petuntse is ground to obtain required slurry; the slurry is injected into a mould to form a rough blank; the rough blank is repaired and glued; after the blank body to be moulded is dried, the recessed surface is made at the position where the glass fitting needs to be adhered to the blank surface; the finished blank body undergoes briscuit firing; the blank body which has undergone briscuit firing undergoes glazing; the blank body which has undergone glazing enters a kiln and undergoes high-temperature glaze firing; a moulded finished product obtained after glaze firing undergoes sole rubbing and mouth polishing; and the glass fitting is mounted and adhered to the recessed surface of the pot surface. By the above method, the problem that glass and porcelain cannot be cofired or firmly combined is overcome.

Description

technical field [0001] The invention belongs to the field of ceramic production technology, and in particular relates to a kind of porcelain made by combining glass and ceramics and a method thereof. Background technique [0002] Glass is an amorphous, non-crystalline inorganic material with a history dating back 400 years. In recent decades, the glass industry has developed greatly. At present, the glass industry creates an output value of about 100 billion U.S. dollars every year in the world. Compared with glass materials, ceramics are an inorganic material with a richer product variety and a more ordered structure. At present, both glass and ceramics are silicate products, but the composition is different. It is difficult to achieve it by sintering alone, because their sintering temperatures are different. Ceramics need at least 1000 degrees Celsius, while glass only needs 560 degrees Celsius. If the sintering temperature is too high, the glass will crack, and the conn...

AI Technical Summary

Problems solved by technology

[0003] The purpose of the embodiments of the present invention is to provide a kind of porcelain and method made by combining glass and ceramics, aiming to solve the problem that there is no technology for making the combination of glass and ceramics firm and the porcelain made by this technology

Images