A kind of bamboo charcoal fiber fabric for home textile

A bamboo charcoal fiber and home textile technology, applied in the field of textile preparation, can solve the problems of fiber material softness and antibacterial properties to be improved, and achieve the effects of jacquard quality stability, shedding prevention, and good moisture absorption and release

Active Publication Date: 2016-03-16
汕头市粤宝利实业有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN103556263A (2014-2-5) discloses a hollow bamboo charcoal viscose fiber and its production process, but the softness and bacteriostasis of the fiber material prepared by this method still need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bamboo charcoal fiber fabric for home textile
  • A kind of bamboo charcoal fiber fabric for home textile
  • A kind of bamboo charcoal fiber fabric for home textile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] Preparation of nano silver:

[0049] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 4:1; The molar ratio of acrylate to silver nitrate is 0.4:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.2:1;

[0050] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 3:1; sodium metaphosphate and nitric acid The molar ratio of silver is 0.8:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0051] The composition ratio of the viscose liquid used for bamboo charcoal fiber fabrics:

[0052] 25 parts of phthalic anhydride, 7 parts of furfuryl alcohol extracted from corncob residue, 10 parts of triethylene glycol, 15 parts of glutaric acid, 8 parts of butanetriol, 5 parts of zinc oxide powder, 3...

Embodiment 2

[0077] Preparation of nano silver:

[0078] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 6:1; The molar ratio of acrylate to silver nitrate is 0.6:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.3:1;

[0079] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 5:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1.3:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0080] The composition ratio of the viscose liquid used for bamboo charcoal fiber fabrics:

[0081] 35 parts of phthalic anhydride, 11 parts of furfuryl alcohol extracted from oat or wheat bran, 12 parts of triethylene glycol, 18 parts of glutaric acid, 10 parts of butanetriol, 7 parts of zinc oxide powde...

Embodiment 3

[0105] Preparation of nano silver:

[0106] A. Add sodium dodecylsulfonate solution, water-based polyacrylate and hydrazine hydrate solution to silver nitrate aqueous solution to obtain a mixed solution, the molar ratio of sodium dodecylsulfonate to silver nitrate is 5:1; The molar ratio of acrylate to silver nitrate is 0.5:1; the molar ratio of hydrazine hydrate to silver nitrate is 0.25:1;

[0107] B. Add dicyclohexyl-18-crown-6 and sodium metaphosphate to the mixture, the molar ratio of dicyclohexyl-18-crown-6 to silver nitrate is 4:1; sodium metaphosphate and nitric acid The molar ratio of silver is 1:1, and the pH value is controlled to be 8-9 to obtain nano silver.

[0108] The composition ratio of the viscose liquid used for bamboo charcoal fiber fabrics:

[0109] 30 parts of phthalic anhydride, 7-11 parts of furfuryl alcohol extracted from bamboo sawdust, 11 parts of triethylene glycol, 16 parts of glutaric acid, 9 parts of butanetriol, 6 parts of zinc oxide powder, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a kind of preparation method of textile, relate in particular to a kind of bamboo charcoal fiber fabric for home textile, it comprises the preparation of bamboo charcoal micro-powder emulsion; the preparation of viscose liquid; the preparation of bamboo charcoal fiber silk; gray cloth preparation: including spinning, warping, pulping Yarn, weaving, two-bath dyeing, fabric post-treatment, opening width, dehydration, drying and sewing steps; cotton fiber is used in the warp direction of spinning, modal fiber or spandex covered silk and the bamboo charcoal fiber silk are used in the weft direction; two Bath dyeing is pad dyeing and double dyeing of the same color; jacquard: including the first loose drying, cut pile, the second loose drying, and making overprinted pattern screens;? The drying temperature of the first loose drying in the jacquard step is 130-140°C, and the drying time is 5-9min; the drying temperature of the second loose drying is 70-90°C, and the drying time is 15-22min. The bamboo charcoal fiber fabric for home textile prepared by the method has good softness and antibacterial property.

Description

technical field [0001] The invention relates to a preparation method of textiles, in particular to a bamboo charcoal fiber fabric used for home textiles. Background technique [0002] Bamboo charcoal has good deodorizing, anti-corrosion, and odor-absorbing functions. Nano-scale bamboo charcoal powder also has antibacterial and bactericidal effects, as well as far-infrared and negative ion properties. CN103556263A (2014-2-5) discloses a hollow bamboo charcoal viscose fiber and its production process, but the softness and bacteriostasis of the fiber material prepared by this method still need to be improved. Contents of the invention [0003] The purpose of the present invention is to provide a kind of softness and antibacterial good bamboo charcoal fiber fabric that is used for home textile. [0004] Above-mentioned technical purpose of the present invention is achieved through the following technical solutions: [0005] A kind of bamboo charcoal fiber fabric that is use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/02D01F8/18D03D15/00D02H3/00D06B3/18D06C13/08D06B15/00B22F9/24D03D15/20D03D15/50
Inventor 丁建中
Owner 汕头市粤宝利实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap